关键词: Lithium metal battery, Solid-state electrolyte, Li-ZnO anode

Abstract: Due to high ionic conductivity and wide electrochemical window, the garnet solid electrolyte is considered as the most promising candidate electrolyte for solid-state lithium metal batteries. However, the high contact impedance between metallic lithium and the garnet solid electrolyte surface seriously hampers its further application. In this work, a Li-(ZnO)_x anode is prepared by the reaction of zinc oxide with metallic lithium and in situ coated on the surface of Li_6.8La₃Zr_1.8Ta_0.2O₁₂(LLZTO). The anode can be perfectly bound to the surface of LLZTO solid electrolyte, and the anode/electrolyte interfacial resistance was reduced from 2319 to 33.75 Ω·cm². The Li-(ZnO)_0.15|LLZTO|Li-(ZnO)_0.15 symmetric battery exhibits a stable Li striping/plating process during charge-discharging at a constant current density of 0.1 mA·cm^-2 for 100 h at room temperature. Moreover, a Li-(ZnO)_0.15|LLZTO-SPE|LFP full battery, comprised of a polyethylene oxide-based solid polymer electrolyte (SPE) film as an interlayer between LiFePO₄ (LFP) cathode and LLZTO solid electrolyte, presents an excellent performance at 60 ℃. The discharge capacity of the full battery reaches 140 mA·h·g^-1 at 0.1 C and the capacity attenuation is less than 3% after 50 cycles.

Key words: Lithium metal battery, Solid-state electrolyte, Li-ZnO anode