Direct Synthesis of Diphenyl Carbonate with Heterogeneous Catalyst and Optimal Synthesis Conditions of the Support Prepared by Sol-gel Method

摘要/Abstract

摘要： The support of catalyst for the direct synthesis of diphenyl carbonate(DPC)by heterogeneous catalytic reaction was prepared by the sol-gel method.Compared with activated charcoal,molecular sieve,porous ceramics, hopcalite,the support prepared by the sol-gel method has higher activity.The characterization of the support by X-ray diffraction(XRD)and transmission electron microscope(TEM)show that the main crystal phase is Co₂MnO₄ and the average particle diameter is about 40 nm.The optimum conditions for synthesis of the support were determined by orthogonal experiments,which indicate that the proportion of Cu,Mn,and Co is the first important factor influencing the yield and selectivity of DPC.Temperature of calcination is the second one.The optimum conditions are:molar proportion of Cu,Mn,and Co being 1:1:1,temperature of calcination 700℃,drying at 100℃,temperature of water bath 85℃.The yield and selectivity of DPC in the process can reach 38% and 99% in the batch operation,respectively.The copper cobalt manganese mixed oxides chosen as the support contribute more to the high catalytic activity than the sol-gel method.

关键词: diphenyl carbonate, heterogeneous catalyst, sol-gel method, optimum condition

Abstract: The support of catalyst for the direct synthesis of diphenyl carbonate(DPC)by heterogeneous catalytic reaction was prepared by the sol-gel method.Compared with activated charcoal,molecular sieve,porous ceramics, hopcalite,the support prepared by the sol-gel method has higher activity.The characterization of the support by X-ray diffraction(XRD)and transmission electron microscope(TEM)show that the main crystal phase is Co₂MnO₄ and the average particle diameter is about 40 nm.The optimum conditions for synthesis of the support were determined by orthogonal experiments,which indicate that the proportion of Cu,Mn,and Co is the first important factor influencing the yield and selectivity of DPC.Temperature of calcination is the second one.The optimum conditions are:molar proportion of Cu,Mn,and Co being 1:1:1,temperature of calcination 700℃,drying at 100℃,temperature of water bath 85℃.The yield and selectivity of DPC in the process can reach 38% and 99% in the batch operation,respectively.The copper cobalt manganese mixed oxides chosen as the support contribute more to the high catalytic activity than the sol-gel method.

Key words: diphenyl carbonate, heterogeneous catalyst, sol-gel method, optimum condition

郭红霞, 陈红萍, 梁英华, 芮玉兰, 吕敬德, 付占达. Direct Synthesis of Diphenyl Carbonate with Heterogeneous Catalyst and Optimal Synthesis Conditions of the Support Prepared by Sol-gel Method[J]. , 2008, 16(2): 223-227.

GUO Hongxia, CHEN Hongping, LIANG Yinghua, RUI Yulan, LÜ Jingde, FU Zhanda. Direct Synthesis of Diphenyl Carbonate with Heterogeneous Catalyst and Optimal Synthesis Conditions of the Support Prepared by Sol-gel Method[J]. , 2008, 16(2): 223-227.

参考文献

1 Meenakshi, G., Ritsuko, N., Mitsuru, U., “Direct synthesis of diphenyl carbonate by oxidative carbonylation of phenol using Pd-Cu based redox catalyst”, J. Mol. Cat. A Chem., 137, 147-154 (1999).
2 Meenakshi, G., Ritsuko, N., Sugiyama, J., “Effect of inorganic redox cocatalyst on Pdcatalyzed for direct synthesis of diphenyl carbonate”, Catal. Lett., 54, 29-31 (1998).
3 Hirotoshi, I., Mistsuru, U., Kazuhiko, T., “Oxidative carbonylation of phenol carbonate catalyzed by Pd-Sn complexes with redox catalyst”, J. Mol. Catal. A Chem., 138, 311-313 (1999).
4 Hirotoshi, I., Mistsuru, U., Kazuhiko, T., “Oxidative carbonylation of phenol carbonate catalyzed by Pd-Sn heterotrinuclear complexes along with Mn redox catalyst without any addition of ammonium halide”, J. Mol .Catal. A Chem., 144, 369-372 (1999).
5 Goyal, M., Nagahata, R., Sugiyama, J., “Direct synthesis of diphenyl carbonate by oxidative carbonylation of phenol using Pd-Cu based redox catalyst system”, J. Mol. Catal. A Chem., 137, 147-154 (1999).
6 Liu, H.W., Zhao, X.Q., Wang, Y.J., “Oxidative carbonylation of phenol to diphenyl carbonate over palladium complexes catalysts”, J. Sichuan Univ., 34 (1), 47-49 (2002). (in Chinese)
7 Okuyama, K., Sugiyama, J., Nagahata, R., “Oxidative carbonylation of phenol to diphenyl carbonate catalyzed by palladium-carbene complexes”, J. Mol. Catal. A Chem., 203, 21-27 (2003).
8 Buysch, H.J., Hess, C., Jentsch, J.D., “Supported platinum-group metal preparation of diaryl carbonates”, Eur. Pat., 736325 (1996).
9 Buysch, H.J., Jentsch, J.D, Rechner, J., “Supported platinum catalysts and process for preparation of diary carbonates”, Eur, Pat., 736324 (1996).
10 Hesse, C., Nothesis, U., Rechner, J., “Supported platinum-group metal for producing diaryl carbonates from carbon monoxide”, WO Pat., 9908786 (1999).
11 Takagi, W., “Preparation of aromatic carbonates as materials for polycarbonates”, Japan Pat., 09278716 (1997).
12 Song, H.Y., Yark, D., Lee, J.S., “Oxidative carbonylation of phenol to diphenyl carbonate over supported palladium catalysts”, J. Mo1. Catal. A Chem., 154, 243-250 (2000).
13 Xue, W., Wang, Y.J., Zhao, X.Q., “Oxidative carbonylation of phenol to diphenyl carbonate over supported embedded catalyst Pd-Cu-O/SiO₂ prepared through W/O microemulsion method”, In: Catalysis and 21st Century Challenge-Basic Science and the Needs of Society, The proceedings of the 13th International Conference on Catalysis, Vol. 7, Paris, 1-321 (2004).
14 Xue, W., Zhao, X.Q., Wang, Y.J., “Effect of promoter copper on the oxidative carbonylation of phenol over the ultrafine embedded catalyst Pd-Cu-O/SiO₂ ”, J. Mol. Catal. A Chem., 232, 77-81 (2005).
15 Zhang, G.X., Wu, Y.X., Ma, P.S., Wu, G.W., Li, D.H., “Study on direct synthesis of diphenyl carbonate with heterogeneous catalyzing reaction (I) Effect of method of preparing Pd catalyst carriers on catalyst activity”, Chin. J. Catal., 23 (2), 130-132 (2002). (in Chi-nese)
16 Zhang, G.X., Ma, P.S., Wu, Y.X., Wu, G.W., Li, D.H., “Study on direct synthesis of diphenyl carbonate with heterogeneous catalyzing reaction (II) Effect of calcination temperature on catalytic activity of catalyst”, Chin. J. Fuel Chem. Tech., 30 (4), 362-367 (2002). (in Chinese)
17 Zhang, G.X., Wu, Y.X., Ma, P.S., Wu, G.W., Li, D.H., “Study on direct synthesis of diphenyl carbonate with heterogeneous catalyzing reaction (III) Effect of lanthanum content on catalytic activity of catalyst”, Chin. J. Mol. Catal., 16 (4), 292-297 (2002). (in Chinese)
18 Zhang, G.X., Wu, Y.X., Ma, P.S., Wu, G.W., Li, D.H., “Study on direct synthesis of diphenyl carbonate with heterogeneous catalyzing reaction (IV) Effect of active components and the supporting meth-ods on catalytic activity of catalyst”, Chin. J. Catal., 23 (5), 410-416 (2002). (in Chinese)
19 Zhang, G.X., Wu, Y.X., Ma, P.S., Tian, Q.F., Wu, G.W., Li, D.H., Wang, C.W., “Study on direct synthesis of diphenyl carbonate with heterogeneous catalytic reaction (V) Screening catalysts and optimizing synthesis conditions”, Chin. J. Chem. Eng., 11 (5), 526-530 (2003).
20 Zhang, G.X., Wu, Y.X., Ma, P.S., Tian, Q.F., Wu, G.W., Li, D.H., “Study on direct synthesis of diphenyl carbonate with heterogeneous catalytic reaction (VI) Effect of Sn loading method and content on activity of Sn-Pd supported catalyst”, Chin. J. Chem. Eng., 12 (2), 191-195 (2004).
21 Iwane, H., Miyagi, H., Imada, S., “Method of producing aromatic carbonate”, Eur. Pat., 0614876 (1993).
22 Takagi, M., Miyagi, H., Yoneyama, T., “Palladium-lead catalyzed oxidative of phenol”, J. Mol. Catal. A Chem., 129, 1-3 (1998).
23 Xue, W., Wang, Y.J., Zhao, X.Q., “Oxidative carbonylation of phenol over the mesoporous palladium-copper-oxide/silica catalyst prepared by sol-gel coupling with W/O microemulsion”, Catal. Today, 105, 724-728 (2005).

[1]	Bowen Jiang, Jia Liu, Guoqiang Yang, Zhibing Zhang. Efficient conversion of CO₂ into cyclic carbonates under atmospheric by halogen and metal-free poly(ionic liquid)s[J]. 中国化学工程学报, 2023, 55(3): 202-211.
[2]	Jiahao Wei, Fan Li, Lina Zhou, Dandan Han, Junbo Gong. Strategies for enhancing peroxymonosulfate activation by heterogenous metal-based catalysis: A review[J]. 中国化学工程学报, 2022, 50(10): 12-28.
[3]	Ruilong Zhang, Zhiping Zhou, Wenna Ge, Yi Lu, Tianshu Liu, Wenming Yang, Jiangdong Dai. Robust, fluorine-free and superhydrophobic composite melamine sponge modified with dual silanized SiO₂ microspheres for oil-water separation[J]. 中国化学工程学报, 2021, 33(5): 50-60.
[4]	Chaofeng Zhang, Tonglu Zhang, Jing Zhang, Jiandong Zhang, Ruifeng Li. Controllable synthesis of polyoxymethylene dimethyl ethers by ionic liquids encapsulated in mesoporous SBA-16[J]. 中国化学工程学报, 2021, 32(4): 175-182.
[5]	Lichao Zhou, Gang Feng, Xiaojing Liu, Zhimiao Wang, Fang Li, Wei Xue, Yanji Wang. Effect of Zr-doping on Pd/Ce_xZr_1-xO₂ catalysts for oxidative carbonylation of phenol[J]. 中国化学工程学报, 2020, 28(10): 2592-2599.
[6]	Mohammad Ali Rezvani, Sahar Khandan, Negin Sabahi, Hamid Saeidian. Deep oxidative desulfurization of gas oil based on sandwich-type polysilicotungstate supported β-cyclodextrin composite as an efficient heterogeneous catalyst[J]. 中国化学工程学报, 2019, 27(10): 2418-2426.
[7]	Hajar Taheri Afarani, Morteza Sadeghi, Ahmad Moheb, Ebrahim Nasr Esfahani. Optimization of the gas separation performance of polyurethane-zeolite 3A and ZSM-5 mixed matrix membranes using response surface methodology[J]. Chinese Journal of Chemical Engineering, 2019, 27(1): 110-129.
[8]	Muhammad Ammar, Yan Cao, Peng He, Liguo Wang, Jiaqiang Chen, Huiquan Li. An efficient green route for hexamethylene-1,6-diisocyanate synthesis by thermal decomposition of hexamethylene-1,6-dicarbamate over Co₃O₄/ZSM-5 catalyst: An indirect utilization of CO₂[J]. Chinese Journal of Chemical Engineering, 2017, 25(12): 1760-1770.
[9]	Radha Devi Chekuri, Siva Rao Tirukkovalluri. One step synthesis and characterization of copper doped sulfated titania and its enhanced photocatalytic activity in visible light by degradation of methyl orange[J]. Chinese Journal of Chemical Engineering, 2016, 24(4): 475-483.
[10]	Magdalena Streckova, Radovan Bures, Maria Faberova, Lubomir Medvecky, Jan Fuzer, Peter Kollar. A comparison of soft magnetic composites designed from different ferromagnetic powders and phenolic resins[J]. Chinese Journal of Chemical Engineering, 2015, 23(4): 736-743.
[11]	郭强, 王涛. Preparation and Characterization of Sodium Sulfate/Silica Composite as a Shape-stabilized Phase Change Material by Sol-gel Method[J]. Chinese Journal of Chemical Engineering, 2014, 22(3): 360-364.
[12]	鲁威, 杜治平, 袁华, 田琦峰, 吴元欣 . Synthesis of Diphenyl Carbonate over the Magnetic Catalysts Pd/La_1-xPb_xMnO₃ (x=0.2-0.7)[J]. Chinese Journal of Chemical Engineering, 2013, 21(1): 8-13.
[13]	袁文辉, 申荣平, 李莉. Synthesis and Conductivity of Oxyapatite Ionic Conductor La_10-xV_x（SiO₄）₆O_3+x[J]. , 2010, 18(2): 328-332.
[14]	梁英华, 郭红霞, 陈红萍, 吕敬德, 张波波. Effect of Doping Cerium in the Support of Catalyst Pd-Co/Cu-Co-Mn Mixed Oxides on the Oxidative Carbonylation of Phenol[J]. , 2009, 17(3): 401-406.
[15]	程庆彦, 梁亚男, 高玲, 王延吉. Synthesis of Pd(C₄H₂O₄)(C₄H₈N₂)_0.5 Complex and the Catalytic Activity for Oxidative Carbonylation of Phenol[J]. , 2008, 16(3): 354-356.