Electrochemically reconstructed copper-polypyrrole modified graphite felt electrodes for efficiently electrocatalytic reduction of nitrate

doi:10.1016/j.cjche.2025.04.005

Abstract

Abstract: In this work, a simple two-step electrodeposition was employed to prepare PPy-Cu/GF (PPy, polypyrrole; GF, graphite felt) composite cathodes for the nitrate reduction. Characterized results revealed that the introduction of PPy as an intermediate layer resulted in the transformation of both granular and dendritic Cu in form of Cu⁺/Cu⁰, Cu²⁺ on the electrode surface. The NO₃^--N of 50 mg·L^-1 was almost completely removed (99.01%) using the PPy-Cu/GF cathode under the optimum condition, which is obviously higher than the GF, PPy/GF and Cu/GF electrodes. NO₃^--N removal was slightly affected over the pH scale of 3.0 e11.0, whereas increasing the current density from 10 to 25 mA·cm^-2 boosted the reduction of NO₃^--N. At a Cl concentration of 2000 mg·L1, the removal of NO₃^--N was slightly reduced, while the selectivity for N₂ increased dramatically due to the active chlorine could oxidize NH₄⁺-N to N₂. Meanwhile, PPy-Cu/ GF cathode exhibits an average removal rate of 97.83% within 12 cycles, highlighting its potential for application in actual water bodies. The EPR analysis and the active species trapping experiment confirmed that the nitrate reduction on the PPy-Cu/GF cathode mainly relies on direct reduction mediated by electron transfer, while ^*H influences the reduction of nitrite to ammonia.

Key words: Electrocatalytic nitrate reduction, Electrodeposition, PPy-Cu/GF cathode

摘要： In this work, a simple two-step electrodeposition was employed to prepare PPy-Cu/GF (PPy, polypyrrole; GF, graphite felt) composite cathodes for the nitrate reduction. Characterized results revealed that the introduction of PPy as an intermediate layer resulted in the transformation of both granular and dendritic Cu in form of Cu⁺/Cu⁰, Cu²⁺ on the electrode surface. The NO₃^--N of 50 mg·L^-1 was almost completely removed (99.01%) using the PPy-Cu/GF cathode under the optimum condition, which is obviously higher than the GF, PPy/GF and Cu/GF electrodes. NO₃^--N removal was slightly affected over the pH scale of 3.0 e11.0, whereas increasing the current density from 10 to 25 mA·cm^-2 boosted the reduction of NO₃^--N. At a Cl concentration of 2000 mg·L1, the removal of NO₃^--N was slightly reduced, while the selectivity for N₂ increased dramatically due to the active chlorine could oxidize NH₄⁺-N to N₂. Meanwhile, PPy-Cu/ GF cathode exhibits an average removal rate of 97.83% within 12 cycles, highlighting its potential for application in actual water bodies. The EPR analysis and the active species trapping experiment confirmed that the nitrate reduction on the PPy-Cu/GF cathode mainly relies on direct reduction mediated by electron transfer, while ^*H influences the reduction of nitrite to ammonia.

关键词: Electrocatalytic nitrate reduction, Electrodeposition, PPy-Cu/GF cathode

Ge Liu, Jiahong Wang, Zhi Hu, Tianjiao Lu, Hao Zhang, Jie Zhu. Electrochemically reconstructed copper-polypyrrole modified graphite felt electrodes for efficiently electrocatalytic reduction of nitrate[J]. Chinese Journal of Chemical Engineering, 2025, 83(7): 51-61.

References

[1] Y.Z. Zhang, X. Chen, W.L. Wang, L.F. Yin, J.C. Crittenden, Electrocatalytic nitrate reduction to ammonia on defective Au1Cu (111) single-atom alloys, Appl. Catal. B Environ. 310(2022) 121346.
[2] Y.R. Feng, X.C. Huang, Z.Y. Wu, H.T. Wang, K.C. Zuo, Q.L. Li, Polarity modulation enhances electrocatalytic reduction of nitrate by iron nanocatalysts, ACS EST Eng. 4(4) (2024) 928-937.
[3] L. Perez-Urrestarazu, J. Lobillo-Eguíba, R. Fern andez-Ca nero, V.M. Fern ~ andezCabanas, Food safety concerns in urban aquaponic production: nitrate con- tents in leafy vegetables, Urban For. Urban Green. 44(2019) 126431.
[4] J. Wang, Y.A. Wang, C. Cai, Y.S. Liu, D.J. Wu, M.Y. Wang, M.H. Li, X.B. Wei, M.H. Shao, M. Gu, Cu-doped iron oxide for the efficient electrocatalytic nitrate reduction reaction, Nano Lett. 23(5) (2023) 1897-1903.
[5] Y. Jin, L.P. Sun, Y.C. Wang, L.H. Huo, H. Zhao, Enhanced electrocatalytic nitrate reduction and energy conversion through Zn-Nitrate battery by Cu3P@ Co(OH)2/CF heterostructure catalyst, Int. J. Hydrogen Energy 71(2024) 820-830.
[6] S.Y. Yuan, Y.H. Xue, R.E. Ma, Q. Ma, Y.Y. Chen, J.W. Fan, Advances in iron-based electrocatalysts for nitrate reduction, Sci. Total Environ. 866(2023) 161444.
[7] X. Ma, J.P. Zhong, R.Y. Wang, D.X. Li, K. Li, L.J. Luo, C.H. Li, Zeolitic imidazolate framework derived Fe catalyst electrocatalytic-driven atomic hydrogen for efficient reduction of nitrate to N₂, J. Hazard. Mater. 471(2024) 134354.
[8] M. Duca, N. Sacre, A. Wang, S. Garbarino, D. Guay, Enhanced electrocatalytic nitrate reduction by preferentially-oriented (100) PtRh and PtIr alloys: the hidden treasures of the ‘miscibility gap’, Appl. Catal. B Environ. 221(2018) 86-96.
[9] L. Shi, Y.M. Li, S.X. He, Y.N. Liu, X.Y. Tang, L. Ao, X.S. Lv, W.Y. Fu, G.M. Jiang, Efficient electrocatalytic nitrate reduction on molecular catalyst with electron-deficient single-atom Cud+ sites, Chem. Eng. J. 495(2024) 153427.
[10] J. Martínez, A. Ortiz, I. Ortiz, State-of-the-art and perspectives of the catalytic and electrocatalytic reduction of aqueous nitrates, Appl. Catal. B Environ. 207(2017) 42-59.
[11] Q.N. Song, M. Li, J.C. Li, S. Zhang, L. Yang, X.Y. Chen, F.B. Meng, X. Liu, Simultaneous electrocatalytic removal of inorganic nitrogen compounds in groundwater: modeling and mechanistic studies, Chem. Eng. J. 430(2022) 133152.
[12] X. Ma, J.P. Zhong, W.M. Huang, R.Y. Wang, S.H. Li, Z.Y. Zhou, C.H. Li, Tuning the d-band centers of bimetallic FeNi catalysts derived from layered double hydroxides for selective electrocatalytic reduction of nitrates, Chem. Eng. J. 474(2023) 145721.
[13] X. Yan, X. Fang, S.S. Lu, H.P. Luo, L. Tan, Y. Liu, H. Chen, F. Jiang, Electrocatalytic reduction of nitrate by copper/iron oxides supported on nitrogen doped carbon spheres, J. Hazard. Mater. Adv. 10(2023) 100313.
[14] J. Hu, C. Tang, Z.H. Bi, S.X. Zhou, Q.Q. Kong, S.S. Gao, X.J. Liu, X. Zhao, G.Z. Hu, Self-supported iron-doped cobalt-copper oxide heterostructures for efficient electrocatalytic denitrification, J. Colloid Interface Sci. 675(2024) 313-325.
[15] X.H. Wu, M. Nazemi, S. Gupta, A. Chismar, K. Hong, H. Jacobs, W.Q. Zhang, K. Rigby, T. Hedtke, Q.X. Wang, E. Stavitski, M.S. Wong, C. Muhich, J.H. Kim, Contrasting capability of single atom palladium for thermocatalytic versus electrocatalytic nitrate reduction reaction, ACS Catal. 13(10) (2023) 6804-6812.
[16] X.D. Wang, M.Q. Zhu, G.S. Zeng, X. Liu, C. Fang, C.H. Li, A three-dimensional Cu nanobelt cathode for highly efficient electrocatalytic nitrate reduction, Nanoscale 12(17) (2020) 9385-9391.
[17] L.L. Chen, Y.H. Hao, J.Y. Chu, S. Liu, F.H. Bai, W.H. Luo, Electrocatalytic nitrate reduction to ammonia: a perspective on Fe/Cu-containing catalysts, Chin. J. Catal. 58(2024) 25-36.
[18] Z.X. Wang, S.Y. Xia, X.F. Deng, G. Baryshnikov, A. Kuklin, H. Ågren, H.B. Zhang, Platinum group nanoparticles doped BCN matrix: efficient catalysts for the electrocatalytic reduction of nitrate to ammonia, J. Colloid Interface Sci. 664(2024) 84-95.
[19] Y. Su, N. Chen, H.L. Ren, L.L. Guo, Z. Li, X.M. Wang, Preparation and properties of indium ion modified graphite felt composite electrode, Front. Chem. 10(2022) 899287.
[20] S.H. Huang, Y. Wang, S.Y. Qiu, J.Q. Wan, Y.W. Ma, Z.C. Yan, Q.M. Xie, In-situ fabrication from MOFs derived MnxCo_3-x@C modified graphite felt cathode for efficient electro-Fenton degradation of ciprofloxacin, Appl. Surf. Sci. 586(2022) 152804.
[21] S.Q. Yang, X.L. Wang, Z.M. Song, C.C. Liu, Z.Y. Li, J.Y. Wang, L.Z. Song, Efficient electrocatalytic nitrate reduction in neutral medium by Cu/CoP/NF composite cathode coupled with Ir-Ru/Ti anode, Chemosphere 307(Pt 4) (2022) 136132.
[22] J. Zhou, S.S. Gao, G.Z. Hu, Recent progress and perspectives on transition metal-based electrocatalysts for efficient nitrate reduction, Energy Fuels 38(8) (2024) 6701-6722.
[23] J.L. Fan, L.K. Arrazolo, J.X. Du, H.M. Xu, S.Y. Fang, Y. Liu, Z.B. Wu, J.H. Kim, X.H. Wu, Effects of ionic interferents on electrocatalytic nitrate reduction: mechanistic insight, Environ. Sci. Technol. 58(29) (2024) 12823-12845.
[24] M.Y. Zheng, Y.C. Wan, L.P. Yang, S. Ao, W.Y. Fu, Z.J. Zhang, Z.H. Huang, T. Ling, F.Y. Kang, R.T. Lv, In situ construction of Cu(I)-Cu(II) pairs for efficient electrocatalytic nitrate reduction reaction to ammonia, J. Energy Chem. 100(2025) 106-113.
[25] S. Garcia-Segura, M. Lanzarini-Lopes, K. Hristovski, P. Westerhoff, Electrocatalytic reduction of nitrate: fundamentals to full-scale water treatment applications, Appl. Catal. B Environ. 236(2018) 546-568.
[26] J.H. Wang, Z. Zhang, S.Q. Ding, Cu supported on the graphene oxide modified graphite felt electrode for highly efficient nitrate electroreduction, J. Environ. Chem. Eng. 10(3) (2022) 108092.
[27] A.L. Pang, A. Arsad, M. Ahmadipour, Synthesis and factor affecting on the conductivity of polypyrrole: a short review, Polym. Adv. Technol. 32(4) (2021) 1428-1454.
[28] Z. Li, L.L. Wang, Y.M. Cai, J.R. Zhang, W.L. Zhu, Electrochemically reconstructed copper-polypyrrole nanofiber network for remediating nitrate-containing water at neutral pH, J. Hazard. Mater. 440(2022) 129828.
[29] P. Pattanayak, N. Pramanik, P. Kumar, P.P. Kundu, Fabrication of cost-effective non-noble metal supported on conducting polymer composite such as copper/polypyrrole graphene oxide (Cu₂O/PPyeGO) as an anode catalyst for methanol oxidation in DMFC, Int. J. Hydrogen Energy 43(25) (2018) 11505-11519.
[30] Z.G. Yin, W.B. Fan, Y.H. Ding, J.X. Li, L.H. Guan, Q.D. Zheng, Shell structure control of PPy-modified CuO composite nanoleaves for lithium batteries with improved cyclic performance, ACS Sustainable Chem. Eng. 3(3) (2015) 507-517.
[31] Z.H. Liu, G. Sun, Z.J. Chen, Y. Ma, K. Qiu, M. Li, B.J. Ni, Anchoring Cu-N active sites on functionalized polyacrylonitrile fibers for highly selective H₂S/CO₂ separation, J. Hazard. Mater. 450(2023) 131084.
[32] Z.L. Li, L.B. Deng, I.A. Kinloch, R.J. Young, Raman spectroscopy of carbon materials and their composites: Graphene, nanotubes and fibres, Prog. Mater. Sci. 135(2023) 101089.
[33] Y. Lei, T.L. Li, L. Yang, Y.Y. Peng, W. Xiong, D.R. Liu, Highly efficient electrocatalytic treatment of high-concentration 4-chlorophenol wastewater on PdCu/PPy/NF composite cathode, Appl. Surf. Sci. 654(2024) 159479.
[34] Q. Li, Q. Dong, T.Y. Zhang, Z.C. Xue, J. Li, Z.N. Wang, H. Sun, Performance of room-temperature activated tubular polypyrrole modified graphite felt composite electrode in vanadium redox flow battery, Electrochim. Acta 409(2022) 139970.
[35] W. Li, C.G. Min, F. Tan, Z.P. Li, B.S. Zhang, R. Si, M.L. Xu, W.P. Liu, L.X. Zhou, Q. M. Wei, Y.Z. Zhang, X.K. Yang, Bottom-up construction of active sites in a CuN₄-C catalyst for highly efficient oxygen reduction reaction, ACS Nano 13(3) (2019) 3177-3187.
[36] Z. Li, Y.S. Wu, H.Q. Wang, Z.B. Wu, X.H. Wu, High-efficiency electrocatalytic reduction of N₂O with single-atom Cu supported on nitrogen-doped carbon, Environ. Sci. Technol. 58(20) (2024) 8976-8987.
[37] R. Hu, Y. Cui, X.J. Chen, C.X. Xu, An efficient Cu-based catalyst prepared by the one-step method of phytic acid assisted glucose for acetylene hydration, Mol. Catal. 560(2024) 114147.
[38] L.H. Zhang, Y.T. Jia, J.Y. Zhan, G.M. Liu, G.H. Liu, F. Li, F.S. Yu, Dopant-induced electronic states regulation boosting electroreduction of dilute nitrate to ammonium, Angew. Chem. Int. Ed 62(22) (2023) e202303483.
[39] Z.M. Jia, T. Feng, M.L. Ma, Z.Y. Li, L. Tang, Emerging advances in Cu-based electrocatalysts for electrochemical nitrate reduction (NO₃RR), Surf. Interfaces 48(2024) 104294.
[40] X.P. Li, J.J. Yang, X.L. Shi, Z.R. Sun, N, P Co-doped graphite felt cathode for efficient removal of ciprofloxacin in an ascorbic acid-coupled electro-Fenton process: simultaneously enhancing H₂O₂ generation and Fe³⁺/Fe²⁺ cycling, Environ. Res. 266(2025) 120577.
[41] A.M. Demeku, C.H. Guo, D.M. Kabtamu, Z.J. Huang, G.C. Chen, A.W. Bayeh, C.H. Wang, Enhanced electrochemical performance of copper-doped cobalt oxide nanowire-modified graphite felt as positive electrode material for vanadium redox flow batteries, Chem. Eng. J. 505(2025) 159170.
[42] M.C. Zhang, M.Y. Liu, M.X. Yang, X.X. Liu, S.Y. Shen, J.S. Wu, W.B. Pei, Coppercobalt bimetallic conductive metaleorganic frameworks as bifunctional oxygen electrocatalyst in alkaline and neutral media, J. Solid State Chem. 325(2023) 124133.
[43] S.Z. Liang, X. Teng, H. Xu, L.S. Chen, J.L. Shi, H* species regulation by MnCo(OH)2 for efficient nitrate electro-reduction in neutral solution, Angew. Chem. Int. Ed 63(11) (2024) e202400206.
[44] S.I. Perez Bakovic, P. Acharya, M. Watkins, H. Thornton, S.X. Hou, L.F. Greenlee, Electrochemically active surface area controls HER activity for Fe_xNi100_x films in alkaline electrolyte, J. Catal. 394(2021) 104-112.
[45] E. Tabesh, H.R. Salimijazi, M. Kharaziha, M. Mahmoudi, M. Hejazi, Development of an in situ chitosan-copper nanoparticle coating by electrophoretic deposition, Surf. Coat. Technol. 364(2019) 239-247.
[46] J. Wang, J. Feng, T.O. Soyol-Erdene, Z. Wei, W.W. Tang, Electrodeposited NiCoP on nickel foam as a self-supported cathode for highly selective electrochemical reduction of nitrate to ammonia, Sep. Purif. Technol. 320(2023) 124155.
[47] X.R. Hu, M.M. Zhang, C. Lai, M. Cheng, F.H. Xu, D.S. Ma, L. Li, H.C. Yan, H. Sun, X. Fan, B.T. Wang, Metal-organic frameworks derived low-cost Cu-doped Co₃O₄ for efficient reduction of ultra-low nitrate concentrations to ammonia, Chem. Eng. J. 493(2024) 152543.
[48] J. Sun, D. Alam, R. Daiyan, H. Masood, T.Q. Zhang, R.W. Zhou, P.J. Cullen, E.C. Lovell, A. Jalili, R. Amal, A hybrid plasma electrocatalytic process for sustainable ammonia production, Energy Environ. Sci. 14(2) (2021) 865-872.
[49] S. Meng, Y. Ling, M.Y. Yang, X.G. Zhao, A.I. Osman, A.H. Al-Muhtaseb, D.W. Rooney, P.S. Yap, Recent research progress of electrocatalytic reduction technology for nitrate wastewater: a review, J. Environ. Chem. Eng. 11(2) (2023) 109418.
[50] Y.C. Feng, T. Su, Y.H. Gong, H.B. Yu, W.C. Qin, M.X. Huo, Enhanced electrocatalytic reduction of nitrate over a ternary alloy catalyst of CuPdFe: structure, performance, and mechanism, J. Environ. Chem. Eng. 12(3) (2024) 112700.
[51] L. He, T.J. Zeng, F.B. Yao, Y. Zhong, C. Tan, Z.J. Pi, K.J. Hou, S.J. Chen, X.M. Li, Q. Yang, Electrocatalytic reduction of nitrate by carbon encapsulated Cu-Fe electroactive nanocatalysts on Ni foam, J. Colloid Interface Sci. 634(2023) 440-449.
[52] C. Wang, Z.F. Cao, H.T. Huang, H. Liu, S. Wang, Electrocatalytic reduction of nitrate via Co₃O₄/Ti cathode prepared by electrodeposition paired with IrO₂- RuO₂ anode, Front. Chem. 10(2022) 900962.
[53] C.Y. Li, J. Yang, C.B. Zhang, C. Wang, C. Lyu, K. Fan, Study on catalytic performance in CO₂ hydrogenation to methanol over AueCu/C₃N₄ catalysts, Catalysts 14(8) (2024) 470.
[54] Z.R. Shen, J.B. Yan, M. Wang, L.D. Xing, B.J. Huang, H.Y. Zhou, W.B. Li, L.S. Chen, J.L. Shi, Cu/Cu+ synergetic effect in Cu₂O/Cu/CF electrocatalysts for efficient nitrate reduction to ammonia, ACS Sustainable Chem. Eng. 11(25) (2023) 9433-9441.
[55] M. Liu, Z.H. Lu, L.H. Yang, R.M. Gao, X.Y. Zhang, Y.J. Wang, Y.H. Wang, Co-N bond promotes the H* pathway for the electrocatalytic reduction of nitrate (NO₃RR) to ammonia, J. Environ. Chem. Eng. 11(3) (2023) 109718.
[56] Y. Li, J.X. Ma, T. David Waite, M.R. Hoffmann, Z.W. Wang, Development of a mechanically flexible 2D-MXene membrane cathode for selective electrochemical reduction of nitrate to N₂: mechanisms and implications, Environ. Sci. Technol. 55(15) (2021) 10695-10703.
[57] Y. Shi, Y.M. Li, R.J. Li, X.G. Zhao, Y.L. Yu, M. Yang, In-situ reconstructed Cu/ Cu₂O heterogeneous nanorods with oxygen vacancies for enhanced electrocatalytic nitrate reduction to ammonia, Chem. Eng. J. 479(2024) 147574.