The crystal transformation characteristics from dihydrate gypsum to α-hemihydrate gypsum in Mg(NO3)2 solution

doi:10.1016/j.cjche.2025.07.009

中国化学工程学报 ›› 2025, Vol. 88 ›› Issue (12): 274-283.DOI: 10.1016/j.cjche.2025.07.009

The crystal transformation characteristics from dihydrate gypsum to α-hemihydrate gypsum in Mg(NO₃)₂ solution

Yunfei Li, Xinyue Deng, Shiqin Yin, Li Lv, Shengwei Tang, Tao Zhang

School of Chemical Engineering, Sichuan University, Chengdu 610000, China

收稿日期:2025-05-20 修回日期:2025-07-24 接受日期:2025-07-25 出版日期:2026-02-09 发布日期:2025-08-12
通讯作者: Tao Zhang,E-mail:zhangtao@scu.edu.cn
基金资助:
This work was financial supported by the Opening Project of Hubei Yihua-Sichuan University Joint Innovation Research Center for new chemical materials (24H1402); Fundamental Research Funds for the Central Universities (SCU2024D009); the National Key Research and Development Program of China (2019YFC1905800).

The crystal transformation characteristics from dihydrate gypsum to α-hemihydrate gypsum in Mg(NO₃)₂ solution

Yunfei Li, Xinyue Deng, Shiqin Yin, Li Lv, Shengwei Tang, Tao Zhang

School of Chemical Engineering, Sichuan University, Chengdu 610000, China

Received:2025-05-20 Revised:2025-07-24 Accepted:2025-07-25 Online:2026-02-09 Published:2025-08-12
Contact: Tao Zhang,E-mail:zhangtao@scu.edu.cn
Supported by:
This work was financial supported by the Opening Project of Hubei Yihua-Sichuan University Joint Innovation Research Center for new chemical materials (24H1402); Fundamental Research Funds for the Central Universities (SCU2024D009); the National Key Research and Development Program of China (2019YFC1905800).

摘要/Abstract

摘要： The preparation of high-strength α-hemihydrate gypsum (α-HH) from dihydrate gypsum (DH) is a potential way to improve the utilization rate of industrial gypsum. α-HH with a low aspect ratio was prepared by atmospheric salt solution method, using Mg(NO₃)₂ solution as the salt medium. The effects of reaction temperature, reaction time, Mg(NO₃)₂ concentration, pH value, and the solid-to-liquid ratio on the purity, yield and aspect ratio of the product were investigated systematically. Under the optimal reaction conditions of 95 ℃, 4 h, 40% (mass) Mg(NO₃)₂, pH 5, and a solid-liquid ratio of 1:5, the yield and purity of the product could reach 89.67% and 99.85%, respectively. Additionally, the average aspect ratio of this product was 2.02, and the compressive strength reached 58.2 MPa. The regulation mechanism was studied by calculating the adsorption energies of Mg(NO₃)₂ on different crystal planes of α-HH, which indicated that Mg(NO₃)₂ exhibited the strongest adsorption on the (1 1 1) plane, and this preferential adsorption retarded the axial growth of α-HH, resulting in a reduced aspect ratio of the crystals. These findings suggest that the Mg(NO₃)₂ solution is an effective approach for preparing high-strength α-HH with controlled morphology.

关键词: α-Hemihydrate gypsum, Mg(NO₃)₂, Crystal morphology, Crystal regulation mechanism

Abstract: The preparation of high-strength α-hemihydrate gypsum (α-HH) from dihydrate gypsum (DH) is a potential way to improve the utilization rate of industrial gypsum. α-HH with a low aspect ratio was prepared by atmospheric salt solution method, using Mg(NO₃)₂ solution as the salt medium. The effects of reaction temperature, reaction time, Mg(NO₃)₂ concentration, pH value, and the solid-to-liquid ratio on the purity, yield and aspect ratio of the product were investigated systematically. Under the optimal reaction conditions of 95 ℃, 4 h, 40% (mass) Mg(NO₃)₂, pH 5, and a solid-liquid ratio of 1:5, the yield and purity of the product could reach 89.67% and 99.85%, respectively. Additionally, the average aspect ratio of this product was 2.02, and the compressive strength reached 58.2 MPa. The regulation mechanism was studied by calculating the adsorption energies of Mg(NO₃)₂ on different crystal planes of α-HH, which indicated that Mg(NO₃)₂ exhibited the strongest adsorption on the (1 1 1) plane, and this preferential adsorption retarded the axial growth of α-HH, resulting in a reduced aspect ratio of the crystals. These findings suggest that the Mg(NO₃)₂ solution is an effective approach for preparing high-strength α-HH with controlled morphology.

Key words: α-Hemihydrate gypsum, Mg(NO₃)₂, Crystal morphology, Crystal regulation mechanism

Yunfei Li, Xinyue Deng, Shiqin Yin, Li Lv, Shengwei Tang, Tao Zhang. The crystal transformation characteristics from dihydrate gypsum to α-hemihydrate gypsum in Mg(NO₃)₂ solution[J]. 中国化学工程学报, 2025, 88(12): 274-283.

参考文献

[1] K.N. Fang, L. Xu, M. Yang, Q.L. Chen, One-step wet-process phosphoric acid by-product CaSO₄ and its purification, Sep. Purif. Technol. 309 (2023) 123048.
[2] Q.J. Guan, H.H. Tang, W. Sun, Y.H. Hu, Z.G. Yin, Insight into influence of glycerol on preparing α-CaSO₄·1/2H₂O from flue gas desulfurization gypsum in glycerol-water solutions with succinic acid and NaCl, Ind. Eng. Chem. Res. 56 (35) (2017) 9831-9838.
[3] F.S. Zha, B.R. Qiao, B. Kang, L. Xu, C.F. Chu, C.B. Yang, Engineering properties of expansive soil stabilized by physically amended titanium gypsum, Constr. Build. Mater. 303 (2021) 124456.
[4] Z.Y. Jiang, X.P. Sun, Y.Q. Luo, X.L. Fu, A. Xu, Y.Z. Bi, Recycling, reusing and environmental safety of industrial by-product gypsum in construction and building materials, Constr. Build. Mater. 432 (2024) 136609.
[5] S.C. Wang, J.Y. Hao, Z.G. Zhu, J.N. Chen, B. Tian, Effect of composite ratio of composite crystal modifiers on the properties of calcined gypsum, Constr. Build. Mater. 450 (2024) 138609.
[6] G. Murali, M. Azab, Recent research in utilization of phosphogypsum as building materials: Review, J. Mater. Res. Technol. 25 (2023) 960-987.
[7] C.B. Liu, J.M. Gao, Y.B. Tang, X.M. Chen, Preparation and characterization of gypsum-based materials used for 3D robocasting, J. Mater. Sci. 53 (24) (2018) 16415-16422.
[8] M. Lin, L. Zhang, J.C. Wang, X.Y. Chen, X.Y. Yang, W.G. Cui, W. Zhang, G.J. Yang, M. Liu, Y. Zhao, C.Y. Gao, Z.R. Gou, Novel highly bioactive and biodegradable gypsum/calcium silicate composite bone cements: From physicochemical characteristics to in vivo aspects, J. Mater. Chem. B 2 (14) (2014) 2030-2038.
[9] I.C. Chen, C.Y. Su, C.C. Lai, Y.S. Tsou, Y.D. Zheng, H.W. Fang, Preparation and characterization of moldable demineralized bone matrix/calcium sulfate composite bone graft materials, J. Funct. Biomater. 12 (4) (2021) 56.
[10] Y. Liu, R.C. Lu, L. He, X.M. Wang, L. Wang, X.Y. Lv, K. Zhang, F.W. Yang, Consolidation of fragile oracle bones using nano calcium sulfate hemihydrate as a protectant, Coatings 12 (6) (2022) 860.
[11] J.Y. Hao, G.J. Cheng, T. Hu, B. Guo, X.J. Li, Preparation of high-performance building gypsum by calcining FGD gypsum adding CaO as crystal modifier, Constr. Build. Mater. 306 (2021) 124910.
[12] E.C. Combe, D.C. Smith, Studies on the preparation of calcium sulphate hemihydrate by an autoclave process, J. Appl. Chem. 18 (10) (1968) 307-312.
[13] J.F. Liu, F.Q. Dong, H.B. Tan, H.P. Zhang, L. Zhou, P. He, L. Zhou, C.X. Feng, R.F. Li, Facile preparation of high-strength α-CaSO₄·0.5H₂O regulated by maleic acid from phosphogypsum: Experimental and molecular dynamics simulation studies, SN Appl. Sci. 2 (10) (2020) 1645.
[14] H.L. Fu, M.F. Li, J.S. Huang, S. Cao, J.L. Lin, M.X. Yuan, G.M. Jiang, Insights into the role of Na+ on the transformation of gypsum into α-hemihydrate whiskers in alcohol-water systems, ACS Omega 7 (18) (2022) 15570-15579.
[15] B.L. Cao, X. Wang, X.T. Zhang, B. Jin, Z.Y. Xu, X.P. Liu, W. Zhang, L.S. Yang, A readily monitored and controllable hydrothermal system for the facile, cost-effective transformation of FGD gypsum to calcium sulfate hemihydrate whiskers, Particuology 54 (2021) 173-180.
[16] Y. Mi, D.Y. Chen, A.W. Wang, Effects of phosphorus impurities on the preparation of α-calcium sulfate hemihydrate from waste phosphogypsum with the salt solution method under atmospheric pressure, CrystEngComm 21 (16) (2019) 2631-2640.
[17] R. Taherdangkoo, M.M. Tian, A. Sadighi, T. Meng, H.C. Yang, C. Butscher, Experimental data on solubility of the two calcium sulfates gypsum and anhydrite in aqueous solutions, Data 7 (10) (2022) 140.
[18] M.M. Zarei, M. Hosseini, A.H. Mohammadi, A. Moosavi, Model development for estimating calcium sulfate dihydrate, hemihydrate, and anhydrite solubilities in multicomponent acid and salt containing aqueous solutions over wide temperature ranges, J. Mol. Liq. 328 (2021) 115473.
[19] X.B. Li, Q. Zhang, B.L. Ke, X.C. Wang, L.J. Li, X.H. Li, S. Mao, Insight into the effect of maleic acid on the preparation of α-hemihydrate gypsum from phosphogypsum in Na₂SO₄ solution, J. Cryst. Growth 493 (2018) 34-40.
[20] Q.J. Guan, Y. Sui, W.J. Yu, Y.J. Bu, C.X. Zeng, C.F. Liu, Z.Y. Zhang, Z.Y. Gao, R. Chi, Deep removal of phosphorus and synchronous preparation of high-strength gypsum from phosphogypsum by crystal modification in NaCl-HCl solutions, Sep. Purif. Technol. 298 (2022) 121592.
[21] H.L. Fu, B.H. Guan, Z.B. Wu, Transformation pathways from calcium sulfite to α-calcium sulfate hemihydrate in concentrated CaCl2 solutions, Fuel 150 (2015) 602-608.
[22] B.H. Guan, L.C. Yang, Z.B. Wu, Z.X. Shen, X.F. Ma, Q.Q. Ye, Preparation of α-calcium sulfate hemihydrate from FGD gypsum in K, Mg-containing concentrated CaCl₂ solution under mild conditions, Fuel 88 (7) (2009) 1286-1293.
[23] Z.Y. Duan, J.X. Li, T.G. Li, S.R. Zheng, W.M. Han, Q.Y. Geng, H.B. Guo, Influence of crystal modifier on the preparation of α-hemihydrate gypsum from phosphogypsum, Constr. Build. Mater. 133 (2017) 323-329.
[24] B. Kong, B.H. Guan, L.C. Yang, Influence of seed crystal and modifier on the morphology of α-calcium sulfate hemihydrate prepared by salt solution method in pilot scale, Adv. Mater. Res. 168-170 (2010) 8-12.
[25] X.B. Li, Q. Zhang, Z.H. Shen, L.J. Li, X.H. Li, S. Mao, L-aspartic acid: A crystal modifier for preparation of hemihydrate from phosphogypsum in CaCl₂ solution, J. Cryst. Growth 511 (2019) 48-55.
[26] Z.R. Li, Y. Liu, D.X. Xing, Q.X. Hua, B.M. Wang, L. Liu, J.W. Tang, Effect of maleic acid and pH on the preparation of α-calcium sulfate hemihydrate from phosphogypsum in Mg(NO₃)2 solution, J. Mater. Cycles Waste Manag. 24 (1) (2022) 143-154.
[27] G. Kresse, J. Furthmuller, Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set, Comput. Mater. Sci. 6 (1) (1996) 15-50.
[28] G. Kresse, J. Furthmuller, Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set, Phys. Rev. B 54 (16) (1996) 11169-11186.
[29] J. Perdew, K. Burke, M. Ernzerhof, Generalized gradient approximation made simple, Phys. Rev. Lett. 77 (18) (1996) 3865-3868.
[30] X.M. Chen, J.M. Gao, Y. Wu, Q.H. Wu, L. Luo, Preparation of CSHW with flue gas desulfurization gypsum, Materials 15 (7) (2022) 2691.
[31] B.H. Guan, Z.X. Shen, Z.B. Wu, L.C. Yang, X.F. Ma, Effect of pH on the preparation of α-calcium sulfate hemihydrate from FGD gypsum with the hydrothermal method, J. Am. Ceram. Soc. 91 (12) (2008) 3835-3840.
[32] Y. Mi, D.Y. Chen, Y.L. He, S.Z. Wang, Morphology-controlled preparation of α-calcium sulfate hemihydrate from phosphogypsum by semi-liquid method, Cryst. Res. Technol. 53 (1) (2018) 1700162.
[33] M. Ossorio, A.E.S. Van Driessche, P. Perez, J.M. Garcia-Ruiz, The gypsum-anhydrite paradox revisited, Chem. Geol. 386 (2014) 16-21.
[34] C. Zhang, X. Zhan, T. Al-Zoubi, Y.L. Ma, P.C. Shih, F.F. Wang, W.X. Chen, S. Pidaparthy, R.M. Stephens, Q. Chen, J.M. Zuo, H. Yang, Electrochemical generation of birnessite MnO₂ nanoflowers for intercalation of Mg2+ ions, Nano Energy 102 (2022) 107696.
[35] M. Uchida, A. Okuwaki, XPS study of the passive layers formed on lead in aqueous nitrate solutions, Chem. Lett. 26 (5) (1997) 449-450.
[36] Y.S. Gao, Z.Y. Gao, W. Sun, Z.G. Yin, J.J. Wang, Y.H. Hu, Adsorption of a novel reagent scheme on scheelite and calcite causing an effective flotation separation, J. Colloid Interface Sci. 512 (2018) 39-46.
[37] D.J. Gao, D. Zhang, Y.Z. Peng, H.L. Diao, W.Q. Wang, Effects of different carboxyl additives on the growth habits of hemihydrate gypsum crystals, Constr. Build. Mater. 316 (2022) 126037.
[38] H.A. Al-Abadleh, V.H. Grassian, Phase transitions in magnesium nitrate thin films: A transmission FT-IR study of the deliquescence and efflorescence of nitric acid reacted magnesium oxide interfaces, J. Phys. Chem. B 107 (39) (2003) 10829-10839.
[39] S. Polat, P. Sayan, Determination of the effects of carboxylic acids on calcium sulfate dihydrate crystallization, Chem. Eng. Technol. 40 (7) (2017) 1354-1361.
[40] X.B. Li, Q. Zhang, Effect of molecular structure of organic acids on the crystal habit of α-CaSO₄·0.5H₂O from phosphogypsum, Crystals 10 (1) (2020) 24.

The crystal transformation characteristics from dihydrate gypsum to α-hemihydrate gypsum in Mg(NO₃)₂ solution

The crystal transformation characteristics from dihydrate gypsum to α-hemihydrate gypsum in Mg(NO₃)₂ solution

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 4

编辑推荐

Metrics

本文评价

[1]	Wencai Ye, Yulu Li, Yonggang Dong, Lin Yang, Yun Yi, Jianxin Cao. Deep decalcification of factory-provided freezing acidolysis solution to achieve α-high-strength gypsum[J]. 中国化学工程学报, 2024, 69(5): 143-151.
[2]	Qiaoqiao Liu, Guihong Lin, Jian Zhou, Liangliang Huang, Chang Liu. Hydrogen-bond mediated and concentrate-dependent NaHCO₃ crystal morphology in NaHCO₃–Na₂CO₃ aqueous solution: Experiments and computer simulations[J]. 中国化学工程学报, 2023, 55(3): 49-58.
[3]	Fang Chen, Tao Zhou, Lijie Li, Chongwei An, Jun Li, Duanlin Cao, Jianlong Wang. Morphology prediction of dihydroxylammonium 5,5'-bistetrazole-1,1'-diolate (TKX-50) crystal in different solvent systems using modified attachment energy model[J]. 中国化学工程学报, 2023, 53(1): 181-193.
[4]	杨芗钰, 钱刚, 张相洋, 段学志, 周兴贵. Effects of Solvent and Impurities on Crystal Morphology of Zinc Lactate Trihydrate[J]. Chinese Journal of Chemical Engineering, 2014, 22(2): 221-226.