Fouling behavior of poly(vinylidene fluoride) (PVDF) ultrafiltration membrane by polyvinyl alcohol (PVA) and chemical cleaning method

doi:10.1016/j.cjche.2020.05.032

Abstract

Abstract: Severe fouling to poly(vinylidene fluoride) (PVDF) membrane is usually caused as filtrating the papermaking wastewater in the ultrafiltration (UF) process. In the paper, fouling behavior and mechanism were investigated, and the low-concentration polyvinyl alcohol (PVA) contained in the sedimentation tank wastewater was found as the main foulant. Consequently, the corresponding cleaning approach was proposed. The experiment and modeling results elaborated that the fouling mode developed from pore blockage to cake layer along with filtration time. Chemical cleaning conditions including the composition and concentration of reagents, cleaning duration and trans-membrane pressure were investigated for their effect on cleaning efficiency. Pure water flux was recovered by over 95% after cleaning the PVDF membrane using the optimal conditions 0.5 wt% NaClO (as oxidant) and 0.1 wt% sodium dodecyl benzene sulfonate (SDBS, as surfactant) at 0.04 MPa for 100 min. In the chemical cleaning method, hypochlorite (ClO^-) could first chain-scissor PVA macromolecules to small molecules and SDBS could wrap the fragments in micelles, so that the foulants were removed from the pores and surface of membrane. After eight cycling tests, pure water flux recovery maintained above 95% and the reused membrane was found intact without defects.

Key words: PVDF membrane, Fouling, PVA, Chemical cleaning

摘要： Severe fouling to poly(vinylidene fluoride) (PVDF) membrane is usually caused as filtrating the papermaking wastewater in the ultrafiltration (UF) process. In the paper, fouling behavior and mechanism were investigated, and the low-concentration polyvinyl alcohol (PVA) contained in the sedimentation tank wastewater was found as the main foulant. Consequently, the corresponding cleaning approach was proposed. The experiment and modeling results elaborated that the fouling mode developed from pore blockage to cake layer along with filtration time. Chemical cleaning conditions including the composition and concentration of reagents, cleaning duration and trans-membrane pressure were investigated for their effect on cleaning efficiency. Pure water flux was recovered by over 95% after cleaning the PVDF membrane using the optimal conditions 0.5 wt% NaClO (as oxidant) and 0.1 wt% sodium dodecyl benzene sulfonate (SDBS, as surfactant) at 0.04 MPa for 100 min. In the chemical cleaning method, hypochlorite (ClO^-) could first chain-scissor PVA macromolecules to small molecules and SDBS could wrap the fragments in micelles, so that the foulants were removed from the pores and surface of membrane. After eight cycling tests, pure water flux recovery maintained above 95% and the reused membrane was found intact without defects.

关键词: PVDF membrane, Fouling, PVA, Chemical cleaning

Weijie Ding, Min Chen, Ming Zhou, Zhaoxiang Zhong, Zhaoliang Cui, Weihong Xing. Fouling behavior of poly(vinylidene fluoride) (PVDF) ultrafiltration membrane by polyvinyl alcohol (PVA) and chemical cleaning method[J]. Chinese Journal of Chemical Engineering, 2020, 28(12): 3018-3026.

References

[1] G. Kang, Y. Cao, Application and modification of poly(vinylidene fluoride) (PVDF) membranes-A review, J. Membr. Sci. 463(2014) 145-165.
[2] V. Buscio, M. Crespi, C. Gutiérrez-Bouzán, Application of PVDF ultrafiltration membranes to treat and reuse textile wastewater, Desalin. Water Treat. 57(2015) 8090-8096.
[3] T.A. Otitoju, A.L. Ahmad, B.S. Ooi, Polyvinylidene fluoride (PVDF) membrane for oil rejection from oily wastewater:A performance review, J. Water Process Eng. 14(2016) 41-59.
[4] Y. Wang, X. Chen, J. Zhang, J. Yin, H. Wang, Investigation of microfiltration for treatment of emulsified oily wastewater from the processing of petroleum products, Desalination 249(2009) 1223-1227.
[5] L. Juang, D. Tseng, H. Lin, Membrane processes for water reuse from the effluent of industrial park wastewater treatment plant:A study on flux and fouling of membrane, Desalination 202(2007) 302-309.
[6] L. Wang, R. Miao, X. Wang, Y. Lv, X. Meng, Y. Yang, D. Huang, L. Feng, Z. Liu, K. Ju, Fouling behavior of typical organic foulants in polyvinylidene fluoride ultrafiltration membranes:Characterization from microforces, Environ. Sci. Technol. 47(2013) 3708-3714.
[7] R. Miao, L. Wang, L. Feng, Z. Liu, Y. Lv, Understanding PVDF ultrafiltration membrane fouling behaviour through model solutions and secondary wastewater effluent, Desalin. Water Treat. 52(2014) 5061-5067.
[8] M.F. Rabuni, N.M.N. Sulaiman, M.K. Aroua, C.Y. Chee, N.A. Hashim, Impact of in situ physical and chemical cleaning on PVDF membrane properties and performances, Chem. Eng. Sci. 122(2015) 426-435.
[9] G. Liu, L. Li, L. Qiu, S. Yu, P. Liu, Y. Zhu, J. Hu, Z. Liu, D. Zhao, H. Yang, Chemical cleaning of ultrafiltration membranes for polymer-flooding wastewater treatment:Efficiency and molecular mechanisms, J. Membr. Sci. 545(2018) 348-357.
[10] X. Wang, J. Ma, Z. Wang, H. Chen, M. Liu, Z. Wu, Reinvestigation of membrane cleaning mechanisms using NaOCl:Role of reagent diffusion, J. Membr. Sci. 550(2018) 278-285.
[11] N. Porcelli, S. Judd, Chemical cleaning of potable water membranes:A review, Sep. Purif. Technol. 71(2010) 137-143.
[12] V. Puspitasari, A. Granville, P. Le-Clech, V. Chen, Cleaning and ageing effect of sodium hypochlorite on polyvinylidene fluoride (PVDF) membrane, Sep. Purif. Technol. 72(2010) 301-308.
[13] Q. Wang, H. Zeng, Z. Wu, J. Cao, Impact of sodium hypochlorite cleaning on the surface properties and performance of PVDF membranes, Appl. Surf. Sci. 428(2018) 289-295.
[14] E. Garmsiri, Y. Rasouli, M. Abbasi, A.A. Izadpanah, Chemical cleaning of mullite ceramic microfiltration membranes which are fouled during oily wastewater treatment, J. Water Process Eng. 19(2017) 81-95.
[15] X. Shi, G. Tal, N.P. Hankins, V. Gitis, Fouling and cleaning of ultrafiltration membranes:A review, J. Water Process Eng. 1(2014) 121-138.
[16] P. Chen, Z. Zhong, F. Liu, W. Xing, Cleaning ceramic membranes used in treating desizing wastewater with a complex-surfactant SDBS-assisted method, Desalination 365(2015) 25-35.
[17] L. Wang, Q. Wang, Y. Li, H. Lin, Ultrasound-assisted chemical cleaning of polyvinylidene fluoride membrane fouled by lactic acid fermentation broth, Desalination 326(2013) 103-108.
[18] D. Kuzmenko, E. Arkhangelsky, S. Belfer, V. Freger, Chemical cleaning of UF membranes fouled by BSA, Desalination 179(2005) 323-333.
[19] Z. Wang, Y. Li, P. Song, X. Wang, NaCl cleaning of 0.1μm polyvinylidene fluoride (PVDF) membrane fouled with humic acid (HA), Chem. Eng. Res. Des. 132(2018) 325-337.
[20] M. Wiśniewska, K. Szewczuk-Karpisz, I. Ostolska, T. Urban, K. Terpiłowski, V.I. Zarko, V.M. Gun'ko, Effect of polyvinyl alcohol adsorption on the mixed alumina-silica-titania suspension stability, J. Ind. Eng. Chem. 23(2015) 265-272.
[21] E. Lee, A.K.J. An, P. Hadi, D.Y.S. Yan, Characterizing flat sheet membrane resistance fraction of chemically enhanced backflush, Chem. Eng. J. 284(2016) 61-67.
[22] K.L. Zeng, J. Zhou, Z.L. Cui, Y. Zhou, C. Shi, X.Z. Wang, L.Y. Zhou, X.B. Ding, Z.H. Wang, E. Drioli, Insight into fouling behavior of poly(vinylidene fluoride) (PVDF) hollow fiber membranes caused by dextran with different pore size distributions, Chin. J. Chem. Eng. 26(2018) 268-277.
[23] S. Lee, M. Dilaver, P. Park, J. Kim, Comparative analysis of fouling characteristics of ceramic and polymeric microfiltration membranes using filtration models, J. Membr. Sci. 432(2013) 97-105.
[24] C. Ho, A.L. Zydney, A combined pore blockage and cake filtration model for protein fouling during microfiltration, J. Colloid Interface Sci. 232(2000) 389-399.
[25] W. Lang, Z. Xuan, J. Shen, H. Xu, Z. Xu, Y. Guo, The contrastive study of chemical treatment on the properties of PVDF/PFSA and PVDF/PVP ultrafiltration membranes, Desalination 341(2014) 72-82.
[26] L. Marbelia, M.R. Bilad, I.F.J. Vankelecom, Gradual PVP leaching from PVDF/PVP blend membranes and its effects on membrane fouling in membrane bioreactors, Sep. Purif. Technol. 213(2019) 276-282.
[27] W. Wu, X. Zhang, L. Qin, X. Li, Q. Meng, C. Shen, G. Zhang, Enhanced MPBR with polyvinylpyrrolidone-graphene oxide/PVDF hollow fiber membrane for efficient ammonia nitrogen wastewater treatment and high-density chlorella cultivation, Chem. Eng. J. 379(2020), 122368.