Abstract: Three transition metal-like facet centered cubic structured transition metal nitrides, γ-Mo₂N, β-W₂N and δ-NbN, are synthesized and applied in the reaction of CO₂ hydrogenation to CO. Among the three nitride catalysts, the γ-Mo₂N exhibits superior activity to target product CO, which is 4.6 and 76 times higher than the other two counterparts of β-W₂N and δ-NbN at 600 ℃, respectively. Additionally, γ-Mo₂N exhibits excellent stability on both cyclic heating–cooling and high space velocity steady state operation. The deactivation degree of cyclic heating–cooling evaluation after 5 cycles and long-term stability performance at 773 and 873 K in 50 h are all less than 10%. In-situ XRD and kinetic studies suggest that the γ-Mo₂N itself is able to activate both of the reactants CO₂ and H₂. Below 400 ℃, the reaction mainly occurs at the surface of γ-Mo₂N catalyst. CO₂ and H₂ competitively adsorbe on the surface of catalyst and CO₂ is the relatively stronger surface adsorbate. At a higher temperature, the interstitial vacancies of the γ-Mo₂N can be reversibly filled with the oxygen from CO₂ dissociation. Both of the surface and bulk phase sites of γ-Mo₂N participate in the high temperature CO₂ hydrogenation pathway.

Key words: Carbon dioxide, Chemical reaction, Catalysis, Reverse water gas shift (RWGS) reaction, Transition metal nitride, In-situ X-ray diffraction characterization

摘要： Three transition metal-like facet centered cubic structured transition metal nitrides, γ-Mo₂N, β-W₂N and δ-NbN, are synthesized and applied in the reaction of CO₂ hydrogenation to CO. Among the three nitride catalysts, the γ-Mo₂N exhibits superior activity to target product CO, which is 4.6 and 76 times higher than the other two counterparts of β-W₂N and δ-NbN at 600 ℃, respectively. Additionally, γ-Mo₂N exhibits excellent stability on both cyclic heating–cooling and high space velocity steady state operation. The deactivation degree of cyclic heating–cooling evaluation after 5 cycles and long-term stability performance at 773 and 873 K in 50 h are all less than 10%. In-situ XRD and kinetic studies suggest that the γ-Mo₂N itself is able to activate both of the reactants CO₂ and H₂. Below 400 ℃, the reaction mainly occurs at the surface of γ-Mo₂N catalyst. CO₂ and H₂ competitively adsorbe on the surface of catalyst and CO₂ is the relatively stronger surface adsorbate. At a higher temperature, the interstitial vacancies of the γ-Mo₂N can be reversibly filled with the oxygen from CO₂ dissociation. Both of the surface and bulk phase sites of γ-Mo₂N participate in the high temperature CO₂ hydrogenation pathway.

关键词: Carbon dioxide, Chemical reaction, Catalysis, Reverse water gas shift (RWGS) reaction, Transition metal nitride, In-situ X-ray diffraction characterization