Thermodynamic data calculation for iron phases in sulfoaluminate cementitious materials prepared using solid wastes

doi:10.1016/j.cjche.2019.01.010

中国化学工程学报 ›› 2019, Vol. 27 ›› Issue (12): 2989-2993.DOI: 10.1016/j.cjche.2019.01.010

• Chemical Engineering Thermodynamics • 上一篇下一篇

Thermodynamic data calculation for iron phases in sulfoaluminate cementitious materials prepared using solid wastes

Wenlong Wang, Guolin Li, Lizhi Zhou, Changzai Ren

National Engineering Laboratory of Coal-fired Pollutants Emission Reduction, Shandong Provincial Key Lab of Energy Carbon Reduction and Resource Utilization, Shandong University, Jinan 250061, China

收稿日期:2018-09-05 修回日期:2018-11-13 出版日期:2019-12-28 发布日期:2020-03-17
通讯作者: Wenlong Wang
基金资助:
Supported by the Program for National Key R&D Plan (2017YFC0703100).

Thermodynamic data calculation for iron phases in sulfoaluminate cementitious materials prepared using solid wastes

Wenlong Wang, Guolin Li, Lizhi Zhou, Changzai Ren

National Engineering Laboratory of Coal-fired Pollutants Emission Reduction, Shandong Provincial Key Lab of Energy Carbon Reduction and Resource Utilization, Shandong University, Jinan 250061, China

Received:2018-09-05 Revised:2018-11-13 Online:2019-12-28 Published:2020-03-17
Contact: Wenlong Wang
Supported by:
Supported by the Program for National Key R&D Plan (2017YFC0703100).

摘要/Abstract

摘要： The preparation of sulfoaluminate cementitious materials (SCM) is a promising way to massively utilize solid wastes. Iron phases are significant in SCM system but the thermodynamic data of some key minerals, such as 6CaO·Al₂O₃·2Fe₂O₃ (C₆AF₂) and 6CaO·2Al₂O₃·Fe₂O₃ (C₆A₂F), are missing, which greatly hinders the SCM optimization in a theoretical way. This work, for the first time, calculated the standard formation enthalpy, Gibbs free energy of formation, entropy and molar heat capacity for C₆AF₂ and C₆A₂F and lowered the errors to the least with the reference of C₄AF data in the literature. By building the function diagram of Gibbs free energy changes with temperature for the basic iron phase formation reactions with the obtained thermodynamic data, it is proved that the formation likeliness of C₆AF₂ is higher than that of C₆A₂F, as is accordant to the literatures and verifies the correctness of obtained data. This work provides a good theoretical foundation to optimize SCM mineral system and to study relevant mechanism deeply.

关键词: Sulfoaluminate cement, Iron phase, Thermodynamic data, Gibbs free energy, Solid waste utilization

Abstract: The preparation of sulfoaluminate cementitious materials (SCM) is a promising way to massively utilize solid wastes. Iron phases are significant in SCM system but the thermodynamic data of some key minerals, such as 6CaO·Al₂O₃·2Fe₂O₃ (C₆AF₂) and 6CaO·2Al₂O₃·Fe₂O₃ (C₆A₂F), are missing, which greatly hinders the SCM optimization in a theoretical way. This work, for the first time, calculated the standard formation enthalpy, Gibbs free energy of formation, entropy and molar heat capacity for C₆AF₂ and C₆A₂F and lowered the errors to the least with the reference of C₄AF data in the literature. By building the function diagram of Gibbs free energy changes with temperature for the basic iron phase formation reactions with the obtained thermodynamic data, it is proved that the formation likeliness of C₆AF₂ is higher than that of C₆A₂F, as is accordant to the literatures and verifies the correctness of obtained data. This work provides a good theoretical foundation to optimize SCM mineral system and to study relevant mechanism deeply.

Key words: Sulfoaluminate cement, Iron phase, Thermodynamic data, Gibbs free energy, Solid waste utilization

Wenlong Wang, Guolin Li, Lizhi Zhou, Changzai Ren. Thermodynamic data calculation for iron phases in sulfoaluminate cementitious materials prepared using solid wastes[J]. 中国化学工程学报, 2019, 27(12): 2989-2993.

Wenlong Wang, Guolin Li, Lizhi Zhou, Changzai Ren. Thermodynamic data calculation for iron phases in sulfoaluminate cementitious materials prepared using solid wastes[J]. Chinese Journal of Chemical Engineering, 2019, 27(12): 2989-2993.

参考文献

[1] F.L. Kapustin, A.A. Ponomarenko, V.N. Oleinik, Sulfoaluminate cements composition and properties, Solid State Phenom. 265(2017) 734-737.
[2] Y.J. Liu, Y.M. Xu, C.L. Geng, Sulfoaluminate cement:An alternative to Portland cement, Adv. Mater. Res. 368-373(2011) 478-484.
[3] B. Liu, M. Suhua, X. Shen, J. Bin, B. Zhong, Progress in research on Portland cement clinker containing calcium sulphoaluminate, Mater. Rev. 58(7) (2008) 3952-3953.
[4] W. Wang, Z. Luo, Z. Shi, K. Cen, Experimental study on cement clinker co-generation in pulverized coal combustion boilers of power plants, Waste Manag. Res. 24(3) (2006) 207-214.
[5] P. Arjunan, M.R. Silsbee, D.M. Roy, Sulfoaluminate-belite cement from low-calcium fly ash and sulfur-rich and other industrial by-products, Cem. Concr. Res. 29(8) (1999) 1305-1311.
[6] C.A. Luz, J. Pera, M. Cheriaf, J.C. Rocha, Behaviour of calcium sulfoaluminate cement in presence of high concentrations of chromium salts, Cem. Concr. Res. 37(4) (2007) 624-629.
[7] Q. Zhou, N.B. Mileston, M. Hayes, An alternative to Portland cement for waste encapsulation-The calcium sulfoaluminate cement system, J. Hazard. Mater. 136(1) (2006) 120-129.
[8] W. Yao, Q. Ling, M.X. Wu, Preparation and composition optimization of low-CO₂-emission cement containing belite, calcium sulfoaluminate and ferrite, Key Eng. Mater. 727(2017) 1067-1073.
[9] J.H. Zhou, J. Shi, T.H. Yang, J.Z. Liu, K.F. Cen, Study of sulfur-fixing characteristics of sulphoaluminate in different atmosphere at high temperature, J. Zheijang Univ. 39(2) (2005) 283-286.
[10] M. Carsana, F. Canonico, L. Bertolini, Corrosion resistance of steel embedded in sulfoaluminate-based binders, Cem. Concr. Compos. 88(2018) 211-219, https://doi.org/10.1016/j.cemconcomp.2018.01.014.
[11] H. Liu, J.R. Qiu, Q.J. Xiong, F.H. Kong, X.P. Zhang, Q.H. Wang, X.Y. Xiao, Transportation and heterogeneous reactions of calcium containing minerals in coal combustion solid residues, Proc. CSEE 25(11) (2005) 72-78.
[12] T.H. Yang, J.H. Zhou, J. Cheng, M. Yi, X.Y. Cao, K.F. Cen, Progress in high temperature phase of sulphoaluminate for desulfuration, J. Combust. Sci. Technol. 9(1) (2003) 35-39.
[13] W. Wang, X. Chen, Y. Chen, Y. Dong, C.Y. Ma, Calculation and verification for the thermodynamic data of 3CaO·3Al₂O₃·CaSO₄, Chin. J. Chem. Eng. 19(3) (2011) 489-495.
[14] Z.S. Ding, M.Q. Wang, S.L. Pan, Silicate Physical Chemistry, China Architecture & Building Press, Beijing, 1980.
[15] H.F.W. Taylor, Cement Chemistry, Academic Press, London, 1998.
[16] Y. Wen, J. Shao, S. Wang, A simplified formula to calculate heat of formation of oxyacid salt and mineral, Acta Metall. Sin. 69(1) (1979) 98-108.
[17] Y. Wen, J. Shao, D. Chen, Calculation of standard free energies of formation of oxyacid salt minerals, Chin. J. Geol. 1(6) (1978) 497-503.
[18] X.B. Li, Y.F. Li, X.M. Liu, G.H. Liu, Z.H. Peng, Y.C. Zhai, A simple method of estimation of Gibbs free energy and enthalpy of complicate silicates, J. Chin. Ceram. Soc. 29(3) (2001) 232-237.
[19] O. Kubaschewski, H. Uenal, Empirical estimation of the heat capacities of inorganic compounds, High Temp.-High Pressures 9(3) (1977) 361-365.
[20] P.J. Spencer, Estimation of thermodynamic data for metallurgical applications, Thermochim. Acta 314(1-2) (1998) 1-21.
[21] W.M. Latimer, Methods of estimating the entropies of solid compounds, J. Am. Chem. Soc. 73(4) (1951) 1480-1482.
[22] K.C. Mills, Thermodynamic Data for Inorganic Sulfides, Selenides, and Tellurides, Butterworths, London, UK, 1974.
[23] D. Ambrose, ChemInform abstract:Publications in the field of chemical thermodynamics by the division of chemical standards at N.P.L, J. Chem. Thermodyn. 14(1) (1982) 61-76.
[24] J. Richter, W. Vreuls, Estimation of the molar entropy of solid and molten-salts based on the linear dependence between entropy and radius of the cation, Ber. Bunsenges. Phys. Chem. 83(1979) 1023-1026.
[25] Y.M. Chen, Kinetics of ettringite formation from calcium aluminoferrite hydration, J. Chin. Ceram. Soc. 28(4) (2000) 303-308.
[26] P.W. Brown, Early hydration of tetracalcium aluminoferrite in gypsum and lime-gypsum solutions, J. Am. Ceram. Soc. 70(7) (1987) 493-496.
[27] Y.M. Wang, M.Z. Su, L. Zhang, Sulfoaluminate Cement, Beijing University of Technology Press, Beijing, 1999(in Chinese).
[28] Y.C. Yuan, Z.M. Ye, J. Chang, Influence of iron phase composition on barium calcium sulphoaluminate cement, J. Univ. Jinan 26(2) (2012) 128-131.
[29] L. Tong, N. Yang, Hydration products of calcium aluminoferrite in the presence of gypsum, Cem. Concr. Res. 24(1) (1994) 150-158.

Thermodynamic data calculation for iron phases in sulfoaluminate cementitious materials prepared using solid wastes

Thermodynamic data calculation for iron phases in sulfoaluminate cementitious materials prepared using solid wastes

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 3

编辑推荐

Metrics

本文评价

[1]	王文龙, 陈晓冬, 陈莹, 董勇, 马春元. Calculation and Verification for the Thermodynamic Data of 3CaO·3Al₂O₃·CaSO₄[J]. , 2011, 19(3): 489-495.
[2]	杨春生, 仲崇立. 预测纯流体表面张力的一个新模型[J]. , 2004, 12(1): 85-91.
[3]	李春喜, 汪文川. 一个基于NRTL方程的液体混合物表面张力模型[J]. , 2001, 9(1): 45-50.