Preparation and characterization of neodymium hydroxide powder via the hydration method

doi:10.1016/j.cjche.2020.04.018

中国化学工程学报 ›› 2020, Vol. 28 ›› Issue (7): 1973-1980.DOI: 10.1016/j.cjche.2020.04.018

• Materials and Product Engineering • 上一篇下一篇

Preparation and characterization of neodymium hydroxide powder via the hydration method

Hongxi Li, Chenggong Xu, Qishan Yang

School of Chemistry and Chemical Engineering, Inner Mongolia University of Science and Technology, Baotou 014010, China

收稿日期:2020-02-15 修回日期:2020-04-09 出版日期:2020-07-28 发布日期:2020-08-31
通讯作者: Qishan Yang
基金资助:
The authors gratefully acknowledge the financial support for this study by the Natural Science Foundation of Inner Mongolia (CN) (2016ZD05).

Preparation and characterization of neodymium hydroxide powder via the hydration method

Hongxi Li, Chenggong Xu, Qishan Yang

School of Chemistry and Chemical Engineering, Inner Mongolia University of Science and Technology, Baotou 014010, China

Received:2020-02-15 Revised:2020-04-09 Online:2020-07-28 Published:2020-08-31
Contact: Qishan Yang
Supported by:
The authors gratefully acknowledge the financial support for this study by the Natural Science Foundation of Inner Mongolia (CN) (2016ZD05).

摘要/Abstract

摘要： The preparation of Nd(OH)₃ powder by the direct hydration method using Nd₂O₃ as a raw material was studied, and the effects of stirring mode, H₂O and Nd₂O₃ molar ratio, stirring rate, and reaction time on temperature change and conversion rate in a hydration system were analyzed. The reasonable process conditions for the direct hydration of Nd(OH)₃ by Nd₂O₃ were then determined. Process, morphology, and structure were considered in the preparation of neodymium hydroxide powder, and its composition was investigated by X-ray powder diffraction, scanning electron microscopy, laser particle size analysis, thermogravimetric differential thermal analysis, and chemical analysis. It has been proved that the process is simple and feasible, in line with the concept of modern green chemistry, and the products also meet the market requirements.

关键词: Hydration method, Neodymium hydroxide, Powder preparation, Influencing factor, Green chemical engineering

Abstract: The preparation of Nd(OH)₃ powder by the direct hydration method using Nd₂O₃ as a raw material was studied, and the effects of stirring mode, H₂O and Nd₂O₃ molar ratio, stirring rate, and reaction time on temperature change and conversion rate in a hydration system were analyzed. The reasonable process conditions for the direct hydration of Nd(OH)₃ by Nd₂O₃ were then determined. Process, morphology, and structure were considered in the preparation of neodymium hydroxide powder, and its composition was investigated by X-ray powder diffraction, scanning electron microscopy, laser particle size analysis, thermogravimetric differential thermal analysis, and chemical analysis. It has been proved that the process is simple and feasible, in line with the concept of modern green chemistry, and the products also meet the market requirements.

Key words: Hydration method, Neodymium hydroxide, Powder preparation, Influencing factor, Green chemical engineering

Hongxi Li, Chenggong Xu, Qishan Yang. Preparation and characterization of neodymium hydroxide powder via the hydration method[J]. 中国化学工程学报, 2020, 28(7): 1973-1980.

Hongxi Li, Chenggong Xu, Qishan Yang. Preparation and characterization of neodymium hydroxide powder via the hydration method[J]. Chinese Journal of Chemical Engineering, 2020, 28(7): 1973-1980.

参考文献

[1] F. Khodam, H.R. Amani-Ghadim, S. Aber, A.R. Amani-Ghadim, I. Ahadzadeh, Neodymium doped mixed metal oxide derived from CoAl-layered double hydroxide:Considerable enhancement in visible light photocatalytic activity, J. Ind. Eng. Chem. 68(2018) 311-324.
[2] Y.B. Xie, C.W. Yuan, Photocatalysis of neodymium ion modified TiO₂ sol under visible light irradiation, Appl. Surf. Sci. 221(2004) 17-24.
[3] J.I. Zhu, Y.H. Zhou, H. Yang, Effects of lanthanum and neodymium hydroxides on secondary alkaline zinc electrode, J. Power Sources 69(1997) 169-173.
[4] D. Yin, K.B. Zhang, L. Peng, Z.S. He, Y. Liu, H.B. Zhang, X.R. Lu, Solid-state reaction synthesis and chemical stability studies in Nd-doped zirconolite-rich ceramics, J Rare Earth 36(2018) 492-498.
[5] S. Balabhadra, M.L. Debasu, C.D. Brites, L.A. Nunes, O.L. Malta, J. Rocha, M. Bettinelli, L.D. Carlos, Boosting the sensitivity of Nd³⁺-based luminescent nanothermometers, Nanoscale 7(2015) 17261-17267.
[6] S.R. Sanivarapu, J.B. Lawrence, G. Sreedhar, Role of surface oxygen vacancies and lanthanide contraction phenomenon of Ln(OH)3(Ln=La, Pr, and Nd) in sulfide-mediated photoelectrochemical water splitting, ACS Omega 3(6) (2018) 6267-6278.
[7] B.C. Yadav, M. Singh, Morphological and humidity sensing investigations on niobium, neodymium, and lanthanum oxides, IEEE Sensors J. 10(11) (2010) 1759-1766.
[8] T.T. Liu, H. Lei, Nd³⁺-doped colloidal SiO₂ composite abrasives:Synthesis and the effects on chemical mechanical polishing (CMP) performances of sapphire wafers, Appl. Surf. Sci. 413(2017) 16-26.
[9] J.J. Wang, G.L. Xiao, Y.Z. Xu, Y. Zhou, B.Q. Xiong, S. Cui, D.J. Wang, D.F. Xu, An investigation of different morphological and structural changes in neodymium hydroxide nanoparticles, J. Cryst. Growth 286(1) (2006) 78-82.
[10] W.Q. Zhu, J. Ma, L. Xu, W.Z. Zhang, Y.S. Chen, Controlled synthesis of Nd(OH)3 and Nd₂O₃ nanoparticles by microemulsion method, Mater. Chem. Phys. 122(2010) 362-367.
[11] S. Arunachalam, B. Kirubasankar, V.M. Murugadoss, D. Vellasamy, S. Angaiah, Facile synthesis of electrostatically anchored Nd(OH)3 nanorods onto graphene nanosheets as a high capacitance electrode material for supercapacitors, New J Chem 42(4) (2018) 2923-2932.
[12] Bin Yu, D.L. Jia, Y.Q. Miao, Nanoparticles of Nd(OH)₃-NiTe₂ for electrocatalytic oxidation of glucose, J Mater Sci-Mater El. 31(3) (2020) 2360-2369.
[13] S.Y. Liu, Y. Cai, X.Y. Cai, H. Li, F. Zhang, Q.Y. Mu, Y.J. Liu, Y.D. Wang, Catalytic photodegradation of Congo red in aqueous solution by Ln(OH)3(Ln=Nd, Sm, Eu, Gd, Tb, and Dy) nanorods, Appl Catal A-Gen. 453(2013) 45-53.
[14] P. Liszkowski, K. Turek, H. Figiel, The intermediate stages of the corrosion of Nd-Fe-B powders in ambient air, J Alloy Compd. 315(1-2) (2001) 270-275.
[15] A. Phuruangrat, S. Thongtem, T. Thongtem, Template-free synthesis of neodymium hydroxide nanorods by microwave-assisted hydrothermal process, and of neodymium oxide nanorods by thermal decomposition, Ceram. Int. 38(2012) 4075-4079.
[16] T. Thongtem, A. Phuruangrat, D.J. Ham, J.S. Lee, S. Thongtem, Controlled Gd₂O₃ nanorods and nanotubes by the annealing of Gd(OH)3 nanorod and nanotube precursors and self-templates produced by a microwave-assisted hydrothermal process, Crystengcomm 12(2010) 2962-2966.
[17] C.Y. Li, H. Liu, J. Yang, A facile hydrothermal approach to the synthesis of nanoscale rare earth hydroxides, Nanoscale Res Lett 10(1) (2015) 144.
[18] N. Ekthammathat, A. Phuruangrat, B. Kuntalue, S. Thongtem, T. Thongtem, Preparation of neodymium hydroxide nanorods and neodymium oxide nanorods by a hydrothermal method, Dig J of Nanomater Bios 10(2015) 715-719.
[19] Y. Xin, Z.P. Wang, Y.X. Qi, Z.L. Zhang, S.X. Zhang, Synthesis of rare earth (Pr, Nd, Sm, Eu and Gd) hydroxide and oxide nanorods (nanobundles) by a widely applicable precipitation route, J Alloy Compd 507(2010) 105-111.
[20] S. Arunachalam, B. Kirubasankar, E. Rajagounder Nagarajan, D. Vellasamy, S. Angaiah, A facile chemical precipitation method for the synthesis of Nd(OH)3 and La(OH)3 nanopowders and their supercapacitor performances, ChemistrySelect 3(2018) 12719-12724.
[21] M. Nagao, H. Hamano, K. Hirata, R. Kumashiro, Y. Kuroda, Hydration process of rareearth sesquioxides having different crystal structures, Langmuir 19(2003) 9201-9209.
[22] P. Bocchetta, M. Santamaria, F. Di Quarto, Template electrosynthesis of La(OH)3 and Nd(OH)3 nanowires using porous anodic alumina membranes, Electrochem. Commun. 9(2007) 683-688.
[23] P. Martineztorres, S.E. Borjasgarcia, N. Gomezortiz, N. Dasguptaschubert, J.L. Pichardomolina, D.R. Garciazavala, Synthesis of neodymium hydroxide nanoparticles with CTAB at low temperature, Microsc. Microanal. 23(2017) 1954-1955.
[24] B.P. Gangwar, S.C. Maiti, S. Sharma, Modifying the hygroscopic property of La₂O₃ by Pr.Sm and Nd doping, J Solid State Chem 256(2017) 109-115.
[25] L.R. Morss, C.M. Haar, S. Mroczkowski, Standard molar enthalpy of formation of neodymium hydroxide, J. Chem. Thermodyn. 21(10) (1989) 1079-1083.
[26] H. Samata, D. Kimura, S. Mizusaki, Y. Nagata, T.C. Ozawa, A. Sato, Synthesis and characterization of neodymium oxyhydroxide crystals, J Alloy Compd 468(1-2) (2009) 566-570.
[27] R.S. Tobias, A.B. Garrett, The thermodynamic properties of neodymium hydroxide Nd(OH)3, in acid, neutral and alkaline solutions at 25°; the hydrolysis of the neodymium and praseodymium ions, Nd³⁺, Pr³⁺, J. Am. Chem. Soc. 80(14) (1958) 3532-3537.
[28] N. Zhang, R. Yi, L.B. Zhou, G.H. Gao, R.R. Shi, G.Z. Qiu, X.H. Liu, Lanthanide hydroxide nanorods and their thermal decomposition to lanthanide oxide nanorods, Mater. Chem. Phys. 114(1) (2009) 160-167.

Preparation and characterization of neodymium hydroxide powder via the hydration method

Preparation and characterization of neodymium hydroxide powder via the hydration method

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 0

编辑推荐

Metrics

本文评价