Preparation of hydrophobic flat sheet membranes from PVDF-HFP copolymer for enhancing the oxygen permeance in nitrogen/oxygen gas mixture

doi:10.1016/j.cjche.2020.02.018

Abstract

Abstract: In this study, poly(vinilydene fluoride-co-hexafluoropropylene) (PVDF-HFP) was used for preparation of hydrophobic membranes using non-solvent induced phase inversion (NIPS) technique. PVDF-HFP copolymer with concentrations of 10 wt% and 12 wt% was prepared to investigate the effect of polymer concentration on pore structure, morphology, hydrophobicity and performance of prepared membranes. Besides, the use of two coagulation baths with the effects of parameters such as coagulant time, polymer type and concentration, and the amount of nonsolvent were studied. The performance of prepared membranes was evaluated based on the permeability and selectivity of oxygen and nitrogen from a gas mixture of nitrogen/oxygen under operating conditions of feed flow rate (1-5 L·min^-1), inlet pressure to membrane module (0.1-0.5 MPa) and temperatures between 25 and 45℃. The results showed that the use of two coagulation baths with different compositions of distillated water and isopropanol, coagulant time, polymer type and concentration, and the amount of non-solvent additive have the most effect on pore structure, morphology, thickness, roughness and crystallinity of fabricated membranes. Porosity ranges for the three fabricated membranes were determined, where the maximum porosity was 73.889% and the minimum value was 56.837%. Also, the maximum and minimum average thicknesses of membrane were 320.85 μm and 115 μm. Besides, the values of 4.7504×10^-7 mol·m^-2·s^-1·Pa^-1, 0.525 and 902.126 nm were achieved for maximum oxygen permeance, O₂/N₂ selectivity and roughness, respectively.

Key words: Oxygen-enriched air, Hydrophobic flat sheet membrane, PVDF-HFP copolymer, Enhancing oxygen permeance, Pore structure

摘要： In this study, poly(vinilydene fluoride-co-hexafluoropropylene) (PVDF-HFP) was used for preparation of hydrophobic membranes using non-solvent induced phase inversion (NIPS) technique. PVDF-HFP copolymer with concentrations of 10 wt% and 12 wt% was prepared to investigate the effect of polymer concentration on pore structure, morphology, hydrophobicity and performance of prepared membranes. Besides, the use of two coagulation baths with the effects of parameters such as coagulant time, polymer type and concentration, and the amount of nonsolvent were studied. The performance of prepared membranes was evaluated based on the permeability and selectivity of oxygen and nitrogen from a gas mixture of nitrogen/oxygen under operating conditions of feed flow rate (1-5 L·min^-1), inlet pressure to membrane module (0.1-0.5 MPa) and temperatures between 25 and 45℃. The results showed that the use of two coagulation baths with different compositions of distillated water and isopropanol, coagulant time, polymer type and concentration, and the amount of non-solvent additive have the most effect on pore structure, morphology, thickness, roughness and crystallinity of fabricated membranes. Porosity ranges for the three fabricated membranes were determined, where the maximum porosity was 73.889% and the minimum value was 56.837%. Also, the maximum and minimum average thicknesses of membrane were 320.85 μm and 115 μm. Besides, the values of 4.7504×10^-7 mol·m^-2·s^-1·Pa^-1, 0.525 and 902.126 nm were achieved for maximum oxygen permeance, O₂/N₂ selectivity and roughness, respectively.

关键词: Oxygen-enriched air, Hydrophobic flat sheet membrane, PVDF-HFP copolymer, Enhancing oxygen permeance, Pore structure

Bahador Akbari, Asghar Lashanizadegan, Parviz Darvishi, Abdolrasoul Pouranfard. Preparation of hydrophobic flat sheet membranes from PVDF-HFP copolymer for enhancing the oxygen permeance in nitrogen/oxygen gas mixture[J]. Chinese Journal of Chemical Engineering, 2020, 28(6): 1566-1581.

References

[1] B. Castro-Dominguez, P. Leelachaikul, A. Takagaki, T. Sugawara, R. Kikuchi, S.T. Oyama, Perfluorocarbon-based supported liquid membranes for O₂/N₂ separation, Sep. Purif. Technol. 116(2013) 19-24.
[2] B. Belaissaoui, Y.L. Moullec, H. Hagi, E. Favre, Energy efficiency of oxygen enriched air production technologies:cryogeny vs membranes, Sep. Purif. Technol. 125(2014) 142-150.
[3] Z. Xu, L. Zhao, X. Chen, Z. Shao, J. Qian, L. Zhu, Z. Zhou, H. Qin, Automatic load change system of cryogenic air separation process, Sep. Purif. Technol. 81(2011) 451-465.
[4] J.W. Phair, S.P.S. Badwal, Materials for separation membranes in hydrogen and oxygen production and future power generation, Sci. Technol. Adv. Mater. 7(2006) 792-805.
[5] H. Zhou, Y. Cai, Y. Xiao, Z.A. Mkhalel, B. You, J. Shi, J. Li, B.H. Chen, Process configurations and simulations for a novel single-column cryogenic air separation process, Ind. Eng. Chem. Res. 51(2012) 15431-15439.
[6] C. Voss, Applications of pressure swing adsorption technology, Adsorption 11(2005) 527-529.
[7] R.W. Baker, I. Roman, H.K. Lonsdale, Liquid membranes for the production of oxygen-enriched air, J. Mem. Sci. 31(1987) 15-29.
[8] S.L. Matson, Membrane oxygen enrichment, J. Mem. Sci. 29(1986) 79-96.
[9] B.D. Bhide, S.A. Stern, A new evaluation of membrane processes for the oxygen enrichment of air. I. Identification of optimum operating conditions and process configuration, J. Mem. Sci. 62(1991) 13-35.
[10] P. Bernardo, E. Drioli, G. Golemme, Membrane gas separation:A review/state of the art, Ind. Eng. Chem. Res. 48(2009) 4638-4663.
[11] W.J. Koros, R. Mahajan, Pushing the limits on possibilities for large scales gas separation:Which strategies? J. Mem. Sci. 175(2000) 181-196.
[12] B. Ameduri, From vinylidene fluoride (VDF) to the applications of VDF-containing polymers and copolymers:Recent developments and future trends, Chem. Rev. 109(2009) 6632-6686.
[13] Z. Cui, E. Drioli, Y.M. Lee, Recent progress in fluoropolymers for membranes, Prog. Polym. Sci. 39(2014) 164-198.
[14] F. Liu, N.A. Hashim, Y. Liu, M. Abed, K. Li, Progress in the production and modification of PVDF membranes, J. Mem. Sci. 375(2011) 1-27.
[15] G.D. Kang, Y.M. Cao, Application and modification poly (vinylidene fluoride) (PVDF) membranes-A review, J. Mem. Sci. 463(2014) 145-165.
[16] S. Wongchitphimon, R. Wang, R. Jiraratananon, Surface modification of polyvinylidene fluoride-co-hexafluoropropylene (PVDF-HFP) hollow fiber membrane for membrane gas absorption, J. Mem. Sci. 381(2011) 183-191.
[17] J. Wang, L. Zheng, Z. Wu, Y. Zhang, X. Zhang, Fabrication of hydrophobic flat sheet and hollow fiber membranes from PVDF and PVDF-CTFE for membrane distillation, J. Mem. Sci. 497(2016) 183-193.
[18] C. Feng, R. Wang, B. Shi, G. Li, Y. Wu, Factors affecting pore structure and performance of poly (vinylidene fluoride-co-hexafluoropropylene) asymmetric porous membrane, J. Mem. Sci. 277(2006) 55-64.
[19] L. Shi, R. Wang, Y. Cao, C. Feng, D.T. Liang, J.H. Tay, Fabrication of poly (vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) asymmetric microporous hollow fiber membranes, J. Mem. Sci. 305(2007) 215-225.
[20] L. Shi, R. Wang, Y. Cao, D.T. Liang, J.H. Tay, Effect of additives on the fabrication of poly (vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) asymmetric microporous hollow fiber membranes, J. Mem. Sci. 315(2008) 195-204.
[21] X. Tian, X. Jiang, Poly (vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) membranes for ethyl acetate removal from water, J. Hazard. Mater. 153(2008) 128-135.
[22] W. Pu, X. He, L. Wang, C. Jiang, C. Wan, Preparation of PVDF-HFP microporous membrane for Li-ion batteries by phase inversion, J. Mem. Sci. 272(2006) 11-14.
[23] Z. Li, G. Su, X. Wang, D. Gao, P. Micro-porous, VDF-HFP based polymer electrolyte filled with AL₂O₃ nanoparticles, Solid State Ionics 176(2005) 1903-1908.
[24] C. Capiglia, Y. Saito, H. Kataoka, T. Kodama, E. Quartarone, P. Mustarelli, Structure and transport properties of polymer gel electrolytes based on PVDF-HFP and LiN (C₂F₅SO₂)₂, Solid State Ionics 131(2000) 291.
[25] C. Lee, J.H. Kim, J.Y. Bae, Polymer gel electrolytes prepared by thermal curing of poly (vinylidene fluoride)-hexafluoropropene/poly (ethylene glycol)/propylene carbonate/lithium perchlorate blends, polymer 44(2003) 7143.
[26] Q. Shi, M.X. Yu, X. Zhou, Y.S. Yan, C.R. Wan, Structure and performance of porous polymer electrolytes based on PVDF-HFP for Lithium ion batteries, J. Power Sources 103(2002) 286.
[27] D. Saikia, A. Kumar, Ionic conduction in PVDF-HFP/PVDF-(PC+DEC)-LiCIO₄ polymer gel electrolytes, Electrochim. Acta 49(16) (2004) 2581-2589.
[28] T. Michot, A. Nishimoto, M. Watanabe, Electrochemical properties of polymer gel electrolytes based on poly (vinylidene fluoride) copolymer and homopolymer, Electrochim. Acta 45(8-9) (2000) 1347-1360.
[29] A.M. Stephan, D. Teeters, Characterization of PVDF-HFP polymer membranes prepared by phase inversion techniques; morphology and charge-discharge studies, Electrochim. Acta 48(14) (2003) 2143-2148.
[30] N.T.K. Sundaram, A. Subramania, Microstructure of PVDF-CO-HFP based electrolyte prepared by prefential polymer dissolution process, J. Mem. Sci. 289(2007) 1-6.
[31] A.M. Stephan, N.G. Ranganathan, S. Gopukumar, D. Teeters, Cycling behavior of poly (vinylidene fluoride-co-hexafluoro propylene) (PVDF-HFP) membranes prepared by phase inversion method, Chem. Phys. 85(2004) 6-11.
[32] J.H. Cao, B.K. Zhu, Y.Y. XU, Structure and ionic conductivity of porous polymer electrolytes based on PVDF-HFP copolymer membranes, J. Mem. Sci. 281(2006) 446-453.
[33] M.C. Garcia-Payo, M. Essalhi, M. Khayet, Preparation and characterization of PVDFHFP copolymer hollow fiber membranes for membrane distillation, Desalination 245(2009) 469-473.
[34] X. Yu, L. An, J. Yang, S.T. Tu, J. Yan, CO₂ capture using superhydrophobic ceramic membrane contactor, J. Mem. Sci. 496(2015) 1-12.
[35] W. Kujawski, J. Kujawa, E. Wierzbowska, S. Cerneaux, M. Bryjak, J. Kujawski, Influence of hydrophobization conditions and ceramic membranes pore size on their properties in vacuum membrane distillation of water-organic solvent mixtures, J. Mem. Sci. 499(2016) 442-451.
[36] A. Larbot, L. Gazagnes, S. Krajewski, M. Bukowska, W. Kujawski, Water desalination using ceramic membrane distillation, Desalination 168(2004) 367-372.
[37] N. Ahmad, C. Leo, A. Ahmad, W. Ramli, Membranes with great hydrophobicity:a review on preparation and characterization, Sep. Purif. Rev. 44(2015) 109-134.
[38] G.R. Guillen, Y. Pan, M. Li, E.M. Hoek, Preparation and characterization of membranes formed by nonsolvent induced phase separation:a review, Ind. Eng. Chem. Res. 50(2011) 3798-3817.
[39] M. Buonomenna, P. Macchi, M. Davoli, E. Drioli, Poly (vinylidene fluoride) membranes by phase inversion:the role the casting and coagulation conditions play in their morphology, crystalline structure and properties, Eur. Polym. J. 43(2007) 1557-1572.
[40] M.D.C. Garcia-Payo, M. Khayet, Effect of PVDF-HFP concentration on membrane distillation performance and structural morphology of hollow fiber membranes, J. Mem. Sci. 347(2010) 209-219.
[41] N. Ghasem, M. Al-Marzouqi, A. Duidar, Effect of PVDF concentration on the morphology and performance of hollow fiber membrane employed as gas-liquid membrane contactor for CO₂ absorption, Sep. Purif. Technol. 98(2012) 174-185.
[42] L. Zheng, Z. Wu, Y. Wei, Y. Zhang, Y. Yuan, J. Wang, Preparation of PVDF-CTFE hydrophobic membranes for MD application:effect of LICL-based mixed additive, J. Mem. Sci. 506(2016) 71-85.
[43] A. Mansourizadeh, A.F. Ismail, Effect of LICL concentration in the polymer dope on the structure and performance of hydrophobic PVDF hollow fiber membranes for CO₂ absorption, J. Chem. Eng. 165(2010) 980-988.
[44] F.M. Kerton, R. Marriott, Alternative Solvent for Green Chemistry, 2nd Edition, RSC Publishing, UK, 2013(chapter 1).
[45] S. Fadhil, T. Marino, H.F. Makki, Q.F. Alsalhy, S. Blefari, F. Macedonio, E. Di Nicolo, L. Giorno, E. Drioli, Novel PVDF-HFP flat-sheet membranes prepared by triethyl phosphate (TEP) solvent for direct contact membrane distillation, Chem. Eng. Process. 102(2016) 16-26.
[46] C. Feng, R. Wang, B. Shi, G. Li, Y. Wu, Factors affecting pore structure and performance of poly (vinylidene fluoride-co-hexafluoro propylene) asymmetric porous membrane, J. Mem. Sci. 277(2006) 55-64.
[47] S. Nejati, C. Boo, C.O. Osuji, M. Elimelech, Engineering flat sheet microporous PVDF films for membrane distillation, J. Mem. Sci. 492(2015) 355-363.
[48] D. Li, R. Wang, T.S. Chung, Fabrication of lab-scale hollow fiber membrane modules with high packing density, Sep. Purif. Technol. 40(2004) 15-30.
[49] L. Zheng, J. Wang, J. Li, Y. Zhang, K. Li, Y. Wei, Preparation, evaluation and modification of PVDF-CTFE hydrophobic membrane for MD desalination application, Desalination 402(2017) 162-172.
[50] L. Zheng, J. Wang, Y. Wei, Y. Zhang, K. Li, Z. Wu, Interconnected PVDF-CTFE hydrophobic membranes for MD desalination:effect of PEGs on phase inversion process, RSC Adv. 6(2016) 20926-20937.
[51] F. Giessible, Advances in atomic force microscopy, Rev. Mod. Phys. 75(3) (2003) 949-968.
[52] T. Yamaguchi, A. Takagaki, T. Sugawara, R. Kikuchi, S.T. Oyama, Supported fluorocarbon liquid membranes for hydrogen/oxygen separation, J. Mem. Sci. 520(2016) 272-280.
[53] D. Hou, G. Dai, J. Wang, H. Fan, L. Zhang, Z. Luan, Preparation and characterization of PVDF/nonwoven fabric flat-sheet composite membranes for desalination through direct contact membrane distillation, Sep. Purif. Technol. 101(2012) 1-10.
[54] W. Pu, X. He, L. Wang, C. Jiang, C. Wan, Preparation of PVDF-HFP microporous membrane for Li-ion batteries by phase inversion, J. Mem. Sci. 272(2006) 11-14.
[55] K.C. Khulbe, T. Matsuura, Characterization of synthetic membranes by Raman spectroscopy, electron spin resonance and atomic force microscopy:a review, Polymer 41(2000) 1917-1935.
[56] F.A. AlMarzooqi, M.R. Bilad, B. Mansoor, H.A. Arafat, A comparative study of image analysis and porometry techniques for characterization of porous membranes, J. Mater. Sci. (2015) 1-16.
[57] M.C. Garcia-Payo, M. Essalhi, M. Khayet, Effects of PVDF-HFP concentration on membrane distillation performance and structural morphology of hollow fiber membranes, J. Mem. Sci. 347(2010) 209-219.
[58] S. Munirasu, F. Banat, A.A. Durrani, M.A. Haija, Intrinsically superhydrophobic PVDF membrane by phase inversion for membrane distillation, Desalination 417(2017) 77-86.
[59] R.S. Murali, T. Sankarshana, S. Sridhar, Air separation by polymer-based membrane technology, Sep. Purif. Rev. 42(2013) 130-186.
[60] B. Sasikumar, G. Arthanareeswaran, A.F. Ismail, Recent progress in ionic liquid membranes for gas separation, J. Mol. Liq. 266(2018) 1-47.
[61] R. Condemarin, P. Scovazzo, Gas permiabilities, solubilities, disffusivities and diffusivity correlations for ammonium-based room temperature ionic liquids with comparison to imidazolium and phosphonium RTIL data, J. Chem. Eng. 147(2009) 51-57.
[62] Q. Alsalhy, S. Algebory, G.M. Alwan, S. Simone, A. Figoli, E. Drioli, Hollow fiber ultrafiltration membranes from poly (vinyl chloride):Preparation, morphologies and properties, Sep. Sci. Technol. 46(2011) 2199-2210.