Abstract: In order to reduce the formaldehyde emission of formaldehyde-based wood adhesive from the source, it is aimed to develop a novel co-condensed resin of glyoxal-monomethylolurea-melamine (G-MMU-M). A series of G-MMU-M resins with various formulations of raw materials were successfully prepared. The basic properties and bonding performance of the G-MMU-M resins were determined. Furthermore, the structures of resins were characterized by FTIR, ¹³C NMR, XPS, and ESI-MS. The results show that the prepared G-MMU-M resin remains stable for 30 d, meanwhile, the dry and wet bonding strength of the plywoods bonded with the resins, solid content and viscosity are influenced greatly by the addition amount of melamine and MMU/G molar ratio. The G-MMU-M resins with MMU/G molar ratio of 0.9:1.0 and 8% melamine exhibit the highest dry and bonding strength of 1.98 MPa and 1.27 MPa, increased by 34% and 63%, respectively, in comparison with glyoxal-monomethylolurea (G-MMU) resin. In the G-MMU-M resins, there were four main oligomers including M—CH(—⁺CH-MMU)-O-MMU, M-CH(—CH₂OH)-MMU-O-MMU, M—CH(—OH)—⁺CH-MMU-O-MMU, and M—CH(—⁺CH-MMU)-MMU-p-G.

Key words: Wood adhesive, Glyoxal-monomethylolurea-melamine, Synthesis, Chemical reaction, Measurement, Structure

摘要： In order to reduce the formaldehyde emission of formaldehyde-based wood adhesive from the source, it is aimed to develop a novel co-condensed resin of glyoxal-monomethylolurea-melamine (G-MMU-M). A series of G-MMU-M resins with various formulations of raw materials were successfully prepared. The basic properties and bonding performance of the G-MMU-M resins were determined. Furthermore, the structures of resins were characterized by FTIR, ¹³C NMR, XPS, and ESI-MS. The results show that the prepared G-MMU-M resin remains stable for 30 d, meanwhile, the dry and wet bonding strength of the plywoods bonded with the resins, solid content and viscosity are influenced greatly by the addition amount of melamine and MMU/G molar ratio. The G-MMU-M resins with MMU/G molar ratio of 0.9:1.0 and 8% melamine exhibit the highest dry and bonding strength of 1.98 MPa and 1.27 MPa, increased by 34% and 63%, respectively, in comparison with glyoxal-monomethylolurea (G-MMU) resin. In the G-MMU-M resins, there were four main oligomers including M—CH(—⁺CH-MMU)-O-MMU, M-CH(—CH₂OH)-MMU-O-MMU, M—CH(—OH)—⁺CH-MMU-O-MMU, and M—CH(—⁺CH-MMU)-MMU-p-G.

关键词: Wood adhesive, Glyoxal-monomethylolurea-melamine, Synthesis, Chemical reaction, Measurement, Structure