Effect of Polyethylene Glycol on the Properties of γ-Al2O3 Formation by Polyaluminum Chloride

• •

Effect of Polyethylene Glycol on the Properties of γ-Al2O3 Formation by Polyaluminum Chloride

赵长伟¹,He Jingsong²,luan zhaokun²

1. 中科院生态环境研究中心水开放室
2.

收稿日期:2011-07-12 修回日期:2012-03-15 发布日期:2012-07-06
通讯作者: 赵长伟

聚乙二醇对聚合氯化铝制备γ-Al2O3的影响

Received:2011-07-12 Revised:2012-03-15 Published:2012-07-06
Contact: changwei zhao

摘要/Abstract

摘要： 本文中采用实验室自制的一种高Al13含量的聚合氯化铝作为原料，通过溶胶-凝胶法和油滴法相结合来制备球形γ-Al2O3。实验中研究了不同分子量的聚乙二醇作为表面活性剂对γ-Al2O3性质的影响。采用NMR、XRD、FT-IR和TG-DTA等分析手段对所制得的铝样品进行分析表征。结果表明，在实验所研究的范围内，样品的表面积，孔体积和孔径都随着聚乙二醇分子量的增加而增加，聚乙二醇10000是最好的表面活性剂，样品经450℃焙烧后所得的γ-Al2O3的表面积为339 m2∙g-1, 孔体积为 0.59 cm3•g-1，孔径为6.9nm。

关键词: γ-氧化铝, 聚合氯化铝, 制备, 聚乙二醇

Abstract: A polyaluminium chloride solution with high Al13 content self-prepared was used as material for preparing the spherical γ-Al2O3 by sol-gel method and oil-drop method. Polyethylene glycol with different molecular weight was used as surfactant to investigate the effect on property of γ-Al2O3. The physical property was characterized by 27Al NMR spectra, X-ray diffraction, FT-IR and TG-DTA. The results showed that surface area, pore volume and pore size of γ-Al2O3 all increased with the increase of polyethylene glycol molecular weight in the experimental research range, polyethylene glycol 10000 was the most suitable pore forming additive in experimental research range. γ-Al2O3 with surface area of 339 m2∙g-1, pore volume of 0.59 cm3•g-1 and pore diameter of 6.9nm were obtained at 450℃.

中图分类号:

赵长伟 He Jingsong luan zhaokun. Effect of Polyethylene Glycol on the Properties of γ-Al2O3 Formation by Polyaluminum Chloride [J]. .

[1]	甘礼华,王玉栋,郝志显,徐子颉,陈龙武. TiO₂/SiO₂气凝胶的非超临界干燥法制备及其对吡啶降解的光催化活性[J]. , 2005, 13(6): 758-763.
[2]	李加友,曹瑜,刘毅,钱绍松,焦庆才. L-瓜氨酸酶法制备中精氨酸脱亚氨酸酶的活性与稳定性研究[J]. , 2005, 13(6): 841-844.
[3]	黄福明,张国伟,胡春圃,应圣康. 硅溶胶/苯乙烯-丙烯酸酯共聚物无机-有机杂化水分散液的制备和表征[J]. , 2005, 13(6): 816-823.
[4]	冯庆革,林清宇,童张法,杉田修一. 具有高比表面积的稻壳灰的制备及其化学活性的研究[J]. , 2004, 12(5): 711-715.
[5]	李华, 范秀山, 王光龙, 刘大壮. 提高钾长石转化的实验室研究[J]. , 2001, 9(4): 447-450.
[6]	陆强, 胡鸣, 熊丹柳, 邓修. 乳状液膜包酶制备6-APA的研究[J]. , 2001, 9(4): 431-435.