Ag-Co3O4: Synthesis, characterization and evaluation of its photocatalytic activity towards degradation of rhodamine B dye in aqueous medium

Muhammad Saeed1, Majid Muneer1, Nida Mumtaz1, Mohsin Siddique2, Nadia Akram1, Muhammad Hamayun3   

  1. 1 Department of Chemistry, Government College University Faisalabad, Pakistan;
    2 Department of Chemistry, Bacha Khan University Charsadda, Pakistan;
    3 Department of Chemistry, University of Gujrat, Hafiz Hayat Campus Gujrat, Pakistan
  • 收稿日期:2017-08-07 修回日期:2018-02-07 出版日期:2018-06-28 发布日期:2018-08-03
  • 通讯作者: Muhammad Saeed,E-mail address:msaeed@gcuf.edu.pk

Ag-Co3O4: Synthesis, characterization and evaluation of its photocatalytic activity towards degradation of rhodamine B dye in aqueous medium

Muhammad Saeed1, Majid Muneer1, Nida Mumtaz1, Mohsin Siddique2, Nadia Akram1, Muhammad Hamayun3   

  1. 1 Department of Chemistry, Government College University Faisalabad, Pakistan;
    2 Department of Chemistry, Bacha Khan University Charsadda, Pakistan;
    3 Department of Chemistry, University of Gujrat, Hafiz Hayat Campus Gujrat, Pakistan
  • Received:2017-08-07 Revised:2018-02-07 Online:2018-06-28 Published:2018-08-03
  • Contact: Muhammad Saeed,E-mail address:msaeed@gcuf.edu.pk

摘要: Synthesis, characterization of Co3O4 and Ag-Co3O4 composites and evaluation of their photo-catalytic activities towards photo-degradation of aqueous solution of rhodamine B dye under irradiation of visible light have been described in this paper. Co3O4 was prepared by solid phase mechano chemical process using Co(NO3)2·6H2O and NH4HCO3 as precursor materials. Ag was deposited on Co3O4 from AgNO3 using Calotropis gigantea extract as reducing agent. XRD, SEM and FTIR were used for characterization of prepared composites. Photo-catalytic efficiencies of as-prepared Co3O4 and Ag-Co3O4 were evaluated for aqueous phase photo-degradation of rhodamine B. It was found that deposition of Ag on Co3O4 highly enhanced the photo-catalytic activity of Co3O4. Photo-catalytic degradation followed the Eley-Rideal mechanism. About 100% and 91% photo-degradation of 40 ml dye solution achieved at 313 K in 90 and 120 min over 0.05 g of Ag-Co3O4 as photo-catalyst using 100 and 200 mg·L-1 as initial concentration of dye respectively.

关键词: Co3O4, Ag-Co3O4, Photo-catalysis, Photo-degradation, Calotropis gigantea, Rhodamine B, Elay-Rideal mechanism

Abstract: Synthesis, characterization of Co3O4 and Ag-Co3O4 composites and evaluation of their photo-catalytic activities towards photo-degradation of aqueous solution of rhodamine B dye under irradiation of visible light have been described in this paper. Co3O4 was prepared by solid phase mechano chemical process using Co(NO3)2·6H2O and NH4HCO3 as precursor materials. Ag was deposited on Co3O4 from AgNO3 using Calotropis gigantea extract as reducing agent. XRD, SEM and FTIR were used for characterization of prepared composites. Photo-catalytic efficiencies of as-prepared Co3O4 and Ag-Co3O4 were evaluated for aqueous phase photo-degradation of rhodamine B. It was found that deposition of Ag on Co3O4 highly enhanced the photo-catalytic activity of Co3O4. Photo-catalytic degradation followed the Eley-Rideal mechanism. About 100% and 91% photo-degradation of 40 ml dye solution achieved at 313 K in 90 and 120 min over 0.05 g of Ag-Co3O4 as photo-catalyst using 100 and 200 mg·L-1 as initial concentration of dye respectively.

Key words: Co3O4, Ag-Co3O4, Photo-catalysis, Photo-degradation, Calotropis gigantea, Rhodamine B, Elay-Rideal mechanism