Direct synthesis of single-phase α-CaSO4·0.5H2O whiskers from waste nitrate solution

doi:10.1016/j.cjche.2020.04.005

中国化学工程学报 ›› 2020, Vol. 28 ›› Issue (6): 1752-1754.DOI: 10.1016/j.cjche.2020.04.005

• Communications • 上一篇

Direct synthesis of single-phase α-CaSO₄·0.5H₂O whiskers from waste nitrate solution

Shuang Shao^1,2, Baozhong Ma^1,2,3, Yongqiang Chen^1,2, Wenjuan Zhang^1,2, Bao Liu^1,2, Peng Xing^1,2, Chengyan Wang^1,2

1 State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China;
2 School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China;
3 Department of Materials Engineering, The University of British Columbia, Vancouver, BC V6T 1Z4, Canada

收稿日期:2020-02-29 修回日期:2020-04-02 出版日期:2020-06-28 发布日期:2020-07-29
通讯作者: Baozhong Ma, Chengyan Wang
基金资助:
This work was supported by the Beijing Natural Science Foundation of China (2182040), the National Natural Science Foundation of China (51674026, U1802253), the Fundamental Research Funds for the Central Universities (FRF-TT-19-001), and the China Scholarship Council (201906465004).

Direct synthesis of single-phase α-CaSO₄·0.5H₂O whiskers from waste nitrate solution

Shuang Shao^1,2, Baozhong Ma^1,2,3, Yongqiang Chen^1,2, Wenjuan Zhang^1,2, Bao Liu^1,2, Peng Xing^1,2, Chengyan Wang^1,2

1 State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China;
2 School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China;
3 Department of Materials Engineering, The University of British Columbia, Vancouver, BC V6T 1Z4, Canada

Received:2020-02-29 Revised:2020-04-02 Online:2020-06-28 Published:2020-07-29
Contact: Baozhong Ma, Chengyan Wang
Supported by:
This work was supported by the Beijing Natural Science Foundation of China (2182040), the National Natural Science Foundation of China (51674026, U1802253), the Fundamental Research Funds for the Central Universities (FRF-TT-19-001), and the China Scholarship Council (201906465004).

摘要/Abstract

摘要： Single-phase α-CaSO₄·0.5H₂O whiskers were directly synthesized from waste Ca(NO₃)₂ solution using a hydrothermal method, and HNO₃ was synchronously regenerated. The effects of reaction temperature and Ca²⁺ concentration on the phase composition and morphology of products were determined by X-ray diffraction and optical microscopy. On the basis of the experimental results, the formation diagram of α-CaSO₄·0.5H₂O was plotted within the range of 5-35 g·L^-1 Ca²⁺ and 115℃-150℃. In addition, the conditions of the direct synthesis of α-CaSO₄·0.5H₂O were determined. Well-crystallized, single-phase α-CaSO₄·0.5H₂O whiskers with high aspect ratios (length, 1785 μm; diameter, 10.63 μm; aspect ratio, 168) and HNO₃ (70.25 g·L^-1) were obtained at the optimal conditions of 25 g·L^-1 Ca²⁺ and 125℃.

关键词: α-CaSO₄·0.5H₂O whiskers, Direct synthesis, Formation diagram, Waste Ca(NO₃)₂ solution, HNO₃ regeneration

Abstract: Single-phase α-CaSO₄·0.5H₂O whiskers were directly synthesized from waste Ca(NO₃)₂ solution using a hydrothermal method, and HNO₃ was synchronously regenerated. The effects of reaction temperature and Ca²⁺ concentration on the phase composition and morphology of products were determined by X-ray diffraction and optical microscopy. On the basis of the experimental results, the formation diagram of α-CaSO₄·0.5H₂O was plotted within the range of 5-35 g·L^-1 Ca²⁺ and 115℃-150℃. In addition, the conditions of the direct synthesis of α-CaSO₄·0.5H₂O were determined. Well-crystallized, single-phase α-CaSO₄·0.5H₂O whiskers with high aspect ratios (length, 1785 μm; diameter, 10.63 μm; aspect ratio, 168) and HNO₃ (70.25 g·L^-1) were obtained at the optimal conditions of 25 g·L^-1 Ca²⁺ and 125℃.

Key words: α-CaSO₄·0.5H₂O whiskers, Direct synthesis, Formation diagram, Waste Ca(NO₃)₂ solution, HNO₃ regeneration

Shuang Shao, Baozhong Ma, Yongqiang Chen, Wenjuan Zhang, Bao Liu, Peng Xing, Chengyan Wang. Direct synthesis of single-phase α-CaSO₄·0.5H₂O whiskers from waste nitrate solution[J]. 中国化学工程学报, 2020, 28(6): 1752-1754.

参考文献

[1] D. Freyer, W. Voigt, Crystallization and phase stability of CaSO₄ and CaSO₄-based salts, Monatsh. Chem. 134(2003) 693-719.
[2] Y. Qi, C. Zeng, C. Wang, X. Ke, L. Zhang, Continuous fabrication of calcium sulfate whiskers with adjustable aspect ratio in microdroplets, Mater. Lett. 194(2017) 231-233.
[3] T. Feldmann, G.P. Demopoulos, The crystal growth kinetics of alpha calcium sulfate hemihydrate in concentrated CaCl₂-HCl solutions, J. Cryst. Growth 351(2012) 9-18.
[4] W. Teng, J. Wang, J. Wu, Y. Du, X.J. Jia, H. Li, T. Wang, Rapid synthesis of alpha calcium sulfate hemihydrate whiskers in glycerol-water solution by using flue-gasdesulfurization gypsum solid waste, J. Cryst. Growth 496(2018) 24-30.
[5] A.J. Lewry, J. Williamson, The setting of gypsum plaster. Part II:The development of microstructure and strength, J. Mater. Sci. 29(1994) 5524-5528.
[6] M.V. Thomas, D.A. Puleo, Calcium sulfate:Properties and clinical applications, J. Biomed. Mater. Res. B. 88(2009) 597-610.
[7] M. Miao, X. Feng, G. Wang, S. Cao, W. Shi, L. Shi, Direct transformation of FGD gypsum to calcium sulfate hemihydrate whiskers:Preparation, simulations, and process analysis, Particuology 19(2015) 53-59.
[8] S. Hou, J. Wang, X. Wang, H. Chen, L. Xiang, Effect of Mg²⁺ on hydrothermal formation of α-CaSO₄·0.5H₂O whiskers with high aspect ratios, Langmuir 30(2014) 9804-9810.
[9] Y. Xin, S.C. Hou, L. Xiang, Y.X. Yu, Adsorption and substitution effects of Mg on the growth of calcium sulfate hemihydrate:An ab initio DFT study, Appl. Surf. Sci. 357(2015) 1552-1557.
[10] B. Ma, C. Wang, W. Yang, B. Yang, Y. Zhang, Selective pressure leaching of Fe (II)-rich limonitic laterite ores from Indonesia using nitric acid, Miner. Eng. 45(2013) 151-158.
[11] B. Ma, W. Yang, B. Yang, C. Wang, Y. Chen, Y. Zhang, Pilot-scale plant study on the innovative nitric acid pressure leaching technology for laterite ores, Hydrometallurgy 155(2015) 88-94.
[12] K. Yoo, K. Lee, M.K. Jha, J.C. Lee, K. Cho, Preparation of nano-sized tin oxide powder from waste Pb-free solder by direct nitric acid leaching, J. Nanosci. Nanotechno. 16(2016) 11238-11241.
[13] B. Ma, P. Xing, C. Wang, Y. Chen, S. Shao, A novel way to synthesize calcium sulfate whiskers with high aspect ratios from concentrated calcium nitrate solution, Mater. Lett. 219(2018) 1-3.
[14] K. Luo, C. Li, L. Xiang, H. Li, P. Ning, Influence of temperature and solution composition on the formation of calcium sulfates, Particuology 8(2010) 240-244.

Direct synthesis of single-phase α-CaSO₄·0.5H₂O whiskers from waste nitrate solution

Direct synthesis of single-phase α-CaSO₄·0.5H₂O whiskers from waste nitrate solution

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 4

编辑推荐

Metrics

本文评价

[1]	Jia Ren, Feng Xin, Yongsheng Xu. A review on direct synthesis of dimethoxymethane[J]. 中国化学工程学报, 2022, 50(10): 43-55.
[2]	Zihao Yao, Jinyan Zhao, Chenxia Zhao, Shengwei Deng, Guilin Zhuang, Xing Zhong, Zhongzhe Wei, Yang Li, Shibin Wang, Jianguo Wang. A first-principles study of reaction mechanism over carbon decorated oxygen-deficient TiO₂ supported Pd catalyst in direct synthesis of H₂O₂[J]. 中国化学工程学报, 2021, 29(3): 126-134.
[3]	Guozhu Liu, Hairui Liang, Yajie Tian, Bofeng Zhang, Li Wang. Direct synthesis of hydrogen peroxide over Pd nanoparticles embedded between HZSM-5 nanosheets layers[J]. 中国化学工程学报, 2020, 28(10): 2577-2586.
[4]	汪超, 王光润, 王金福. A Bi-component Cu Catalyst for the Direct Synthesis of Methylchlorosilane from Silicon and Methyl Chloride[J]. Chinese Journal of Chemical Engineering, 2014, 22(3): 299-304.