Thermodynamic analysis on the direct preparation of metallic vanadium from NaVO3 by molten salt electrolysis

doi:10.1016/j.cjche.2016.01.006

Chinese Journal of Chemical Engineering ›› 2016, Vol. 24 ›› Issue (5): 671-676.DOI: 10.1016/j.cjche.2016.01.006

• 第25届中国过程控制会议专栏 • 上一篇

Thermodynamic analysis on the direct preparation of metallic vanadium from NaVO₃ by molten salt electrolysis

WeiWeng¹, Mingyong Wang², Xuzhong Gong², ZhiWang², Zhancheng Guo¹

1 State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China;
2 National Engineering Laboratory for Hydrometallurgical Cleaner Production Technology, Key Laboratory of Green Process and Engineering, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100190, China

收稿日期:2015-06-30 修回日期:2015-12-15 出版日期:2016-05-28 发布日期:2016-06-14
通讯作者: Mingyong Wang
基金资助:
Supported by the National Basic Research Program of China (2013CB632606), the National Natural Science Foundation of China (51474200) and the Youth Innovation Promotion Association, CAS (2015036).

Thermodynamic analysis on the direct preparation of metallic vanadium from NaVO₃ by molten salt electrolysis

WeiWeng¹, Mingyong Wang², Xuzhong Gong², ZhiWang², Zhancheng Guo¹

1 State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China;
2 National Engineering Laboratory for Hydrometallurgical Cleaner Production Technology, Key Laboratory of Green Process and Engineering, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100190, China

Received:2015-06-30 Revised:2015-12-15 Online:2016-05-28 Published:2016-06-14
Contact: Mingyong Wang
Supported by:
Supported by the National Basic Research Program of China (2013CB632606), the National Natural Science Foundation of China (51474200) and the Youth Innovation Promotion Association, CAS (2015036).

摘要/Abstract

摘要： A novel and environmentally friendly route to directly prepare metallic vanadium from NaVO₃ by molten salt electrolysis is proposed. The feasibility about the direct electro-reduction of NaVO₃ to metallic vanadium is analyzed based on the thermodynamic calculations and experimental verifications. The theoretical decomposition voltage of NaVO₃ to metallic vanadium is only 0.47 V at 800℃ and much lower than that of the alkali and alkali earth metal chloride salts. The value is slightly higher than that of low-valence vanadium oxides such as V₂O₃, V₃O₅ and VO. However, the low-valence vanadium oxides can be further electro-reduced to metallic vanadium thermodynamically. The thermodynamic analysis is verified by the experimental results. The direct preparation of metallic vanadium from NaVO₃ by molten salt electrolysis is feasible.

关键词: Molten salt electrolysis, NaVO₃, Thermodynamic analysis, Metallic vanadium, Decomposition voltage

Abstract: A novel and environmentally friendly route to directly prepare metallic vanadium from NaVO₃ by molten salt electrolysis is proposed. The feasibility about the direct electro-reduction of NaVO₃ to metallic vanadium is analyzed based on the thermodynamic calculations and experimental verifications. The theoretical decomposition voltage of NaVO₃ to metallic vanadium is only 0.47 V at 800℃ and much lower than that of the alkali and alkali earth metal chloride salts. The value is slightly higher than that of low-valence vanadium oxides such as V₂O₃, V₃O₅ and VO. However, the low-valence vanadium oxides can be further electro-reduced to metallic vanadium thermodynamically. The thermodynamic analysis is verified by the experimental results. The direct preparation of metallic vanadium from NaVO₃ by molten salt electrolysis is feasible.

Key words: Molten salt electrolysis, NaVO₃, Thermodynamic analysis, Metallic vanadium, Decomposition voltage

WeiWeng, Mingyong Wang, Xuzhong Gong, ZhiWang, Zhancheng Guo. Thermodynamic analysis on the direct preparation of metallic vanadium from NaVO₃ by molten salt electrolysis[J]. Chinese Journal of Chemical Engineering, 2016, 24(5): 671-676.

参考文献

[1] H. Matsui, K. Fukumoto, D.L. Smith, H.M. Chung, W.V. Witzenburg, S.N. Votinov, Status of vanadium alloys for fusion reactors, J. Nucl. Mater. 92(1996) 233-237.

[2] R.R. Moskalyk, A.M. Alfantazi, Processing of vanadium:A review, Miner. Eng. 16(2003) 793-805.

[3] D.L. Smith, B.A. Loomis, D.R. Diercks, Vanadium-base alloys for fusion reactor applications-A review, J. Nucl. Mater. 135(1985) 125-139.

[4] K. Tachikawa, Y. Yoshida, Studies on the formation of V₃Ga and V₃Si superconducting compounds by a new diffusion process, J. Mater. Sci. 7(1972) 1154-1160.

[5] C.K. Gupta, Proceedings of the International Symposium on Vanadium, Conference of Metallurgists, Montreal, Canada, 2002.

[6] Z.F. Cai, Z.M. Zhang, Z.C. Guo, H.Q. Tang, Direct electrochemical reduction of solid vanadium oxide to metal vanadium at low temperature in molten CaCl₂-NaCl, Int. J. Miner. Metall. Mater. 19(6) (2012) 499-505.

[7] V. Ivanchenko, T. Pryadko, Ternary alloy system, Springer, Germany, 2008.

[8] C.T.Wang, E.F. Baroch, S.A.Worcester, Y.S. Shen, Preparation and properties of highpurity vanadium and V-15Cr-5Ti, Metall. Mater. Trans. B Process Metall. Mater. Process. Sci. 1(1970) 1683-1689.

[9] H.A. Beale, R.J. Arsenault, The preparation and some mechanical properties of highpurity vanadium, Metall. Mater. Trans. B Process Metall. Mater. Process. Sci. 1(1970) 3355-3360.

[10] G.Q. Zhang, T.A. Zhang, G.Z. Lv, Y. Zhang, Y. Liu, Z.L. Liu, Extraction of vanadiumfrom vanadium slag by high pressure oxidative acid leaching, Int. J. Miner. Metall. Mater. 22(1) (2015) 21-26.

[11] M. Aarabi-Karasgani, F. Rashchi, N. Mostoufi, E. Vahidi, Leaching of vanadium from LD converter slag using sulfuric acid, Hydrometallurgy 102(2010) 14-21.

[12] M.R. Tavakoli, D.B. Dreisinger, The kinetics of oxidative leaching of vanadium trioxide, Hydrometallurgy 147-148(2014) 83-89.

[13] M. Feng, S.N. Wang, H. Du, S.L. Zheng, Y. Zhang, Solubility investigations in the NaOH-Na₃VO₄-Na₂CrO₄-Na₂CO₃-H₂O system at (40 and 80)℃, Fluid Phase Equilib. 409(2016) 119-123.

[14] N.Q. Minh, Extraction of metals by molten salt electrolysis:chemical fundamentals and design factors, JOM 37(1985) 28-33.

[15] V. Constantin, Influence of the operating parameters over the current efficiency and corrosion rate in the Hall-Heroult aluminum cell with tin oxide anode substrate material, Chin. J. Chem. Eng. 23(4) (2015) 722-726.

[16] S.L. Wang, W. Wang, S.C. Li, S.H. Cao, Cathodic behavior of molten CaCl₂-CaO and CaCl₂-NaCl-CaO, Int. J. Miner. Metall. Mater. 17(6) (2010) 791-794.

[17] D. Chery, V. Lair, M. Cassir, CO₂ electrochemical reduction into CO or C in molten carbonates:A thermodynamic point of view, Electrochim. Acta 160(2015) 74-81.

[18] X. Wang, C.F. Liao, Preparation and characterization of tungsten powder through molten salt electrolysis in a CaWO₄-CaCl₂-NaCl system, Int. J. Refract. Met. Hard Mater. 31(2012) 205-209.

[19] S.L.Wang, Y. Xue, H. Sun, Electrochemical study on the electrodeoxidation of Nb₂O₅ in equimolar CaCl₂ and NaCl melt, J. Electroanal. Chem. 595(2) (2006) 109-114.

[20] E.B. Freidina, D.J. Fray, Study of the ternary system CaCl₂-NaCl-CaO by DSC, Thermochim. Acta 354(2000) 59-62.

[21] R.O. Suzuki, K. Teranuma, K. Ona, Calciothermic reduction of titanium oxide and insitu electrolysis inmolten CaCl₂, Metall. Mater. Trans. B Process Metall. Mater. Process. Sci. 34(3) (2003) 287-295.

[22] R. Abdulaziz, L. Brown, D. Inman, S. Simons, P. Shearing, D. Brett, Novel fluidised cathode approach for the electrochemical reduction of tungsten oxide in molten LiCl-KCl eutectic, Electrochem. Commun. 41(2014) 44-46.

[23] R.O. Suzuki, Calciothermic reduction of TiO₂ and in situ electrolysis of CaO in the molten CaCl₂, J. Phys. Chem. Solids 66(2005) 461-465.

[24] H. Lin, B.W. Tao, Q. Li, Y.R. Li, In situ synthesis of V₈C₇ nanopowders from a new precursor, Int. J. Refract. Met. Hard Mater. 31(2012) 138-140.

[25] M. Mahaian, K. Singh, O.P. Pandey, Single step synthesis of nano vanadium carbide-V₈C₇ phase, Int. J. Refract. Met. Hard Mater. 36(2013) 106-110.

[26] A.A. Said, Thermal decomposition of ammonium metavanadate doped with Fe, Co, or Ni hydroxides, J. Therm. Anal. 37(1991) 849-860.

[27] A.M. Martinez, Y. Castrillejo, E. Barrado, G.M. Haarberg, G. Picard, A chemical and electrochemical study of titanium ions in the molten equimolar CaCl₂+NaCl mixture at 550℃, J. Electroanal. Chem. 449(1998) 67-80.

Thermodynamic analysis on the direct preparation of metallic vanadium from NaVO₃ by molten salt electrolysis

Thermodynamic analysis on the direct preparation of metallic vanadium from NaVO₃ by molten salt electrolysis

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 3

编辑推荐

Metrics

本文评价

[1]	Atif Abdalazeez, Wenju Wang, Siddig Abuelgasim. Syngas production from chemical looping reforming of ethanol over iron-based oxygen carriers: Theoretical analysis and experimental investigation[J]. 中国化学工程学报, 2021, 38(10): 123-131.
[2]	刘永卓, 郭庆杰. Investigation into Syngas Generation from Solid Fuel Using CaSO₄-based Chemical Looping Gasification Process[J]. Chinese Journal of Chemical Engineering, 2013, 21(2): 127-134.
[3]	高青, 卓宁, 马其良. ENHANCED HEAT TRANSFER OF GLASS TUBE HEAT EXCHANGER[J]. , 1993, 1(2): 105-113.