Engineering an ultrathin amorphous TiO2 layer for boosting the weatherability of TiO2 pigment with high lightening power

doi:10.1016/j.cjche.2019.04.002

中国化学工程学报 ›› 2019, Vol. 27 ›› Issue (11): 2825-2834.DOI: 10.1016/j.cjche.2019.04.002

• Materials and Product Engineering • 上一篇下一篇

Engineering an ultrathin amorphous TiO₂ layer for boosting the weatherability of TiO₂ pigment with high lightening power

Yangyang Yu¹, Kejing Wu², Shiyu Lu³, Kui Ma¹, Shan Zhong¹, Hegui Zhang¹, Yingming Zhu², Jing Guo⁴, Hairong Yue^1,2, Changjun Liu^1,2, Siyang Tang¹, Bin Liang^1,2

1 Low-Carbon Technology and Chemical Reaction Engineering Laboratory, School of Chemical Engineering, Sichuan University, Chengdu 610065, China;
2 Institute of New Energy and Low-Carbon Technology, Sichuan University, Chengdu 610207, China;
3 Institute for Clean Energy & Advanced Materials, Faculty of Materials and Energy, Southwest University, Chongqing 400715, China;
4 Shanxi Province Key Laboratory of Higee-Oriented Chemical Engineering, North University of China, Taiyuan 030051, China

收稿日期:2018-11-12 修回日期:2019-03-25 出版日期:2019-11-28 发布日期:2020-01-19
通讯作者: Bin Liang
基金资助:
Supported by the National Key R&D Program of China (2018YFB0605700).

Engineering an ultrathin amorphous TiO₂ layer for boosting the weatherability of TiO₂ pigment with high lightening power

Yangyang Yu¹, Kejing Wu², Shiyu Lu³, Kui Ma¹, Shan Zhong¹, Hegui Zhang¹, Yingming Zhu², Jing Guo⁴, Hairong Yue^1,2, Changjun Liu^1,2, Siyang Tang¹, Bin Liang^1,2

1 Low-Carbon Technology and Chemical Reaction Engineering Laboratory, School of Chemical Engineering, Sichuan University, Chengdu 610065, China;
2 Institute of New Energy and Low-Carbon Technology, Sichuan University, Chengdu 610207, China;
3 Institute for Clean Energy & Advanced Materials, Faculty of Materials and Energy, Southwest University, Chongqing 400715, China;
4 Shanxi Province Key Laboratory of Higee-Oriented Chemical Engineering, North University of China, Taiyuan 030051, China

Received:2018-11-12 Revised:2019-03-25 Online:2019-11-28 Published:2020-01-19
Contact: Bin Liang
Supported by:
Supported by the National Key R&D Program of China (2018YFB0605700).

摘要/Abstract

摘要： TiO₂ pigments are typically coated with inert layers to suppress the photocatalytic activity and improve the weatherability. However, the traditional inert layers have a lower refractive index compared to TiO₂, and therefore reduce the lightening power of TiO₂. In the present work, a uniform, amorphous, 2.9-nm-thick TiO₂ protective layer was deposited onto the surface of anatase TiO₂ pigments according to pulsed chemical vapor deposition at room temperature, with TiCl₄ as titanium precursor. Amorphous TiO₂ coating layers exhibited poor photocatalytic activity, leading to a boosted weatherability. Similarly, this coating method is also effective for TiO₂ coating with amorphous SiO₂ and SnO₂ layers. However, the lightening power of amorphous TiO₂ layer is higher than those of amorphous SiO₂ and SnO₂ layers. According to the measurements of photoluminescence lifetime, surface photocurrent density, charge-transfer resistance, and electron spin resonance spectroscopy, it is revealed that the amorphous layer can prevent the migration of photogenerated electrons and holes onto the surface, decreasing the densities of surface electron and hole, and thereby suppress the photocatalytic activity.

关键词: TiO₂ pigments, Pulsed chemical vapor deposition, Ultrathin layer, Weatherability, Lightening power, Photocatalytic suppression mechanism

Abstract: TiO₂ pigments are typically coated with inert layers to suppress the photocatalytic activity and improve the weatherability. However, the traditional inert layers have a lower refractive index compared to TiO₂, and therefore reduce the lightening power of TiO₂. In the present work, a uniform, amorphous, 2.9-nm-thick TiO₂ protective layer was deposited onto the surface of anatase TiO₂ pigments according to pulsed chemical vapor deposition at room temperature, with TiCl₄ as titanium precursor. Amorphous TiO₂ coating layers exhibited poor photocatalytic activity, leading to a boosted weatherability. Similarly, this coating method is also effective for TiO₂ coating with amorphous SiO₂ and SnO₂ layers. However, the lightening power of amorphous TiO₂ layer is higher than those of amorphous SiO₂ and SnO₂ layers. According to the measurements of photoluminescence lifetime, surface photocurrent density, charge-transfer resistance, and electron spin resonance spectroscopy, it is revealed that the amorphous layer can prevent the migration of photogenerated electrons and holes onto the surface, decreasing the densities of surface electron and hole, and thereby suppress the photocatalytic activity.

Key words: TiO₂ pigments, Pulsed chemical vapor deposition, Ultrathin layer, Weatherability, Lightening power, Photocatalytic suppression mechanism

Yangyang Yu, Kejing Wu, Shiyu Lu, Kui Ma, Shan Zhong, Hegui Zhang, Yingming Zhu, Jing Guo, Hairong Yue, Changjun Liu, Siyang Tang, Bin Liang. Engineering an ultrathin amorphous TiO₂ layer for boosting the weatherability of TiO₂ pigment with high lightening power[J]. 中国化学工程学报, 2019, 27(11): 2825-2834.

参考文献

[1] D. Wang, J.L. Chu, Y.H. Liu, L. Jie, T.Y. Xue, W.J. Wang, T. Qi, Novel process for titanium dioxide production from titanium slag:NaOH-KOH binary molten salt roasting and water leaching, Ind. Eng. Chem. Res. 52(2013) 15756-15762.
[2] L.S. Zhao, Y.H. Liu, L. Wang, H.X. Zhao, D.S. Chen, B.N. Zhong, J.C. Wang, T. Qi, Production of rutile TiO₂ pigment from titanium slag obtained by hydrochloric acid leaching of vanadium-bearing titanomagnetite, Ind. Eng. Chem. Res. 53(2014) 70-77.
[3] Y. Wang, J. Li, L. Wang, T.Y. Xue, T. Qi, Preparation of rutile titanium dioxide white pigment via doping and calcination of metatitanic acid obtained by the NaOH molten salt method, Ind. Eng. Chem. Res. 49(2010) 7693-7696.
[4] Y.L. Lin, T.J. Wang, J. Yong, Surface characteristics of hydrous silica-coated TiO₂ particles, Powder Technol. 123(2002) 194-198.
[5] H.X. Wu, T.J. Wang, Y. Jin, Film-coating process of hydrated alumina on TiO₂ particles, Ind. Eng. Chem. Res. 45(2006) 1337-1342.
[6] H.X. Wu, T.J. Wang, Y. Jin, Morphology "phase diagram" of the hydrous alumina coating on TiO₂ particles during aqueous precipitation, Ind. Eng. Chem. Res. 45(2006) 5274-5278.
[7] Y.M. Liu, C. Ge, M. Ren, H.B. Yin, A.L. Wang, D.Z. Zhang, C.Z. Liu, J. Chen, H. Feng, H. Yao, T.S. Jiang, Effects of coating parameters on the morphology of SiO₂-coated TiO₂ and the pigmentary properties, Appl. Surf. Sci. 254(2008) 2809-2819.
[8] Y.S. Zhang, H.B. Yin, A.L. Wang, C. Liu, L.B. Yu, T.S. Jiang, Y. Hang, Evolution of zirconia coating layer on rutile TiO₂ surface and the pigmentary property, J. Phys. Chem. Solids 71(2010) 1458-1466.
[9] J. Li, T.C. Sun, Y. Wang, L.N. Wang, J.K. Qu, T. Qi, Preparation and film-growing mechanism of hydrous zirconia coated on TiO₂, Int. J. Miner. Metall. Mater. 17(2010) 660-667.
[10] B.X. Wei, L. Zhao, T.J. Wang, H. Gao, H.X. Wu, Y. Jin, Photo-stability of TiO₂ particles coated with several transition metal oxides and its measurement by rhodamine-B degradation, Adv. Powder Technol. 24(2013) 708-713.
[11] H. Gao, B. Qiao, T.J. Wang, D.Z. Wang, Y. Jin, Cerium oxide coating of titanium dioxide pigment to decrease its photocatalytic activity, Ind. Eng. Chem. Res. 53(2014) 189-197.
[12] X.H. Liang, A.W. Weimer, Photoactivity passivation of TiO₂ nanoparticles using molecular layer deposited (MLD) polymer films, J. Nanopart. Res. 12(2010) 135-142.
[13] B.X. Wei, L. Zhao, T.J. Wang, Y. Jin, Detrimental thixotropic thinning of filter cake of SiO₂-Al₂O₃ composite coated TiO₂ particles and its control, Ind. Eng. Chem. Res. 50(2011) 13799-13804.
[14] Y.S. Zhang, H.B. Yin, A.L. Wang, M. Ren, Z.M. Gu, Y.M. Liu, Y.T. Shen, L.B. Yu, T.S. Jiang, Deposition and characterization of binary Al₂O₃/SiO₂ coating layers on the surfaces of rutile TiO₂ and the pigmentary properties, Appl. Surf. Sci. 257(2010) 1351-1360.
[15] E. Jang, K. Sridharan, Y.M. Park, T.J. Park, Eliminated phototoxicity of TiO₂ particles by an atomic-layer-deposited Al₂O₃ coating layer for UV-protection applications, Chemistry 22(2016) 12022-12026.
[16] J. Guo, S.J. Yuan, Y.Y. Yu, J.R. van Ommen, H. Van Bui, B. Liang, Room-temperature pulsed CVD-grown SiO₂ protective layer on TiO₂ particles for photocatalytic activity suppression, RSC Adv. 7(2017) 4547-4554.
[17] Q.H. Powell, T.T. Kodas, B.M. Anderson, Coating of TiO₂ particles by chemical vapor deposition of SiO₂, Chem. Vap. Depos. 2(51) (1996) 179-181.
[18] D.J. Simpson, A. Thilagam, G.P. Cavallaro, K. Kaplun, A.R. Gerson, SiO₂ coated pure and doped titania pigments:Low temperature CVD deposition and quantum chemical study, Phys. Chem. Chem. Phys. 13(47) (2011) 21132-21138.
[19] H. Azizpour, M. Talebi, F.D. Tichelaar, R. Sotudeh-Gharebagh, J. Guo, J.R. van Ommen, N. Mostoufi, Effective coating of titania nanoparticles with alumina via atomic layer deposition, Appl. Surf. Sci. 426(2017) 480-496.
[20] D. Valdesueiro, M. Gmh, M.T. Kreutzer, J.R. van Ommen, Gas-phase deposition of ultrathin aluminium oxide films on nanoparticles at ambient conditions, Materials 8(2015) 1249-1263.
[21] J. Guo, B. Hao Van, D. Valdesueiro, S.J. Yuan, B. Liang, J.R. van Ommen, Suppressing the photocatalytic activity of TiO₂ nanoparticles by extremely thin Al₂O₃ films grown by gas-phase deposition at ambient conditions, Nanomaterials 8(2018) 61(19).
[22] B. Vidjayacoumar, D.J.H. Emslie, S.B. Clendenning, J.M. Blackwell, J.F. Britten, A. Rheingold, Investigation of AlMe₃, BEt₃, and ZnEt₂ as co-reagents for lowtemperature copper metal ALD/pulsed-CVD, Chem. Mater. 22(2010) 4844-4853.
[23] Y.Y. Yu, Y.M. Zhu, J. Guo, H.R. Yue, H.G. Zhang, C.J. Liu, S.Y. Tang, B. Liang, Suppression of TiO₂ photocatalytic activity by low-temperature pulsed CVD-grown SnO₂ protective layer, Ind. Eng. Chem. Res. 57(2018) 8679-8688.
[24] J. Aarik, A. Aidla, A.A. Kiisler, T. Uustare, V. Sammelselg, Effect of crystal structure on optical properties of TiO₂ films grown by atomic layer deposition, Thin Solid Films 305(1997) 270-273.
[25] G.D. Parfitt, K.S.W. Sing, Characterization of powder surfaces, Academic Press, New York, 1976.
[26] E. Palomares, J.N. Clifford, S.A. Haque, A. Thierry Lutz, J.R. Durrant, Control of charge recombination dynamics in dye sensitized solar cells by the use of conformally deposited metal oxide blocking layers, J. Am. Chem. Soc. 125(2003) 475-482.
[27] C. Armistead, A. Tyler, F. Hambleton, S. Mitchell, J.A. Hockey, Surface hydroxylation of silica, J. Phys. Chem. 73(1969) 3947-3953.
[28] D. Longrie, D. Deduytsche, C. Detavernier, Reactor concepts for atomic layer deposition on agitated particles:A review, J. Vac. Sci. Technol. A 32(2014), 010802.
[29] S.G. Zhang, L. Li, Y.Z. Liu, Q.L. Zhang, TiO₂-SA-Arg nanoparticles stabilized pickering emulsion for photocatalytic degradation of nitrobenzene in a rotating annular reactor, Chin. J. Chem. Eng. 25(2017) 223-231.
[30] F.M. Wang, Z.S. Shi, F. Gong, J.T. Jiu, A. Motonari, Morphology control of anatase TiO₂ by surfactant-assisted hydrothermal method, Chin. J. Chem. Eng. 15(2007) 754-759.
[31] J.H. Shen, Y.H. Zhu, X.L. Yang, C.Z. Li, Magnetic composite microspheres with exposed {001} faceted TiO₂ shells:A highly active and selective visible-light photocatalyst, J. Mater. Chem. 22(26) (2012) 13341-13347.
[32] G.X. Song, Z.Y. Chu, W.Q. Jin, H.Q. Sun, Enhanced performance of g-C₃N₄/TiO₂ photocatalysts for degradation of organic pollutants under visible light, Chin. J. Chem. Eng. 23(2015) 1326-1334.
[33] J.B. Metson, Charge compensation and binding energy referencing in XPS analysis, Surf. Interface Anal. 27(1999) 1069-1072.
[34] Q.H. Tian, Z.X. Zhang, L. Yang, S.I. Hirano, Encapsulation of SnO₂ nanoparticles into hollow TiO₂ nanowires as high performance anode materials for lithium ion batteries, J. Power Sources 253(2014) 9-16.
[35] X.Y. Hou, Y.J. Hu, H. Jiang, Y.F. Li, W.G. Li, C.Z. Li, One-step synthesis of SnOx nanocrystalline aggregates encapsulated by amorphous TiO₂ as an anode in Li-ion battery, J. Mater. Chem. A 3(18) (2015) 9982-9988.
[36] A.S. Tselesh, Anodic behaviour of tin in citrate solutions:The IR and XPS study on the composition of the passive layer, Thin Solid Films 516(2008) 6253-6260.
[37] M. Ren, H.B. Yin, Z.Z. Lu, A.L. Wang, L.B. Yu, T.S. Jiang, Evolution of rutile TiO₂ coating layers on lamellar sericite surface induced by Sn⁴⁺ and the pigmentary properties, Powder Technol. 204(2010) 249-254.
[38] L.J. Luo, Y. Yang, M. Xiao, L.C. Bian, B. Yuan, Y.J. Liu, F.Z. Jiang, X.J. Pan, A novel biotemplated synthesis of TiO₂/wood charcoal composites for synergistic removal of bisphenol A by adsorption and photocatalytic degradation, Chem. Eng. J. 262(2015) 1275-1283.
[39] Y. Duval, J.A. Mielczarski, O.S. Pokrovsky, E. Mielczarski, J.J. Ehrhardt, Evidence of the existence of three types of species at the quartz-aqueous solution interface at pH 0-10:XPS surface group quantification and surface complexation modeling, J. Phys. Chem. B 106(2002) 2937-2945.
[40] X.L. Wang, S.O. Pehkonen, J. Rämö, M. Väänänen, J.G. Highfield, K. Laasonen, Experimental and computational studies of nitrogen doped Degussa P25 TiO₂:Application to visible-light driven photo-oxidation of as As (III), Catal. Sci. Technol. 2(2012) 784-793.
[41] Z.W. Zhao, W.D. Zhang, X.S. Lv, Y.J. Sun, F. Dong, Y.X. Zhang, Noble metal-free Bi nanoparticles supported on TiO₂ with plasmon-enhanced visible light photocatalytic air purification, Environ. Sci.:Nano 3(2016) 1306-1317.
[42] R.D. Chekuri, S.R. Tirukkovalluri, One step synthesis and characterization of copper doped sulfated titania and its enhanced photocatalytic activity in visible light by degradation of methyl orange, Chin. J. Chem. Eng. 24(4) (2016) 475-483.
[43] H.B. Jiang, Q. Cuan, C.Z. Wen, J. Xing, D. Wu, X.Q. Gong, C.Z. Li, H.G. Yang, Anatase TiO₂ crystals with exposed high-index facets, Angew. Chem. Int. Ed. 50(16) (2011) 3764-3768.
[44] J.B. Mu, B. Chen, Z.C. Guo, M.Y. Zhang, Z.Y. Zhang, C.L. Shao, Y.C. Liu, Tin oxide (SnO₂) nanoparticles/electrospun carbon nanofibers (CNFs) heterostructures:Controlled fabrication and high capacitive behavior, J. Colloid Interface Sci. 356(2011) 706-712.
[45] A. Groza, A. Surmeian, C. Diplasu, C. Negrila, B. Mihalcea, M. Ganciu, Infrared and Xray photoelectron spectroscopy in surface characterization of polydimethylsiloxane thin films generated on metallic substrates in multipoints to plane corona discharges, Rom. J. Phys. 61(2016) 648-656.
[46] L. Zhang, Y.R. Hong, T.S. Zhang, C.Z. Li, A novel approach to prepare PBT nanocomposites with elastomer-modified SiO₂ particles, Polym. Compos. 30(5) (2009) 673-679.
[47] S.R. Wang, F. Teng, Y.X. Zhao, Effect of the molecular structure and surface charge of a bismuth catalyst on the adsorption and photocatalytic degradation of dye mixtures, RSC Adv. 5(2015) 76588-76598.
[48] A. Farhadi, M.R. Mohammadi, M. Ghorbani, On the assessment of photocatalytic activity and charge carrier mechanism of TiO₂@SnO₂ core-shell nanoparticles for water decontamination, J. Photochem. Photobiol. A 338(2017) 171-177.
[49] A.L. Linsebigler, G. Lu, J.T. Yates Jr., Photocatalysis on TiO₂ surfaces:Principles, mechanisms, and selected results, Chem. Rev. 95(1995) 735-758.
[50] R.J. Dillon, J.B. Joo, F. Zaera, Y.D. Yin, C.J. Bardeen, Correlating the excited state relaxation dynamics as measured by photoluminescence and transient absorption with the photocatalytic activity of Au@TiO₂ core-shell nanostructures, Phys. Chem. Chem. Phys. 15(2013) 1488-1496.
[51] F. Kan, S. Izumi, T. Ohno, M. Matsumura, Time-resolved photoluminescence of particulate TiO₂ photocatalysts suspended in aqueous solutions, J. Photochem. Photobiol. A 132(2000) 99-104.
[52] D. Stockwell, Y. Yang, J. Huang, C. Anfuso, Z. Huang, T. Lian, Comparison of electrontransfer dynamics from coumarin 343 to TiO₂, SnO₂, and ZnO nanocrystalline thin films:Role of interface-bound charge-separated pairs, J. Phys. Chem. C 114(2010) 6560-6566.
[53] M.H. Zhou, J.G. Yu, S.W. Liu, P.C. Zhai, L. Jiang, Effects of calcination temperatures on photocatalytic activity of SnO₂/TiO₂ composite films prepared by an EPD method, J. Hazard. Mater. 154(2008) 1141-1148.
[54] C.L. Xiang, C.A. Okonkwo, Q. Xiong, L.Q. Wang, L.S. Jia, A novel TiO₂ film photoanode decorated with spirulina-derived residual groups for enhanced photocurrent in dyesensitized solar cells, Sol. Energy 134(2016) 461-467.
[55] T. Hong, Y.H. Sun, W.P. Jepson, Study on corrosion inhibitor in large pipelines under multiphase flow using EIS, Corros. Sci. 44(2002) 101-112.
[56] S.Y. Lu, M. Jin, Y. Zhang, Y.B. Niu, J.C. Gao, C.M. Li, Chemically exfoliating biomass into a graphene-like porous active carbon with rational pore structure, good conductivity, and large surface area for high-performance supercapacitors, Adv. Energy Mater. 8(2018), 1702545.
[57] W.W. He, H.K. Kim, W.G. Warner, D. Melka, J.H. Callahan, J.J. Yin, Photogenerated charge carriers and reactive oxygen species in ZnO/Au hybrid nanostructures with enhanced photocatalytic and antibacterial activity, J. Am. Chem. Soc. 136(2014) 750-757.
[58] M.J. Chen, Y. Li, Z.Y. Wang, Y.X. Gao, Y. Huang, J.J. Cao, W. Ho, S. Lee, Controllable synthesis of core-shell Bi@amorphous Bi₂O₃ nanospheres with tunable optical and photocatalytic activity for NO removal, Ind. Eng. Chem. Res. 56(2017) 10251-10258.
[59] X.Y. Pan, N. Zhang, X.Z. Fu, Y.J. Xu, Selective oxidation of benzyl alcohol over TiO₂ nanosheets with exposed {001} facets:Catalyst deactivation and regeneration, Appl. Catal. A Gen. 453(2013) 181-187.
[60] H.C. Ma, M. Zhao, H.M. Xing, Y.H. Fu, X.F. Zhang, X.L. Dong, Synthesis and enhanced photoreactivity of metallic Bi-decorated BiOBr composites with abundant oxygen vacancies, J. Mater. Sci. Mater. Electron. 26(2015) 10002-10011.

Engineering an ultrathin amorphous TiO₂ layer for boosting the weatherability of TiO₂ pigment with high lightening power

Engineering an ultrathin amorphous TiO₂ layer for boosting the weatherability of TiO₂ pigment with high lightening power

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 0

编辑推荐

Metrics

本文评价