Ultrasonic cavitation-enabled microfluidic approach toward the continuous synthesis of cesium lead halide perovskite nanocrystals

doi:10.1016/j.cjche.2022.12.001

Abstract

Abstract: Ligand assisted reprecipitation (LARP) is a widely used method for cesium lead halide perovskite nanocrystals (NCs) synthesis. Nevertheless, the ultrafast kinetics of LARP, as well as the inefficient transport properties and discontinuity of batch reactors, challenge the particle size control and experimental repeatability. To address these issues, an ultrasonic cavitation-enabled microfluidic approach was developed to achieve the continuous synthesis of cesium lead halide perovskite via LARP. It was found that the mixing between the good solvent and antisolvent in the microchannel was greatly enhanced by intensive ultrasonic cavitation. The mixing time could be reduced to below 10 ms under the irradiation of 35 W ultrasound. By modulating the mixing degree, LARP was proved to be a mixing-sensitive process. The effects of ultrasonic power, ultrasonic treatment time, total flow rate, water additive, and reprecipitation temperature on the synthesis of CsPbBr₃ NCs were systematically investigated. As compared to CsPbBr₃ NCs synthesized in the batch reactor, the sample synthesized via the ultrasonic cavitation-enabled microfluidic approach possessed stronger photoluminescence intensity and better repeatability. Moreover, the ultrasonic cavitation-enabled microfluidic approach could also realize the continuous synthesis of cesium lead halide perovskite NCs with different halide compositions to cover a wide visible spectrum (426-661 nm). The ultrasonic cavitation-enabled microfluidic approach paved the way for the large-scale of high-quality cesium lead halide perovskite NCs.

Key words: Microreactor, Ultrasound, Mixing, CsPbBr₃ nanocrystals, Synthesis

摘要： Ligand assisted reprecipitation (LARP) is a widely used method for cesium lead halide perovskite nanocrystals (NCs) synthesis. Nevertheless, the ultrafast kinetics of LARP, as well as the inefficient transport properties and discontinuity of batch reactors, challenge the particle size control and experimental repeatability. To address these issues, an ultrasonic cavitation-enabled microfluidic approach was developed to achieve the continuous synthesis of cesium lead halide perovskite via LARP. It was found that the mixing between the good solvent and antisolvent in the microchannel was greatly enhanced by intensive ultrasonic cavitation. The mixing time could be reduced to below 10 ms under the irradiation of 35 W ultrasound. By modulating the mixing degree, LARP was proved to be a mixing-sensitive process. The effects of ultrasonic power, ultrasonic treatment time, total flow rate, water additive, and reprecipitation temperature on the synthesis of CsPbBr₃ NCs were systematically investigated. As compared to CsPbBr₃ NCs synthesized in the batch reactor, the sample synthesized via the ultrasonic cavitation-enabled microfluidic approach possessed stronger photoluminescence intensity and better repeatability. Moreover, the ultrasonic cavitation-enabled microfluidic approach could also realize the continuous synthesis of cesium lead halide perovskite NCs with different halide compositions to cover a wide visible spectrum (426-661 nm). The ultrasonic cavitation-enabled microfluidic approach paved the way for the large-scale of high-quality cesium lead halide perovskite NCs.

关键词: Microreactor, Ultrasound, Mixing, CsPbBr₃ nanocrystals, Synthesis

Mingzhi Li, Zhikai Liu, Wang Yao, Chao Xu, Yangping Yu, Mei Yang, Guangwen Chen. Ultrasonic cavitation-enabled microfluidic approach toward the continuous synthesis of cesium lead halide perovskite nanocrystals[J]. Chinese Journal of Chemical Engineering, 2023, 59(7): 32-41.

References

[1] H.F. Zhao, Z.J. Hu, L.F. Wei, P. Zeng, C.Y. Kuang, X.C. Liu, S. Bai, F. Gao, M.Z. Liu, Efficient and high-luminance perovskite light-emitting diodes based on CsPbBr3 nanocrystals synthesized from a dual-purpose organic lead source, Small 16 (46) (2020) 2003939.
[2] Q. Wang, Y. Tong, H.T. Ye, X.J. Liang, K.Q. Yang, W.D. Xiang, Dual-protective CsPbX₃ perovskite nanocomposites with improved stability for upconverted lasing and backlight displays, ACS Sustain. Chem. Eng. 9 (34) (2021) 11548-11555.
[3] Y. Cheng, S.D. Ling, Y.H. Geng, Y.D. Wang, J.H. Xu, Microfluidic synthesis of quantum dots and their applications in bio-sensing and bio-imaging, Nanoscale Adv. 3 (8) (2021) 2180-2195.
[4] D.Q. Chen, X. Chen, Luminescent perovskite quantum dots: Synthesis, microstructures, optical properties and applications, J. Mater. Chem. C 7 (6) (2019) 1413-1446.
[5] X.M. Li, Y. Wu, S.L. Zhang, B. Cai, Y. Gu, J.Z. Song, H.B. Zeng, CsPbX₃ quantum dots for lighting and displays: Room-temperature synthesis, photoluminescence superiorities, underlying origins and white light-emitting diodes, Adv. Funct. Mater. 26 (15) (2016) 2435-2445.
[6] S.H. Tu, M. Chen, L.M. Wu, Nucleation-controlled growth of ultra-small perovskite quantum dots for bright blue light-emitting diodes, J. Mater. Chem. C 9 (48) (2021) 17444-17450.
[7] Y.H. Geng, J.Z. Guo, H.Q. Wang, S.D. Ling, Z. Chen, S. Chen, J.H. Xu, Large-scale production of ligand-engineered robust lead halide perovskite nanocrystals by a droplet-based microreactor system, Small 18 (19) (2022) 2200740.
[8] R.W. Epps, K.C. Felton, C.W. Coley, M. Abolhasani, Automated microfluidic platform for systematic studies of colloidal perovskite nanocrystals: Towards continuous nano-manufacturing, Lab Chip 17 (23) (2017) 4040-4047.
[9] R. Radjagobalou, J.F. Blanco, L. Petrizza, M. Le Bechec, O. Dechy-Cabaret, S. Lacombe, M. Save, K. Loubiere, Efficient photooxygenation process of biosourced α-terpinene by combining controlled LED-driven flow photochemistry and rose bengal-anchored polymer colloids, ACS Sustain. Chem. Eng. 8 (50) (2020) 18568-18576.
[10] Y. Tang, L.S. Rao, Z.T. Li, H.G. Lu, C.M. Yan, S.D. Yu, X.R. Ding, B.H. Yu, Rapid synthesis of highly photoluminescent nitrogen-doped carbon quantum dots via a microreactor with foamy copper for the detection of Hg²⁺ ions, Sens. Actuators B Chem. 258 (2018) 637-647.
[11] Y.H. Geng, J.Z. Guo, D.L. Si, X.J. Wu, H.Y. Liu, Z. Chen, S. Chen, J.H. Xu, A nano-liter droplet-based microfluidic reactor serves as continuous large-scale production of inorganic perovskite nanocrystals, Sci. China Mater. 65 (10) (2022) 2746-2754.
[12] I. Lignos, S. Stavrakis, G. Nedelcu, L. Protesescu, A.J. de Mello, M.V. Kovalenko, Synthesis of cesium lead halide perovskite nanocrystals in a droplet-based microfluidic platform: Fast parametric space mapping, Nano Lett. 16 (3) (2016) 1869-1877.
[13] X.B. Tang, F.Q. Yang, Kinetic analysis of the growth behavior of perovskite CsPbBr₃ nanocrystals in a microfluidic system, Lab Chip 22 (15) (2022) 2832-2843.
[14] P.C. Lin, H.B. Chen, Z. Wei, Y.R. Lin, J.H. Lin, Y. Chen, Z.D. Cheng, Continuous-flow synthesis of doped all-inorganic perovskite nanocrystals enabled by a microfluidic reactor for light-emitting diode application, Sci. China Mater. 63 (8) (2020) 1526-1536.
[15] S.I. Kawasaki, K. Sue, R. Ookawara, Y. Wakashima, A. Suzuki, Y. Hakuta, K. Arai, Engineering study of continuous supercritical hydrothermal method using a T-shaped mixer: Experimental synthesis of NiO nanoparticles and CFD simulation, J. Supercrit. Fluids 54 (1) (2010) 96-102.
[16] N. Kockmann, T. Kiefer, M. Engler, P. Woias, Convective mixing and chemical reactions in microchannels with high flow rates, Sens. Actuators B Chem. 117 (2) (2006) 495-508.
[17] S.N. Zhao, C.Q. Yao, Q. Zhang, G.W. Chen, Q. Yuan, Acoustic cavitation and ultrasound-assisted nitration process in ultrasonic microreactors: The effects of channel dimension, solvent properties and temperature, Chem. Eng. J. 374 (2019) 68-78.
[18] W.M. Yang, H.F. Yang, W.H. Ding, B. Zhang, L. Zhang, L.X. Wang, M.X. Yu, Q.T. Zhang, High quantum yield ZnO quantum dots synthesizing via an ultrasonication microreactor method, Ultrason. Sonochem. 33 (2016) 106-117.
[19] H.A. Vaidya, Ö. Ertunç, T. Lichtenegger, J. Hachmann, A. Delgado, A. Skupin, High-speed visualization of acoustically excited cavitation bubbles in a cluster near a rigid boundary, J. Vis. 20 (2) (2017) 359-368.
[20] Z. Dong, D. Fernandez Rivas, S. Kuhn, Acoustophoretic focusing effects on particle synthesis and clogging in microreactors, Lab Chip 19 (2) (2019) 316-327.
[21] Z. Dong, A.P. Udepurkar, S. Kuhn, Synergistic effects of the alternating application of low and high frequency ultrasound for particle synthesis in microreactors, Ultrason. Sonochem. 60 (2020) 104800.
[22] V. Sebastián, N. Zaborenko, L. Gu, K.F. Jensen, Microfluidic assisted synthesis of hybrid Au-Pd dumbbell-like nanostructures: sequential addition of reagents and ultrasonic radiation, Cryst. Growth Des. 17 (5) (2017) 2700-2710.
[23] C.K. Ng, H. Deng, H.C. Li, W.P. Yin, T. Alan, J.J. Jasieniak, Synthesis of CsPbBr 3 perovskite nanocrystals with acoustically actuated millisecond mixing, J. Mater. Chem. C 9 (1) (2021) 313-321.
[24] Q. Zhang, Z.Y. Dong, S.N. Zhao, Z.K. Liu, G.W. Chen, Ultrasound-assisted gas-liquid mass transfer process in microreactors: The influence of surfactant, channel size and ultrasound frequency, Chem. Eng. J. 405 (2021) 126720.
[25] S.N. Zhao, C.Q. Yao, Z.Y. Dong, G.W. Chen, Q. Yuan, Role of ultrasonic oscillation in chemical processes in microreactors: A mesoscale issue, Particuology 48 (2020) 88-99.
[26] W.J. Lan, S.W. Li, Y.C. Lu, J.H. Xu, G.S. Luo, Controllable preparation of microscale tubes with multiphase co-laminar flow in a double co-axial microdevice, Lab Chip 9 (22) (2009) 3282-3288.
[27] J.M. Lim, A. Swami, L.M. Gilson, S. Chopra, S. Choi, J. Wu, R. Langer, R. Karnik, O.C. Farokhzad, Ultra-high throughput synthesis of nanoparticles with homogeneous size distribution using a coaxial turbulent jet mixer, ACS Nano 8 (6) (2014) 6056-6065.
[28] Z.Y. Dong, C.Q. Yao, Y.C. Zhang, G.W. Chen, Q. Yuan, J. Xu, Hydrodynamics and mass transfer of oscillating gas-liquid flow in ultrasonic microreactors, AIChE J. 62 (4) (2016) 1294-1307.
[29] Y.P. Wu, Y.K. Ren, Y. Tao, L.K. Hou, Q.M. Hu, H.Y. Jiang, A novel micromixer based on the alternating current-flow field effect transistor, Lab Chip 17 (1) (2016) 186-197.
[30] Z.Y. Dong, S.N. Zhao, Y.C. Zhang, C.Q. Yao, Q. Yuan, G.W. Chen, Mixing and residence time distribution in ultrasonic microreactors, AIChE J. 63 (4) (2017) 1404-1418.
[31] L. Polavarapu, B. Nickel, J. Feldmann, A.S. Urban, Advances in quantum-confined perovskite nanocrystals for optoelectronics, Adv. Energy Mater. 7 (16) (2017) 1700267.
[32] J.J. Cao, C. Yan, C. Luo, W. Li, X.K. Zeng, Z. Xu, X.H. Fu, Q. Wang, X. Chu, H.C. Huang, X.Y. Zhao, J. Lu, W.Q. Yang, Cryogenic-temperature thermodynamically suppressed and strongly confined CsPbBr 3 quantum dots for deeply blue light-emitting diodes, Adv. Opt. Mater. 9 (17) (2021) 2100300.
[33] S.H. Zou, Y.S. Liu, J.H. Li, C.P. Liu, R. Feng, F.L. Jiang, Y.X. Li, J.Z. Song, H.B. Zeng, M.C. Hong, X.Y. Chen, Stabilizing cesium lead halide perovskite lattice through Mn(II) substitution for air-stable light-emitting diodes, J. Am. Chem. Soc. 139 (33) (2017) 11443-11450.
[34] Y. Kim, E. Yassitepe, O. Voznyy, R. Comin, G. Walters, X.W. Gong, P. Kanjanaboos, A.F. Nogueira, E.H. Sargent, Efficient luminescence from perovskite quantum dot solids, ACS Appl. Mater. Interfaces 7 (45) (2015) 25007-25013.
[35] Y.F. Sun, H.D. Zhang, K. Zhu, W.G. Ye, L.S. She, X.M. Gao, W.Y. Ji, Q.H. Zeng, Research on the influence of polar solvents on CsPbBr₃ perovskite QDs, RSC Adv. 11 (44) (2021) 27333-27337.
[36] T. Udayabhaskararao, M. Kazes, L. Houben, H. Lin, D. Oron, Nucleation, growth, and structural transformations of perovskite nanocrystals, Chem. Mater. 29 (3) (2017) 1302-1308.
[37] X.Y. Zhang, X. Bai, H. Wu, X.T. Zhang, C. Sun, Y. Zhang, W. Zhang, W.T. Zheng, W.W. Yu, A.L. Rogach, Water-assisted size and shape control of CsPbBr₃ perovskite nanocrystals, Angew. Chem. Int. Ed. 57 (13) (2018) 3337-3342.
[38] L.Z. Guo, X.Z. Zhang, Y.H. Zhang, T. Yu, C.H. Cheng, Y. Cheng, X.P. Li, J.S. Zhang, S. Xu, Y.Z. Cao, B.J. Chen, Color-adjustable CsPbBr_3-xI_x quantum dots glasses for wide color gamut display, J. Non Cryst. Solids 551 (2021) 120432.