Strong water-resistant Co-Mn solid solution derived from bimetallic metal–organic frameworks for catalytic destruction of toluene

doi:10.1016/j.cjche.2024.06.027

Chinese Journal of Chemical Engineering ›› 2024, Vol. 75 ›› Issue (11): 142-151.DOI: 10.1016/j.cjche.2024.06.027

Previous Articles Next Articles

Strong water-resistant Co-Mn solid solution derived from bimetallic metal–organic frameworks for catalytic destruction of toluene

Juan Lei¹, Ying Huang^2,3, Baobao Bai^2,3, Xiaoli Ren¹, Lijun Cheng¹, Shuang Wang²

1. Department of Environmental and Safety Engineering, Taiyuan Institute of Technology, Taiyuan 030018, China;
2. College of Environment and Ecology, Taiyuan University of Technology, Jinzhong 030600, China;
3. Shanxi Key Laboratory of Compound Air Pollutions Identification and Control, Taiyuan University of Technology, Jinzhong 030600, China

Received:2024-04-16 Revised:2024-06-12 Accepted:2024-06-13 Online:2024-08-23 Published:2024-11-28
Contact: Shuang Wang,E-mail:wangshuang@tyut.edu.cn
Supported by:
The authors acknowledge the financial support of the National Natural Science Foundation of China (22408252, 22078215), Natural Science Foundation for Youths of Shanxi Province (202103021223347), Taiyuan Institute of Technology Talent Introduction Research funding Project (2022KJ010), and Shanxi Province Science and Technology Major Special Plan “Reveal The List and Take Charge” Project (202201090301014).

Strong water-resistant Co-Mn solid solution derived from bimetallic metal–organic frameworks for catalytic destruction of toluene

Juan Lei¹, Ying Huang^2,3, Baobao Bai^2,3, Xiaoli Ren¹, Lijun Cheng¹, Shuang Wang²

1. Department of Environmental and Safety Engineering, Taiyuan Institute of Technology, Taiyuan 030018, China;
2. College of Environment and Ecology, Taiyuan University of Technology, Jinzhong 030600, China;
3. Shanxi Key Laboratory of Compound Air Pollutions Identification and Control, Taiyuan University of Technology, Jinzhong 030600, China

通讯作者: Shuang Wang,E-mail:wangshuang@tyut.edu.cn
基金资助:
The authors acknowledge the financial support of the National Natural Science Foundation of China (22408252, 22078215), Natural Science Foundation for Youths of Shanxi Province (202103021223347), Taiyuan Institute of Technology Talent Introduction Research funding Project (2022KJ010), and Shanxi Province Science and Technology Major Special Plan “Reveal The List and Take Charge” Project (202201090301014).

Abstract

Abstract: The construction of Co-Mn mixed-metal oxide catalysts derived from bimetallic metal-organic frameworks (MOFs) has great significance for catalytic destruction of toluene. Hence, a series of Co_aMn_bO_x-MOFs with different physicochemical properties were successfully synthesized via pyrolysis of Co—Mn bimetallic MOFs. Attributing to the higher specific surface area, more active sites (Co³⁺ and Mn³⁺), stronger reducibility, and abundant defect sites, the as-prepared Co₁Mn₁O_x-MOFs displayed an optimal catalytic performance, especially the excellent water vapor resistance. The result of the in situ diffuse reflectance infrared Fourier transform spectroscopy demonstrated that toluene can be degraded at relatively low temperatures (＜100 ℃). Benzyl alcohol, benzaldehyde, benzoic acid, and maleic anhydride were the main intermediate products in toluene degradation process. This work reveals the value of bimetallic MOFs derived Co—Mn oxides for toluene oxidation and presents a novel avenue for designing mixed-metal oxide catalysts with potential applications in volatile organic compounds (VOCs) catalytic oxidation.

Key words: Co-Mn oxide catalyst, Bimetallic metal-organic frameworks (MOFs), Catalytic oxidation, Water-resistant

摘要： The construction of Co-Mn mixed-metal oxide catalysts derived from bimetallic metal-organic frameworks (MOFs) has great significance for catalytic destruction of toluene. Hence, a series of Co_aMn_bO_x-MOFs with different physicochemical properties were successfully synthesized via pyrolysis of Co—Mn bimetallic MOFs. Attributing to the higher specific surface area, more active sites (Co³⁺ and Mn³⁺), stronger reducibility, and abundant defect sites, the as-prepared Co₁Mn₁O_x-MOFs displayed an optimal catalytic performance, especially the excellent water vapor resistance. The result of the in situ diffuse reflectance infrared Fourier transform spectroscopy demonstrated that toluene can be degraded at relatively low temperatures (＜100 ℃). Benzyl alcohol, benzaldehyde, benzoic acid, and maleic anhydride were the main intermediate products in toluene degradation process. This work reveals the value of bimetallic MOFs derived Co—Mn oxides for toluene oxidation and presents a novel avenue for designing mixed-metal oxide catalysts with potential applications in volatile organic compounds (VOCs) catalytic oxidation.

关键词: Co-Mn oxide catalyst, Bimetallic metal-organic frameworks (MOFs), Catalytic oxidation, Water-resistant

Juan Lei, Ying Huang, Baobao Bai, Xiaoli Ren, Lijun Cheng, Shuang Wang. Strong water-resistant Co-Mn solid solution derived from bimetallic metal–organic frameworks for catalytic destruction of toluene[J]. Chinese Journal of Chemical Engineering, 2024, 75(11): 142-151.

References

[1] H.Y. Li, Z.X. Song, Y.L. Mao, X.J. Zhang, Z.Z. Huang, W. Liu, H.R. Gao, D.Y. Dong, Degradation mechanism of toluene over Ce-M (Cu, Co and Fe) catalysts: effect of oxygen vacancies on reaction intermediates, Appl. Surf. Sci. 652 (2024) 159272.
[2] Z.H. Lu, L. Guo, Q.Y. Shen, F.K. Bi, C.Y. Li, X.D. Zhang, The application of metal-organic frameworks and their derivatives in the catalytic oxidation of typical gaseous pollutants: recent progress and perspective, Sep. Purif. Technol. 340 (2024) 126772.
[3] F.K. Bi, J.F. Wei, S.T. Ma, Q.Y. Zhao, J.R. Zhang, R. Qiao, J.C. Xu, B.L. Liu, Y.D. Huang, X.D. Zhang, Fluorination modification enhanced the water resistance of Universitetet i Oslo-67 for multiple volatile organic compounds adsorption under high humidity conditions: mechanism study, J. Colloid Interface Sci. 665 (2024) 898-910.
[4] B. Gao, X.B. Feng, Y.F. Zhang, Z.X. Zhou, J.F. Wei, R. Qiao, F.K. Bi, N. Liu, X.D. Zhang, Graphene-based aerogels in water and air treatment: a review, Chem. Eng. J. 484 (2024) 149604.
[5] X.D. Zhang, R.Z. Rao, B. Gao, S.T. Ma, F.K. Bi, C.Y. Li, Z.Q. Zhu, N. Liu, Y.Q. Yang, Z. Wang, Crystal engineering of TiO₂ enhanced photothermal catalytic degradation of DEHP on Pt catalysts, Mater. Today Chem. 34 (2023) 101755.
[6] X.D. Zhang, B. Gao, R.Z. Rao, F.K. Bi, C.Y. Li, K. Yue, Y.X. Wang, J.C. Xu, X.B. Feng, Y.Q. Yang, Defects materials of Institut Lavoisier-125(Ti) materials enhanced photocatalytic activity for toluene and chlorobenzene mixtures degradation: mechanism study, J. Colloid Interface Sci. 660 (2024) 423-439.
[7] F.K. Bi, J.F. Wei, B. Gao, N. Liu, J.C. Xu, B.L. Liu, Y.D. Huang, X.D. Zhang, New insight into the antagonism mechanism between binary VOCs during their degradation over Pd/ZrO₂ catalysts, ACS EST Eng. 4 (6) (2024) 1346-1355.
[8] Q.Y. Shen, Z.H. Lu, F.K. Bi, D.F. Zhang, L.J. Li, X.D. Zhang, Y.Q. Yang, M.H. Wu, Regulating electronic metal-support interaction by synthetic methods to enhance the toluene degradation over Pt/Co₃O₄ catalysts, Sep. Purif. Technol. 325 (2023) 124707.
[9] L. Sun, S.Z. Zhao, X.L. Tang, Q.J. Yu, F.Y. Gao, J. Liu, Y. Wang, Y.S. Zhou, H.H. Yi, Recent advances in catalytic oxidation of VOCs by two-dimensional ultra-thin nanomaterials, Sci. Total Environ. 920 (2024) 170748.
[10] Z.Z. Huang, M. Zhao, J.W. Luo, X.J. Zhang, W. Liu, Y.H. Wei, J.G. Zhao, Z.X. Song, Interaction in LaO_x-Co₃O₄ for highly efficient purification of toluene: insight into LaO_x content and synergistic effect contribution, Sep. Purif. Technol. 251 (2020) 117369.
[11] Z.X. Song, M. Zhao, Y.L. Mao, X.J. Zhang, J.W. Luo, B. Liu, H. Lu, W. Liu, Y. Xing, X.F. Zhu, Turning the structural properties and redox ability of Co-La catalyst in the catalytic oxidation of toluene, Sep. Purif. Technol. 274 (2021) 119025.
[12] Z.X. Song, Y.H. Wei, Z.A. Ma, X.J. Zhang, Y.L. Mao, J.W. Luo, X.F. Zhu, W. Liu, J.J. Jin, Influence of different sources of cerium on the oxidation-reduction ability and oxygen vacancies of CeO₂-MnO_x in the catalytic oxidation of toluene, Surf. Interfaces 24 (2021) 101042.
[13] H.Y. Li, Z.X. Song, Z.F. Zhang, X.J. Zhang, Y.L. Mao, W. Liu, Z.Z. Huang, J.H. Zhang, D.Y. Dong, Y.L. Luo, Catalytic combustion of toluene performance over MnO_x catalysts: effect of KMnO₄ content, Appl. Organomet. Chem., (2024) e7388.
[14] J. Lei, S. Wang, J.P. Li, Y.P. Xu, S.Y. Li, Different effect of Y (Y=Cu, Mn, Fe, Ni) doping on Co₃O₄ derived from Co-MOF for toluene catalytic destruction, Chem. Eng. Sci. 251 (2022) 117436.
[15] Z.X. Song, H.Y. Li, X.J. Zhang, Z.F. Zhang, Y.L. Mao, W. Liu, Z.P. Liu, D.J. Mo, X.F. Zhu, Z.Z. Huang, The catalytic oxidation performance of toluene over the MnO _x catalysts: effect of MnSO₄ content, Chem. Phys. Impact 5 (2022) 100124.
[16] J. Lei, J.J. Chen, B.B. Bai, P. Wang, S. Wang, J.P. Li, Regulation of the existing state of Cu species in high water-toletant CuO_x-Mn₃O₄ for VOCs mixtrue catalytic oxidation, Chem. Eng. Sci. 284 (2024) 119455.
[17] W.L. Zhang, M.Y. Li, X.T. Wang, X.W. Zhang, X.Y. Niu, Y.J. Zhu, Boosting catalytic toluene combustion over Mn doped Co₃O₄ spinel catalysts: improved mobility of surface oxygen due to formation of Mn-O-Co bonds, Appl. Surf. Sci. 590 (2022) 153140.
[18] R. Huang, L. Luo, W. Hu, Z.X. Tang, X. Ji, L.Q. Chen, Z.S. Yu, Y.H. Zhang, D. Zhang, P. Xiao, Insight into the pH effect on the oxygen species and Mn chemical valence of Co-Mn catalysts for total toluene oxidation, Catal. Sci. Technol. 12 (13) (2022) 4157-4168.
[19] J. Yao, F. Dong, H. Feng, Z.C. Tang, Hierarchical MnO_x/Co₃O₄ nanoarrays on Ni foam for catalytic oxidation of volatile organic compounds, ACS Appl. Nano Mater., 4(9) (2021) 9322-9332.
[20] N. Liu, K.X. Tang, D.H. Wang, F.H. Fei, H.P. Cui, F. Li, J.Q. Lei, D. Crawshaw, X.D. Zhang, L. Tang, Enhanced photocatalytic CO₂ reduction by integrating an iron based metal-organic framework and a photosensitizer, Sep. Purif. Technol. 332 (2024) 125873.
[21] Q.Y. Shen, Z.H. Lu, F.K. Bi, Y.Y. Fang, L.P. Song, Y. Yang, M.H. Wu, X.D. Zhang, Effect of actual working conditions on catalyst structure and activity for oxidation of volatile organic compounds: a review, Fuel 343 (2023) 128012.
[22] Y.Q. Yang, B.R. Jie, J.Y. Ye, F.Y. Gan, S.L. Yu, H.D. Lin, X.D. Zhang, N-doped catalysts built by iron-based metal-organic framework efficiently activated peroxymonosulfate for the tetracycline degradation, J. Mol. Liq. 392 (2023) 123505.
[23] Y. Wang, H.H. Li, J. Xu, J.Y. Yu, J.F. Wang, H. Jiang, C.Y. Li, X.D. Zhang, N. Liu, High-performance carbon@ metal oxide nanocomposites derived metal-organic framework-perovskite hybrid boosted microwave-induced catalytic degradation of norfloxacin: performance, degradation pathway and mechanism, Sep. Purif. Technol. 330 (2024) 125399.
[24] M.C. Zhou, C.S. Zhou, D. Chen, H. Wu, Z. Zhang, H.M. Yang, W. Ruan, Y.M. Zhou, Z.Q. Tan, Mn decorated UIO-66 catalyst for gaseous toluene removal: synergistic effect of enhanced hydroxyl from H₂O₂, Fuel 309 (2022) 122229.
[25] X.D. Zhang, F.K. Bi, Z.Q. Zhu, Y. Yang, S.H. Zhao, J.F. Chen, X.T. Lv, Y.X. Wang, J.C. Xu, N. Liu, The promoting effect of H₂O on rod-like MnCeO_x derived from MOFs for toluene oxidation: a combined experimental and theoretical investigation, Appl. Catal. B Environ. 297 (2021) 120393.
[26] Y.F. Zheng, Q. Zhao, C.P. Shan, S.C. Lu, Y. Su, R. Han, C.F. Song, N. Ji, D.G. Ma, Q.L. Liu, Enhanced acetone oxidation over the CeO₂/Co₃O₄ catalyst derived from metal-organic frameworks, ACS Appl. Mater. Interfaces 12 (25) (2020) 28139-28147.
[27] X.Y. Gu, C. Huang, Z.C. Xu, H. Wu, R.L. Dong, R. Liu, J. Chen, H.J. Zhu, Core-shell Co-MOF-74@Mn-MOF-74 catalysts with Controllable shell thickness and their enhanced catalytic activity for toluene oxidation, J. Solid State Chem. 294 (2021) 121803.
[28] Y.L. Guo, M.C. Wen, S.N. Song, Q.X. Liu, G.Y. Li, T.C. An, Enhanced catalytic elimination of typical VOCs over ZnCoO_x catalyst derived from in situ pyrolysis of ZnCo bimetallic zeolitic imidazolate frameworks, Appl. Catal. B Environ. 308 (2022) 121212.
[29] Y.X. Li, W. Han, R.X. Wang, L.T. Weng, A. Serrano-Lotina, M.A. Banares, Q.Y. Wang, K.L. Yeung, Performance of an aliovalent-substituted CoCeO_x catalyst from bimetallic MOF for VOC oxidation in air, Appl. Catal. B Environ. 275 (2020) 119121.
[30] Y.J. Luo, Y.B. Zheng, J.C. Zuo, X.S. Feng, X.Y. Wang, T.H. Zhang, K. Zhang, L.L. Jiang, Insights into the high performance of Mn-Co oxides derived from metal-organic frameworks for total toluene oxidation, J. Hazard. Mater. 349 (2018) 119-127.
[31] R.S. Qiu, Y. Kong, W. Wang, Z. Wang, Y.Q. Hao, X.F. Wei, X.W. Qi, L.H. Hui, J. Qi, H.W. Wang, The high activity of Co-Mn-based solid solution catalysts for lean methane combustion, J. Alloys Compd. 952 (2023) 169973.
[32] J.J. Zhang, A. Raza, Y. Zhao, S. Guo, Z.U.D. Babar, L.L. Xu, C.H. Cao, G. Li, Intrinsically robust cubic MnCoO_x solid solution: achieving high activity for sustainable acidic water oxidation, J. Mater. Chem. A 11 (46) (2023) 25345-25355.
[33] F. Sha, S. Tang, C.Z. Tang, Z.D. Feng, J.J. Wang, C. Li, The role of surface hydroxyls on ZnZrO solid solution catalyst in CO₂ hydrogenation to methanol, Chin. J. Catal. 45 (2023) 162-173.
[34] Y.H. Wang, C.Y. Yao, Y.J. Cao, C. Zhang, W.X. Tang, Confined nanoreactor for synthesis of MnCe composite oxide nanowires with enhanced catalytic activity towards aromatic VOCs oxidation, Ceram. Int. 49 (1) (2023) 1137-1147.
[35] B. Wang, X.Y. Lu, C.W. Tsang, Y.H. Wang, W.K. Au, H.F. Guo, Y.Y. Tang, Charge-driven self-assembly synthesis of straw-sheaf-like Co₃O₄ with superior cyclability and rate capability for lithium-ion batteries, Chem. Eng. J. 338 (2018) 278-286.
[36] F.K. Bi, S.T. Ma, B. Gao, B.L. Liu, Y.D. Huang, R. Qiao, X.D. Zhang, Boosting toluene deep oxidation by tuning metal-support interaction in MOF-derived Pd@ZrO₂ catalysts: the role of interfacial interaction between Pd and ZrO₂, Fuel 357 (2024) 129833.
[37] F.K. Bi, X.B. Feng, Z.X. Zhou, Y.F. Zhang, J.F. Wei, L. Yuan, B.L. Liu, Y.D. Huang, X.D. Zhang, Mn-based catalysts derived from the non-thermal treatment of Mn-MIL-100 to enhance its water-resistance for toluene oxidation: mechanism study, Chem. Eng. J. 485 (2024) 149776.
[38] C. Wang, Y. Li, H.A. Liu, Z.Y. Hu, X.H. Hao, H.P. Jia, J. Chen, C.Z. Lu, Constructing a high concentration CuO/CeO₂ interface for complete oxidation of toluene: the fantastic application of spatial confinement strategy, J. Rare Earths 41 (6) (2023) 850-861.
[39] P. Liu, Y.X. Liao, J.J. Li, L.W. Chen, M.L. Fu, P.Q. Wu, R.L. Zhu, X.L. Liang, T.L. Wu, D.Q. Ye, Insight into the effect of manganese substitution on mesoporous hollow spinel cobalt oxides for catalytic oxidation of toluene, J. Colloid Interface Sci. 594 (2021) 713-726.
[40] J.R. Li, W.P. Zhang, C. Li, C. He, Efficient catalytic degradation of toluene at a readily prepared Mn-Cu catalyst: catalytic performance and reaction pathway, J. Colloid Interface Sci. 591 (2021) 396-408.
[41] Y.Z. Zhang, Y.F. Li, Z.Q. Zeng, J.L. Hu, Z.G. Huang, Promotion mechanism of CuMn₂O₄ modification with NaOH on toluene oxidation: boosting the ring-opening of benzoate, Fuel 314 (2022) 122747.
[42] J. Lei, P. Wang, S. Wang, J.P. Li, Y.P. Xu, S.Y. Li, Enhancement effect of Mn doping on Co₃O₄ derived from Co-MOF for toluene catalytic oxidation, Chin. J. Chem. Eng. 52 (2022) 1-9.
[43] Y.F. Zheng, K.X. Fu, Z.H. Yu, Y. Su, R. Han, Q.L. Liu, Oxygen vacancies in a catalyst for VOCs oxidation: synthesis, characterization, and catalytic effects, J. Mater. Chem. A 10 (27) (2022) 14171-14186.
[44] J. Zeng, H.M. Xie, H.Y. Zhang, M. Huang, X.C. Liu, G.L. Zhou, Y. Jiang, Insight into the effects of oxygen vacancy on the toluene oxidation over α-MnO₂ catalyst, Chemosphere 291 (Pt 3) (2022) 132890.
[45] W.H. Yang, Z.A. Su, Z.H. Xu, W.N. Yang, Y. Peng, J.H. Li, Comparative study of α-, β-, γ- and δ-MnO₂ on toluene oxidation: oxygen vacancies and reaction intermediates, Appl. Catal. B Environ. 260 (2020) 118150.
[46] Q. Zhao, Y.F. Zheng, C.F. Song, Q.L. Liu, N. Ji, D.G. Ma, X.B. Lu, Novel monolithic catalysts derived from in situ decoration of Co₃O₄ and hierarchical Co₃O₄@MnO_x on Ni foam for VOC oxidation, Appl. Catal. B Environ. 265 (2020) 118552.
[47] C.P. Shan, Y. Zhang, Q. Zhao, K.X. Fu, Y.F. Zheng, R. Han, C.X. Liu, N. Ji, W.C. Wang, Q.L. Liu, Acid etching-induced in situ growth of λ-MnO₂ over CoMn spinel for low-temperature volatile organic compound oxidation, Environ. Sci. Technol. 56 (14) (2022) 10381-10390.
[48] L.Y. Zhang, Y.J. Liu, X. Fang, Y. Cheng, Regulating oxygen species for promoted deep oxidation of toluene: a comparative study of adsorbed oxygen and lattice oxygen, Fuel 321 (2022) 124116.
[49] M. Piumetti, D. Fino, N. Russo, Mesoporous manganese oxides prepared by solution combustion synthesis as catalysts for the total oxidation of VOCs, Appl. Catal. B Environ. 163 (2015) 277-287.
[50] L. Wang, Y.G. Sun, Y.B. Zhu, J. Zhang, J. Ding, J.D. Gao, W.X. Ji, Y.Y. Li, L.Q. Wang, Y.L. Ma, Revealing the mechanism of high water resistant and excellent active of CuMn oxide catalyst derived from bimetal-organic framework for acetone catalytic oxidation, J. Colloid Interface Sci. 622 (2022) 577-590.
[51] C. Feng, Y.X. Wang, C. Chen, X.Q. Fu, Y. Pan, H.C. Xin, Z. Wang, Y.K. Lu, X.B. Li, R.D. Zhang, Y.Q. Liu, Fabrication of highly dispersed Pd-Mn3O₄ catalyst for efficient catalytic propane total oxidation, J. Colloid Interface Sci. 650 (Pt B) (2023) 1415-1423.
[52] H.L. Zhang, S.M. Wang, M.J. Wang, G.H. Li, L.H. Yu, X.H. Liu, Z. Wang, C.H. Zhang, Catalytic oxidation of vinyl chloride over Co-Ce composite oxides derived from ZIF-67 template: effect of cerium incorporation, J. Rare Earths 41 (6) (2023) 870-880.
[53] Y. Liu, H.H. Yang, H. Zhou, X.L. Yi, J.J. Zhan, Water durability modification of cerium-manganese oxide by tin shell for efficient airborne benzene oxidation, J. Hazard. Mater. 436 (2022) 129207.
[54] R.M. Fang, J. Huang, X.Y. Huang, X.A. Luo, Y.J. Sun, F. Dong, H.B. Huang, Reheat treatment under vacuum induces pre-calcined α-MnO₂ with oxygen vacancy as efficient catalysts for toluene oxidation, Chemosphere 289 (2022) 133081.
[55] J.L. Wang, X.X. Lai, H.L. Zhang, X.Y. Zhou, T. Lin, J.L. Wang, Y.Q. Chen, Low-temperature toluene oxidation on Ag/Ce_xZr_1-xO₂ monolithic catalysts: synergistic catalysis of silver and ceria-zirconia, Combust. Flame 248 (2023) 112577.
[56] X.X. Lai, X.Y. Zhou, H.L. Zhang, X. Jiang, T. Lin, Y.Q. Chen, Toluene oxidation over monolithic MnO_x/La-Al₂O₃ catalyst prepared by a CTAB-assisted impregnation method, Appl. Surf. Sci. 526 (2020) 146714.
[57] Y. Lyu, C.T. Li, X.Y. Du, Y.C. Zhu, Y.D. Zhang, S.H. Li, Catalytic oxidation of toluene over MnO₂ catalysts with different Mn (II) precursors and the study of reaction pathway, Fuel 262 (2020) 116610.
[58] J.F. Yao, F. Dong, X. Xu, M. Wen, Z.Y. Ji, H. Feng, X.L. Wang, Z.C. Tang, Rational design and construction of monolithic ordered mesoporous Co₃O₄@SiO₂ catalyst by a novel 3D printed technology for catalytic oxidation of toluene, ACS Appl. Mater. Interfaces 14 (19) (2022) 22170-22185.
[59] Z.A. Su, W.Z. Si, H. Liu, S.C. Xiong, X.F. Chu, W.H. Yang, Y. Peng, J.J. Chen, X.Z. Cao, J.H. Li, Boosting the catalytic performance of CeO₂ in toluene combustion via the Ce-Ce homogeneous interface, Environ. Sci. Technol. 55 (18) (2021) 12630-12639.
[60] X.B. Feng, L.H. Xia, Z.Y. Jiang, M.J. Tian, S.G. Zhang, C. He, Dramatically promoted toluene destruction over Mn@Na-Al₂O₃@Al monolithic catalysts by Ce incorporation: oxygen vacancy construction and reaction mechanism, Fuel 326 (2022) 125051.

Strong water-resistant Co-Mn solid solution derived from bimetallic metal–organic frameworks for catalytic destruction of toluene

Strong water-resistant Co-Mn solid solution derived from bimetallic metal–organic frameworks for catalytic destruction of toluene

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 14

Recommended Articles

Metrics

Comments

[1]	Baowei Wang, Yi Liao, Tingting Wang. Metal oxide particle electrodes for degradation of high concentration phenol wastewater via electrocatalytic advanced oxidation [J]. Chinese Journal of Chemical Engineering, 2024, 75(11): 204-213.
[2]	Chenyang Zhao, Yinhan Cheng, Guangfei Qu, Yongheng Yuan, Fenghui Wu, Ye Liu, Shan Liu, Junyan Li, Ping Ning. High-performance liquid-phase catalytic purification of phosphine in tail gas using Pd(II)/Cu(II) composite [J]. Chinese Journal of Chemical Engineering, 2023, 57(5): 98-108.
[3]	Peiyin Chen, Yanxiong Fang, Kaihong Xie, Yao Chen, Yang Liu, Hongliang Zuo, Weijian Lu, Baoyu Liu. Lacunary silicotungstic heteropoly salts as high-performance catalysts in oxidation of cyclopentene [J]. Chinese Journal of Chemical Engineering, 2023, 56(4): 152-159.
[4]	Fengrong Li, Xuezhen Liu, ZhengYi Zhao, Xia An, Yali Du, Xu Wu. Fabrication of highly dispersed carbon doped Cu-based oxides as superior selective catalytic oxidation of ammonia catalysts via employing citric acid-modified carbon nanotubes doping CuAl-LDHs [J]. Chinese Journal of Chemical Engineering, 2023, 63(11): 185-196.
[5]	Juan Lei, Peng Wang, Shuang Wang, Jinping Li, Yongping Xu, Shuying Li. Enhancement effect of Mn doping on Co₃O₄ derived from Co-MOF for toluene catalytic oxidation [J]. Chinese Journal of Chemical Engineering, 2022, 52(12): 1-9.
[6]	Zhen Wei, Xuanqi Kang, Shangyuan Xu, Xiaokang Zhou, Bo Jia, Qing Feng. Electrochemical oxidation of Rhodamine B with cerium and sodium dodecyl benzene sulfonate co-modified Ti/PbO₂ electrodes: Preparation, characterization, optimization, application [J]. Chinese Journal of Chemical Engineering, 2021, 32(4): 191-202.
[7]	Zhihao Yi, Jie Sun, Jigang Li, Tian Zhou, Shouping Wei, Hongjia Xie, Yulin Yang. High efficient removal of HCN over porous CuO/CeO₂ micro-nano spheres at lower temperature range [J]. Chinese Journal of Chemical Engineering, 2021, 38(10): 155-164.
[8]	Mohammad Hossein Sheikh-Mohseni, Sajjad Sedaghat, Pirouz Derakhshi, Aliakbar Safekordi. Green bio-synthesis of Ni/montmorillonite nanocomposite using extract of Allium jesdianum as the nano-catalyst for electrocatalytic oxidation of methanol [J]. Chinese Journal of Chemical Engineering, 2020, 28(10): 2555-2565.
[9]	Pengyu Zhu, Kaijin Zhu, Rob Puzey, Xiaoli Ren. Degradation analysis of A²/O combined with AgNO₃ + K₂FeO₄ on coking wastewater [J]. Chin.J.Chem.Eng., 2018, 26(7): 1555-1560.
[10]	Vasu Chaudhary, Sweta. Synthesis and catalytic activity of SBA-15 supported catalysts for styrene oxidation [J]. Chin.J.Chem.Eng., 2018, 26(6): 1300-1306.
[11]	SHE Yuanbin, WANG Weijie, LI Guojun. Oxidation of p/o-Cresols to p/o-Hydroxybenzaldehydes Catalyzed by Metalloporphyrins with Molecular Oxygen [J]. Chin.J.Chem.Eng., 2012, 20(2): 262-266.
[12]	TIAN Wenyu, XUE Weilan, ZENG Zuoxiang, SHAO Ji. Kinetics of 2-Methyl-6-acetyl-naphthalene Liquid Phase Catalytic Oxidation [J]. , 2009, 17(1): 72-77.
[13]	ZHANG Yukun, LI Chufu, HE Xiaorong, CHEN Bingzhen. Simulation and Optimization in the Process of Toluene Liquid-phase Catalytic Oxidation [J]. Chin.J.Chem.Eng., 2008, 16(1): 36-38.
[14]	LIU Pingle, ZOU Lishan, LUO He'an, WANG Liangjie, ZHENG Jinhua. Estimation of Kinetic Parameters for Autocatalytic Oxidation of Cyclohexane Based on a Modified Adaptive Genetic Algorithm [J]. , 2004, 12(1): 49-54.