Combustion Synthesis of La0.8Sr0.2MnO3 and Its Effect on HMX Thermal Decomposition

Abstract

Abstract: Perovskite-type La_0.8Sr_0.2MnO₃ was prepared by stearic acid gel combustion method.The obtained powders were characterized by X-ray diffraction(XRD),Fourier transform infrared spectroscopy(FT-IR),scaning electron micrograph(SEM)and X-ray photoelectron spectroscopy(XPS)techniques.The catalytic activity of La_0.8Sr_0.2MnO₃ was investigated on thermal decomposition of octahydro-1,3,5,7-tetranitro-1,3,5,7-tetrazocine (HMX)by thermal gravity-differential scanning calorimetry(TG-DSC)techniques.The experimental results show that La_0.8Sr_0.2MnO₃ is an effective catalyst for HMX thermal decomposition.The surface-adsorbed species such as H₂O,OH^- and adsorbed oxygen(Oad)could result in an advance in the onset temperature of HMX thermal decomposition.The mixture system of Mn³⁺ and Mn⁴⁺ ions and lattice oxygen could play key roles for the increase of the decomposition heat of HMX because these exothermic reactions could be catalyzed by La_0.8Sr_0.2MnO₃ between CO and NO_x(from the thermal decomposition of HMX)and the oxidation reaction of CO.According to the previous researches and our results,perovskite-type La_0.8Sr_0.2MnO₃ may be used as a novel catalyst or modifier for nitrate ester plasticized polyether(NEPE)propellant.

Key words: stearic acid gel combustion synthesis, perovskite-type La_0.8Sr_0.2MnO₃, octahydro-1,3,5,7-tetranitro-1,3,5,7-tetrazocine, thermal decomposition

摘要： Perovskite-type La_0.8Sr_0.2MnO₃ was prepared by stearic acid gel combustion method.The obtained powders were characterized by X-ray diffraction(XRD),Fourier transform infrared spectroscopy(FT-IR),scaning electron micrograph(SEM)and X-ray photoelectron spectroscopy(XPS)techniques.The catalytic activity of La_0.8Sr_0.2MnO₃ was investigated on thermal decomposition of octahydro-1,3,5,7-tetranitro-1,3,5,7-tetrazocine (HMX)by thermal gravity-differential scanning calorimetry(TG-DSC)techniques.The experimental results show that La_0.8Sr_0.2MnO₃ is an effective catalyst for HMX thermal decomposition.The surface-adsorbed species such as H₂O,OH^- and adsorbed oxygen(Oad)could result in an advance in the onset temperature of HMX thermal decomposition.The mixture system of Mn³⁺ and Mn⁴⁺ ions and lattice oxygen could play key roles for the increase of the decomposition heat of HMX because these exothermic reactions could be catalyzed by La_0.8Sr_0.2MnO₃ between CO and NO_x(from the thermal decomposition of HMX)and the oxidation reaction of CO.According to the previous researches and our results,perovskite-type La_0.8Sr_0.2MnO₃ may be used as a novel catalyst or modifier for nitrate ester plasticized polyether(NEPE)propellant.

关键词: stearic acid gel combustion synthesis, perovskite-type La_0.8Sr_0.2MnO₃, octahydro-1,3,5,7-tetranitro-1,3,5,7-tetrazocine, thermal decomposition

WANG Yan, GONG Lei, LI Yanbin, WEI Zhixian. Combustion Synthesis of La_0.8Sr_0.2MnO₃ and Its Effect on HMX Thermal Decomposition[J]. , 2010, 18(3): 397-401.

王艳, 龚磊, 李延斌, 卫芝贤. Combustion Synthesis of La_0.8Sr_0.2MnO₃ and Its Effect on HMX Thermal Decomposition[J]. , 2010, 18(3): 397-401.

References

1 Dinka, P., Mukasyan, A.S., “Perovskite catalysts for the auto-reforming of sulfur containing fuels”, J. Power Sources, 167, 472-481(2007).
2 Niu, J.R., Deng, J.G., Liu, W., Zhang, L., Wang, G.Z., Dai, H.X., He, H., Zi, X.H., “Nanosized perovskite-type oxides La_1-xSr_xMO_3-δ(M=Co, Mn; x=0, 0.4) for the catalytic removal of ethylacetate”, Catal. Today, 126, 420-429(2007).
3 Delmastro, A., Mazza, D., Ronchetti, S., Vallino, M., Spinicci, R., Brovetto, P., Salis, M., “Synthesis and characterization of non-stoichiometric LaFeO₃ perovskite”, Mater. Sci. Eng. B-Solid State Mater. Adv. Technol., 79, 140-145(2001).
4 Grossin, D., Noudem, J.G., “Synthesis of fine La_0.8Sr_0.2MnO₃ powder by different ways”, Solid State Sci., 6, 939-944(2004).
5 Chaichanawong, J., Sato, K., Abe, H., Murata, K., Fukui, T., Charinpanitkul, T., Tanthapanichakoon, W., Naito, M., “Formation of strontium-doped lanthanum manganite(La_0.8Sr_0.2MnO₃) by mechanical milling without media balls”, Advanced Powder Technol, 17, 613-622(2006).
6 Stepanov, R.S., Kruglyakova, L.A., Astakhov, A.M., Pekhotin, K.V., “Effect of metal formiates and oxalates on HMX decomposition”, Comb. Explos. Shock Waves, 40, 576-579(2004).
7 Liu, Z.R., Yin, C.M., Liu, Y., Zhao, F.Q., Luo, Y., “Catalytic effects of nanometal oxides on the decomposition of HMX”, J. Ener. Mater.(Chin), 13(5), 278-283(2005).(in Chinese)
8 Jiang, Z., Li, S.F., Zhao, F.Q., Chen, P., Yin, C.M., Li, S.W., “Effect of nano metal powder on the thermal decomposition characteristics of HMX”, J. Propulsion Tech.(Chin), 23(3), 258-261(2002).(in Chinese)
9 Wei, Z.X., Xu, Y.Q., Liu, H.Y., Hu, C.W., “Preparation and catalytic activities of LaFeO₃ and Fe₂O₃ for HMX thermal decomposition”, J. Hazardous Mater., 165, 1056-1061(2009).
10 Fu, C.J., Su, K.N., Zhang, N.Q., Zhou, D.R., “Preparation of ultrafine La_0.8Sr_0.2MnO_3-δ powders by low temperature combustion synthesis”, J. Funct. Mater., 37, 925-928(2006).(in Chinese)
11 Ponce, S., Pe a, M.A., Fierro, J.L.G., “Surface properties and catalytic performance in methane combustion of Sr-substituted lanthanum manganites”, Appl. Catal. B:Environ., 24, 193-205(2004).
12 Wu, L., Yu, J.C., Zhang, L.Z., Wang, X.C., Li, S.K., “Selective self-propagating combustion synthesis of hexagonal and orthorhombic nanocrystalline yttrium iron oxide”, J. Solid State Chem., 177, 3666-3674(2004).
13 Nagabhushana, B.M., Sreekanth, C.R.P., Ramesh, K.P.K.P., Shivakumara, C., Chandrappa, G.T., “Combustion synthesis, characterization and metal-insulator transition studies of nanocrystalline La_1-xCa_xMnO₃(0.0≤x≤0.5″)”, Mater. Chem. Phys, 102, 47-52(2007).
14 Milt, V.G., Spretz, R., Ulla, M.A., Lombardo, E.A., García, F.J.L., “The nature of active sites for the oxidation of methane on La-based perovskites”, Catal. Lett., 42, 57-63(1996).
15 Wei, Z.X., Wei, L., Gong, L., Wang, Y., Hu, C.W., “Combustion synthesis and effect of LaMnO₃ and La_0.8Sr_0.2MnO₃ on RDX thermal decomposition”, J. Hazardous Mater., 177, 554-559(2010).
16 Barbara, K., W odzimierz, T., “Partial substitution of lanthanum with silver in the LaMnO₃ perovskite:Effect of the modification on the activity of monolithic catalysts in the reactions of methane and carbon oxide oxidation”, Appl. Catal. A:General, 335, 28-36(2008).
17 Zeman, S., Shu, Y., Friedl, Z., Vágenknecht, J., “Thermal reactivity of some nitroand nitroso-compounds derived from 1,3,5,7tetraazabicyclo[3.3.1] nonane at contamination by ammonium nitrate”, J. Hazardous Mater., A, 121, 11-21(2005).
18 Richard, B.J., “Thermal decomposition of energetic materials:Temporal behaviors of the rates of formation of the gaseous pyrolysis products from condensed-phase decomposition of octahydro-l,3,5,7-tetranitro-l,3,5,7-tetrazocine”, J. Phys. Chem., 94, 6706-6718(1990).
19 Pe a, M.A., Fierro, J.L.G., “Chemical structures and performance of perovskite oxides”, Chem. Rev, 101, 1981-2018(2001).
20 Lin, P.Y., Fu, Y.L., Yu, S.M., “An approch to the oxidation reaction mechanism of CO on La_0.5Sr_0.5MnO₃ ”, J. Catal., 2, 186-193(1981).(in Chinese)
21 Teng, F., Han, W., Liang, S.H., Gaugeu, B., Zong, R.L., Zhu, Y.F., “Catalytic behavior of hydrothermally synthesized La_0.5Sr_0.5MnO₃ single-crystal cubes in the oxidation of CO and CH₄”, J. Catal., 250, 1-11(2007).
22 Labhsetwar, N., Biniwale, R. B., Kumar, R., Rayalu, S., Devotta, S., “Application of supported perovskite-type catalysts for vehicular emission control”, Catalysis Surveys from Asia, 10, 55-64(2006).
23 Gongwer, P.E., Brill, T.B., “Thermal decomposition of energetic materials 73:The identity and temperature dependence of minor products from flash-heated RDX”, Combust. Flame, 115, 417-423(1998).
24 Li, J.F., Si, F.M., “Study on modification technology of the combustion property of the NEPE propellant”, J. Ener. Mater., 10, 4-9(2002).(in Chinese)

[1]	Yan Cao, Yafang Chi, Ammar Muhammad, Peng He, liguo Wang, Huiquan Li. Non-phosgene synthesis of hexamethylene-1,6-diisocyanate from thermal decomposition of hexamethylene-1,6-dicarbamate over Zn–Co bimetallic supported ZSM-5 catalyst [J]. Chinese Journal of Chemical Engineering, 2019, 27(3): 549-555.
[2]	Weizao Liu, Xiaomei Wang, Zhenpu Lu, Hairong Yue, Bin Liang, Li Lü, Chun Li. Preparation of synthetic rutile via selective sulfation of ilmenite with (NH₄)₂SO₄ followed by targeted removal of impurities [J]. , 2017, 25(6): 821-828.
[3]	Hongying Hao, Yadong Zhang, Xiaoya Chen. Investigation on specific heat capacity and thermal behavior of sodium hydroxyethyl sulfonate [J]. , 2017, 25(3): 319-323.
[4]	Muhammad Ammar, Yan Cao, Peng He, Liguo Wang, Jiaqiang Chen, Huiquan Li. An efficient green route for hexamethylene-1,6-diisocyanate synthesis by thermal decomposition of hexamethylene-1,6-dicarbamate over Co₃O₄/ZSM-5 catalyst: An indirect utilization of CO₂ [J]. Chin.J.Chem.Eng., 2017, 25(12): 1760-1770.
[5]	LI Mingchun, ZHAO Zhongliang, JING Yu, LIU Jiatao, WU Yusheng. The Soret and Dufour Effects in Non-thermal Equilibrium Packed Beds with Forced Convection and Endothermic Reactions [J]. Chin.J.Chem.Eng., 2013, 21(8): 867-875.
[6]	NONG Weijian, CHEN Xiaopeng, WANG Linlin, LIANG Jiezhen, ZHONG Lingping, TONG Zhangfa . Thermal Decomposition Kinetics of Abietic Acid in Static Air [J]. Chin.J.Chem.Eng., 2013, 21(7): 724-729.
[7]	LIANG Rui, YANG Meirong, XUAN Xiaopeng. Thermal Stability and Thermal Decomposition Kinetics of 1-Butyl-3-methylimidazolium Dicyanamide [J]. , 2010, 18(5): 736-741.
[8]	JING Qi, LÜ Xiuyang. Kinetics of Non-catalyzed Decomposition of Glucose in High-temperature Liquid Water [J]. , 2008, 16(6): 890-894.
[9]	FENGXiaogui,JINGShan,WUQiulin,CHENJing,SONGChongli. Thermal decomposition of potassium titanium hexacyanoferrate(II) loaded with cesium in a fixed bed calciner [J]. , 2007, 15(2): 184-189.
[10]	LIU Runjing, CHEN Jianfeng, GUO Fen, YUN Jimmy, SHEN Zhigang. Kinetics and Mechanism of Decomposition of Nano-sized Calcium Carbonate under Non- isothermal Condition [J]. , 2003, 11(3): 302-306.

Combustion Synthesis of La_0.8Sr_0.2MnO₃ and Its Effect on HMX Thermal Decomposition

Combustion Synthesis of La_0.8Sr_0.2MnO₃ and Its Effect on HMX Thermal Decomposition

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 10

Recommended Articles

Metrics

Comments