Mechanical strength and the degradation mechanism of metakaolin based geopolymer mixed with ordinary Portland cement and cured at high temperature and high relative humidity

doi:10.1016/j.cjche.2023.02.006

中国化学工程学报 ›› 2023, Vol. 60 ›› Issue (8): 118-130.DOI: 10.1016/j.cjche.2023.02.006

• Full Length Article • 上一篇下一篇

Mechanical strength and the degradation mechanism of metakaolin based geopolymer mixed with ordinary Portland cement and cured at high temperature and high relative humidity

Xia Miao^1,2, Xiaofan Pang³, Shiyu Li³, Haoguang Wei^1,2, Jianhao Yin³, Xiangming Kong³

1. State Key Laboratory of Shale Oil and Gas Enrichment Mechanisms and Effective Development, Beijing 100101, China;
2. Sinopec Research Institute of Petroleum Engineering Co., Ltd, Beijing 100101, China;
3. Department of Civil Engineering, Tsinghua University, Beijing 100084, China

收稿日期:2022-09-14 修回日期:2023-02-01 出版日期:2023-08-28 发布日期:2023-10-28
通讯作者: Xiaofan Pang,E-mail:pangxiaofan@tsinghua.edu.cn;Xiangming Kong,E-mail:kxm@tsinghua.edu.cn
基金资助:
This work is supported by the State Key Laboratory of Shale Oil and Gas Enrichment Mechanisms and Effective Development (20-YYGZ-KF-GC-04).

Mechanical strength and the degradation mechanism of metakaolin based geopolymer mixed with ordinary Portland cement and cured at high temperature and high relative humidity

Xia Miao^1,2, Xiaofan Pang³, Shiyu Li³, Haoguang Wei^1,2, Jianhao Yin³, Xiangming Kong³

1. State Key Laboratory of Shale Oil and Gas Enrichment Mechanisms and Effective Development, Beijing 100101, China;
2. Sinopec Research Institute of Petroleum Engineering Co., Ltd, Beijing 100101, China;
3. Department of Civil Engineering, Tsinghua University, Beijing 100084, China

Received:2022-09-14 Revised:2023-02-01 Online:2023-08-28 Published:2023-10-28
Contact: Xiaofan Pang,E-mail:pangxiaofan@tsinghua.edu.cn;Xiangming Kong,E-mail:kxm@tsinghua.edu.cn
Supported by:
This work is supported by the State Key Laboratory of Shale Oil and Gas Enrichment Mechanisms and Effective Development (20-YYGZ-KF-GC-04).

摘要/Abstract

摘要： Geopolymer is a new type of eco-friendly cementitious material, and its superior drying and high temperature resistance has been widely recognized. The service performance of geopolymer under 150 ℃ high-temperature hydrothermal conditions is still less discussed. In this paper, the mechanical strength of pure metakaolin system with low calcium content and metakaolin-cement system with high calcium content under hydrothermal and non-hydrothermal conditions were studied. The results show that under 150 ℃ hydrothermal conditions, the strength of pure metakaolin geopolymer sharply decreases by reduction rate of 81.8% compared to the sample under 150 ℃ drying conditions, while the strength of metakaolin-cement geopolymers is well retained with only a slight decrease of 14.4%. This is mainly because the predominantly hydration product sodium aluminosilicate (N-A-S-H) gel of pure metakaolin system undergoes the process of “dissociation-repolymerization-crystallization” under 150 ℃ hydrothermal conditions, resulting in the loss of cementation ability and obvious deterioration of mechanical strength. In the metakaolin-cement system, the high-calcium calcium silicate gel (C-A-S-H) gel maintains a stable structure, thereby maintaining the macroscopic strength of the material under the hydrothermal conditions.

关键词: Geopolymer, Hydrothermal conditions, Strength, Degradation, Crystallization, Gels

Abstract: Geopolymer is a new type of eco-friendly cementitious material, and its superior drying and high temperature resistance has been widely recognized. The service performance of geopolymer under 150 ℃ high-temperature hydrothermal conditions is still less discussed. In this paper, the mechanical strength of pure metakaolin system with low calcium content and metakaolin-cement system with high calcium content under hydrothermal and non-hydrothermal conditions were studied. The results show that under 150 ℃ hydrothermal conditions, the strength of pure metakaolin geopolymer sharply decreases by reduction rate of 81.8% compared to the sample under 150 ℃ drying conditions, while the strength of metakaolin-cement geopolymers is well retained with only a slight decrease of 14.4%. This is mainly because the predominantly hydration product sodium aluminosilicate (N-A-S-H) gel of pure metakaolin system undergoes the process of “dissociation-repolymerization-crystallization” under 150 ℃ hydrothermal conditions, resulting in the loss of cementation ability and obvious deterioration of mechanical strength. In the metakaolin-cement system, the high-calcium calcium silicate gel (C-A-S-H) gel maintains a stable structure, thereby maintaining the macroscopic strength of the material under the hydrothermal conditions.

Key words: Geopolymer, Hydrothermal conditions, Strength, Degradation, Crystallization, Gels

Xia Miao, Xiaofan Pang, Shiyu Li, Haoguang Wei, Jianhao Yin, Xiangming Kong. Mechanical strength and the degradation mechanism of metakaolin based geopolymer mixed with ordinary Portland cement and cured at high temperature and high relative humidity[J]. 中国化学工程学报, 2023, 60(8): 118-130.

参考文献

[1] J. Davidovits, Geopolymer Chemistry And Applications, 5th edition, Geopolymer Institute, Saint Quentin, 2020.
[2] H. Xu, J.S.J. van Deventer, The geopolymerisation of alumino-silicate minerals, Int. J. Miner. Process. 59 (3) (2000) 247-266.
[3] D.L.Y. Kong, J.G. Sanjayan, Effect of elevated temperatures on geopolymer paste, mortar and concrete, Cem. Concr. Res. 40 (2) (2010) 334-339.
[4] F. Farooq, X. Jin, M. Faisal Javed, A. Akbar, M. Izhar Shah, F. Aslam, R. Alyousef, Geopolymer concrete as sustainable material: A state of the art review, Constr. Build. Mater. 306 (2021) 124762.
[5] T.A. Aiken, J. Kwasny, W. Sha, M.N. Soutsos, Effect of slag content and activator dosage on the resistance of fly ash geopolymer binders to sulfuric acid attack, Cem. Concr. Res. 111 (2018) 23-40.
[6] D.M. Ren, C.J. Yan, P. Duan, Z.H. Zhang, L.Y. Li, Z.Y. Yan, Durability performances of wollastonite, tremolite and basalt fiber-reinforced metakaolin geopolymer composites under sulfate and chloride attack, Constr. Build. Mater. 134 (2017) 56-66.
[7] P. Duxson, J.L. Provis, G.C. Lukey, J.S.J. van Deventer, The role of inorganic polymer technology in the development of ‘green concrete’, Cem. Concr. Res. 37 (12) (2007) 1590-1597.
[8] N B Singh, S K Saxena, M. Kumar, Effect of nanomaterials on the properties of geopolymer mortars and concrete, Mater. Today Proc. 5 (3) (2018) 9035-9040.
[9] S. Adjei, S. Elkatatny, W.N. Aggrey, Y. Abdelraouf, Geopolymer as the future oil-well cement: A review, J. Petroleum Sci. Eng. 208 (2022) 109485.
[10] Y. Yan, Z.C. Guan, W.J. Yan, H.T. Wang, Mechanical response and damage mechanism of cement sheath during perforation in oil and gas well, J. Petroleum Sci. Eng. 188 (2020) 106924.
[11] S. Salehi, M.J. Khattak, A.H. Bwala, F.K. S, Characterization, morphology and shear bond strength analysis of geopolymers: Implications for oil and gas well cementing applications, J. Nat. Gas Sci. Eng. 38 (2017) 323-332.
[12] N.M. Faqir, S. Elkatatny, M. Mahmoud, R. Shawabkeh, Fabrication of kaolin-based cement plug for CO₂ storage wells, Appl. Clay Sci. 141 (2017) 81-87.
[13] F.N. Okoye, S. Prakash, N.B. Singh, Durability of fly ash based geopolymer concrete in the presence of silica fume, J. Clean. Prod. 149 (2017) 1062-1067.
[14] P. Sajan, T.Y. Jiang, C. Lau, G. Tan, K. Ng, Combined effect of curing temperature, curing period and alkaline concentration on the mechanical properties of fly ash-based geopolymer, Clean. Mater. 1 (2021) 100002.
[15] T. Luukkonen, Z. Abdollahnejad, J. Yliniemi, P. Kinnunen, M. Illikainen, One-part alkali-activated materials: A review, Cem. Concr. Res. 103 (2018) 21-34.
[16] N. Chuewangkam, P. Payakaniti, P. Chindaprasirt, S. Pinitsoontorn, Ohmic heating as an effective path to rapidly cure and strengthen alkali activated material, Constr. Build. Mater. 322 (2022) 126425.
[17] S. Samantasinghar, S. Singh, Effects of curing environment on strength and microstructure of alkali-activated fly ash-slag binder, Constr. Build. Mater. 235 (2020) 117481.
[18] S. Salehi, J. Khattak, F.K. Saleh, S. Igbojekwe, Investigation of mix design and properties of geopolymers for application as wellbore cement, J. Petroleum Sci. Eng. 178 (2019) 133-139.
[19] B.H. Mo, H. Zhu, X.M. Cui, Y. He, S.Y. Gong, Effect of curing temperature on geopolymerization of metakaolin-based geopolymers, Appl. Clay Sci. 99 (2014) 144-148.
[20] L. Yun Ming, K. Hussin, M.M. Al Bakri Abdullah, M. Binhussain, L. Musa, I. Khairul Nizar, C.M.R. Ghazali, C.Y. Heah, Effect of curing regimes on metakaolin geopolymer pastes produced from geopolymer powder, Adv. Mater. Res. 626 (2012) 931-936.
[21] J.K. Yuan, P.G. He, D.C. Jia, C. Yang, Y. zhang, S. Yan, Z.H. Yang, X.M. Duan, S.J. Wang, Y. Zhou, Effect of curing temperature and SiO₂/K₂O molar ratio on the performance of metakaolin-based geopolymers, Ceram. Int. 42 (14) (2016) 16184-16190.
[22] M.X. Peng, Z.H. Wang, Q.G. Xiao, F. Song, W. Xie, L.C. Yu, H.W. Huang, S.J. Yi, Effects of alkali on one-part alkali-activated cement synthesized by calcining bentonite with dolomite and Na₂CO₃, Appl. Clay Sci. 139 (2017) 64-71.
[23] R.R. Suppiah, S.H.A. Rahman, N. Shafiq, S. Irawan, Uniaxial compressive strength of geopolymer cement for oil well cement, J. Petrol. Explor. Prod. Technol. 10 (1) (2020) 67-70.
[24] N. Poornima, D. Katyal, T. Revathi, M. Sivasakthi, R. Jeyalakshmi, Effect of curing on mechanical strength and microstructure of fly ash blend GGBS geopolymer, Portland cement mortar and its behavior at elevated temperature, Mater. Today Proc. 47 (2021) 863-870.
[25] H.Y. Zhang, V. Kodur, B. Wu, L. Cao, F. Wang, Thermal behavior and mechanical properties of geopolymer mortar after exposure to elevated temperatures, Constr. Build. Mater. 109 (2016) 17-24.
[26] A. Nazari, A. Bagheri, J.G. Sanjayan, M. Dao, C. Mallawa, P. Zannis, S. Zumbo, Thermal shock reactions of Ordinary Portland cement and geopolymer concrete: Microstructural and mechanical investigation, Constr. Build. Mater. 196 (2019) 492-498.
[27] P. Sturm, G.J.G. Gluth, S. Simon, H.J.H. Brouwers, H.C. Kühne, The effect of heat treatment on the mechanical and structural properties of one-part geopolymer-zeolite composites, Thermochimica Acta 635 (2016) 41-58.
[28] D. Koloušek, J. Brus, M. Urbanova, J. Andertova, V. Hulinsky, J. Vorel, Preparation, structure and hydrothermal stability of alternative (sodium silicate-free) geopolymers, J. Mater. Sci. 42 (22) (2007) 9267-9275.
[29] Y. Liu, C.J. Yan, X.M. Qiu, D. Li, H.Q. Wang, A. Alshameri, Preparation of faujasite block from fly ash-based geopolymer via in-situ hydrothermal method, J. Taiwan Inst. Chem. Eng. 59 (2016) 433-439.
[30] H.R. Khalid, N.K. Lee, S.M. Park, N. Abbas, H.K. Lee, Synthesis of geopolymer-supported zeolites via robust one-step method and their adsorption potential, J. Hazard. Mater. 353 (2018) 522-533.
[31] N.K. Lee, H.R. Khalid, H.K. Lee, Synthesis of mesoporous geopolymers containing zeolite phases by a hydrothermal treatment, Microporous Mesoporous Mater. 229 (2016) 22-30.
[32] P.G. He, M.R. Wang, S. Fu, D.C. Jia, S. Yan, J.K. Yuan, J.H. Xu, P.F. Wang, Y. Zhou, Effects of Si/Al ratio on the structure and properties of metakaolin based geopolymer, Ceram. Int. 42 (13) (2016) 14416-14422.
[33] Q. Wan, F. Rao, S.X. Song, R.E. García, R.M. Estrella, C.L. Patiño, Y.M. Zhang, Geopolymerization reaction, microstructure and simulation of metakaolin-based geopolymers at extended Si/Al ratios, Cem. Concr. Compos. 79 (2017) 45-52.
[34] Y.S. Zhang, W. Sun, Z.J. Li, Composition design and microstructural characterization of calcined kaolin-based geopolymer cement, Appl. Clay Sci. 47 (3-4) (2010) 271-275.
[35] Z. Zuhua, Y. Xiao, Z. Huajun, C. Yue, Role of water in the synthesis of calcined kaolin-based geopolymer, Appl. Clay Sci. 43 (2) (2009) 218-223.
[36] M. Lizcano, A. Gonzalez, S. Basu, K. Lozano, M. Radovic, Effects of water content and chemical composition on structural properties of alkaline activated metakaolin-based geopolymers, J. Am. Ceram. Soc. 95 (7) (2012) 2169-2177.
[37] P. De Silva, K. Sagoe-Crenstil, V. Sirivivatnanon, Kinetics of geopolymerization: role of Al₂O₃ and SiO₂, Cem. Concr. Res. 37 (4) (2007) 512-518.
[38] P. Duxson, J.L. Provis, G.C. Lukey, S.W. Mallicoat, W.M. Kriven, J.S.J. van Deventer, Understanding the relationship between geopolymer composition, microstructure and mechanical properties, Colloids Surf. A Physicochem. Eng. Aspects 269 (1-3) (2005) 47-58.
[39] Y. Cui, D.M. Wang, Y.R. Wang, R. Sun, Y.F. Rui, Effects of the n(H₂O: Na₂Oeq) ratio on the geopolymerization process and microstructures of fly ash-based geopolymers, J. Non Cryst. Solids 511 (2019) 19-28.
[40] GB/T 17671-2021, Test method of cement mortar strength (ISO method), China Building Material Council, Beijing, 2021. (in Chinese).
[41] H.W. Tian, X.M. Kong, T. Su, D.M. Wang, Comparative study of two PCE superplasticizers with varied charge density in Portland cement and sulfoaluminate cement systems, Cem. Concr. Res. 115 (2019) 43-58.
[42] A.V. Kirschner, H. Harmuth, Investigation of geopolymer binders with respect to their application for building materials, Ceram. Silikaty 48 (3) (2004) 117-120.
[43] I. Ozer, S. Soyer-Uzun, Relations between the structural characteristics and compressive strength in metakaolin based geopolymers with different molar Si/Al ratios, Ceram. Int. 41 (8) (2015) 10192-10198.
[44] Z.M. Li, S.Z. Zhang, Y.B. Zuo, W. Chen, G. Ye, Chemical deformation of metakaolin based geopolymer, Cem. Concr. Res. 120 (2019) 108-118.
[45] Z. Zheng, X. Ma, Z.H. Zhang, Y.X. Li, In-situ transition of amorphous gels to Na-P1 zeolite in geopolymer: Mechanical and adsorption properties, Constr. Build. Mater. 202 (2019) 851-860.
[46] R. Sánchez-Hernández, I. Padilla, S. López-Andrés, A. López-Delgado, Eco-friendly bench-scale zeolitization of an Al-containing waste into gismondine-type zeolite under effluent recycling, J. Clean. Prod. 161 (2017) 792-802.
[47] Y. Liu, C.J. Yan, J.J. Zhao, Z.H. Zhang, H.Q. Wang, S. Zhou, L.M. Wu, Synthesis of zeolite P1 from fly ash under solvent-free conditions for ammonium removal from water, J. Clean. Prod. 202 (2018) 11-22.
[48] W.Z. Liu, T. Aldahri, S. Ren, C.C. Xu, S. Rohani, B. Liang, C. Li, Solvent-free synthesis of hydroxycancrinite zeolite microspheres during the carbonation process of blast furnace slag, J. Alloys Compd. 847 (2020) 156456.
[49] L.M. Huang, Z.H. Yang, Hydration kinetics of tricalcium silicate with the presence of portlandite and calcium silicate hydrate, Thermochimica Acta 681 (2019) 178398.
[50] S. Grangeon, F. Claret, C. Lerouge, F. Warmont, T. Sato, S. Anraku, C. Numako, Y. Linard, B. Lanson, On the nature of structural disorder in calcium silicate hydrates with a calcium/silicon ratio similar to tobermorite, Cem. Concr. Res. 52 (2013) 31-37.
[51] E. L'Hôpital, B. Lothenbach, K. Scrivener, D.A. Kulik, Alkali uptake in calcium alumina silicate hydrate (C-A-S-H), Cem. Concr. Res. 85 (2016) 122-136.
[52] I. Garcia-Lodeiro, A. Palomo, A. Fernández-Jiménez, D.E. MacPhee, Compatibility studies between N-A-S-H and C-A-S-H gels. Study in the ternary diagram Na₂O-CaO-Al₂O₃-SiO₂-H₂O, Cem. Concr. Res. 41 (9) (2011) 923-931.
[53] B. Walkley, R. San Nicolas, M.A. Sani, G.J. Rees, J.V. Hanna, J.S.J. van Deventer, J.L. Provis, Phase evolution of C-(N)-A-S-H/N-A-S-H gel blends investigated via alkali-activation of synthetic calcium aluminosilicate precursors, Cem. Concr. Res. 89 (2016) 120-135.
[54] D.B. Istuque, L. Reig, J.C.B. Moraes, J.L. Akasaki, M.V. Borrachero, L. Soriano, J. Payá, J.A. Malmonge, M.M. Tashima, Behaviour of metakaolin-based geopolymers incorporating sewage sludge ash (SSA), Mater. Lett. 180 (2016) 192-195.
[55] P. De Silva, K. Sagoe-Crenstil, Medium-term phase stability of Na₂O-Al₂O₃-SiO₂-H₂O geopolymer systems, Cem. Concr. Res. 38 (6) (2008) 870-876.
[56] T. da Silva Rocha, D.P. Dias, F.C.C. França, R.R. de Salles Guerra, L.R. da Costa de Oliveira Marques, Metakaolin-based geopolymer mortars with different alkaline activators (Na+ and K+), Constr. Build. Mater. 178 (2018) 453-461.
[57] P. Rożek, M. Król, W. Mozgawa, Geopolymer-zeolite composites: A review, J. Clean. Prod. 230 (2019) 557-579.
[58] Z.H. Liu, Q. Tang, C.M. Li, Y. He, X.M.Cui, Preparation of NaA zeolite spheres from geopolymer gels using a one-step method in silicone oil, Int. J. Appl. Ceram. Technol. 14 (5) (2017) 982-986.
[59] S.K. Lee, J.F.Stebbins, The degree of aluminum avoidance in aluminosilicate glasses, Am. Mineral. 84 (5-6) (1999) 937-945.
[60] P. Duxson, J.L. Provis, G.C. Lukey, F. Separovic, J.S. van Deventer, 29Si NMR study of structural ordering in aluminosilicate geopolymer gels, Langmuir 21 (7) (2005) 3028-3036.
[61] B. Walkley, J.L. Provis, Solid-state nuclear magnetic resonance spectroscopy of cements, Mater. Today Adv. 1 (2019) 100007.
[62] X. Gao, Q.L. Yu, H.J.H. Brouwers, Apply 29Si, 27Al MAS NMR and selective dissolution in identifying the reaction degree of alkali activated slag-fly ash composites, Ceram. Int. 43 (15) (2017) 12408-12419.
[63] H. Lin, H. Liu, Y. Li, X.M. Kong, Properties and reaction mechanism of phosphoric acid activated metakaolin geopolymer at varied curing temperatures, Cem. Concr. Res. 144 (2021) 106425.
[64] H. Sreenivasan, E. Adesanya, H. Niu, P. Perumal, A.M. Kantola, V.V. Telkki, M. Huttula, W. Cao, J.L. Provis, M. Illikainen, P. Kinnunen, Evidence of formation of an amorphous magnesium silicate (AMS) phase during alkali activation of (Na-Mg) aluminosilicate glasses, Cem. Concr. Res. 145 (2021) 106464.
[65] B. Walkley, R. San Nicolas, M.A. Sani, J.D. Gehman, J.S.J. van Deventer, J.L. Provis, Synthesis of stoichiometrically controlled reactive aluminosilicate and calcium-aluminosilicate powders, Powder Technol. 297 (2016) 17-33.
[66] S. Greiser, P. Sturm, G.J.G. Gluth, M. Hunger, C. Jäger, Differentiation of the solid-state NMR signals of gel, zeolite phases and water species in geopolymer-zeolite composites, Ceram. Int. 43 (2) (2017) 2202-2208.
[67] R.R. Xu, W.Q. Pang, J.H. Yu, Q.S. Huo, J.S. Chen, Chemistry of Zeolites and Related Porous Materials, Wiley, New York, 2007.

Mechanical strength and the degradation mechanism of metakaolin based geopolymer mixed with ordinary Portland cement and cured at high temperature and high relative humidity

Mechanical strength and the degradation mechanism of metakaolin based geopolymer mixed with ordinary Portland cement and cured at high temperature and high relative humidity

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	Xiaolin Pan, Mengyuan Gao, Yun Wang, Yanping He, Tian Si, Yanlin Sun. Poly(lactic acid)-aspirin microspheres prepared via the traditional and improved solvent evaporation methods and its application performances[J]. 中国化学工程学报, 2023, 60(8): 194-204.
[2]	Yingxi Gao, Jiayi Shi, Jie Wang, Fan Zhang, Shichao Tian, Zhiyong Zhou, Zhongqi Ren. Enrichment of nervonic acid in Acer truncatum Bunge oil by combination of two-stage molecular distillation, one-stage urea complexation and five-stage solvent crystallization[J]. 中国化学工程学报, 2023, 59(7): 61-71.
[3]	Guangyuan Chen, Tong Zhou, Meng Zhang, Zhongxiang Ding, Zhikun Zhou, Yuanhui Ji, Haiying Tang, Changsong Wang. Effects of heavy metal ions Cu²⁺/Pb²⁺/Zn²⁺ on kinetic rate constants of struvite crystallization[J]. 中国化学工程学报, 2023, 57(5): 10-16.
[4]	Hu Chen, Ying Wang, Puyu Wang, Yongkang Lv. Assessing quinoline removal performances of an aerobic continuous moving bed biofilm reactor (MBBR) bioaugmented with Pseudomonas citronellolis LV1[J]. 中国化学工程学报, 2023, 57(5): 132-140.
[5]	Yaqiao Liu, Shuozhen Hu, Xinsheng Zhang, Shigang Sun. Investigation of photoelectrocatalytic degradation mechanism of methylene blue by α-Fe₂O₃ nanorods array[J]. 中国化学工程学报, 2023, 57(5): 162-172.
[6]	Pengbao Lian, Lizhen Chen, Dan He, Guangyuan Zhang, Zishuai Xu, Jianlong Wang. Crystallization thermodynamics of 2,4(5)-dinitroimidazole in binary solvents[J]. 中国化学工程学报, 2023, 57(5): 173-182.
[7]	Jiajun Wang, Wenbin Yang, Jiangtao Geng, Zhigang Shao, Wei Song. Experimental investigation on degradation mechanism of membrane electrode assembly at different humidity under automotive protocol[J]. 中国化学工程学报, 2023, 56(4): 70-79.
[8]	Iltaf Khan, Chunjuan Wang, Shoaib Khan, Jinyin Chen, Aftab Khan, Sayyar Ali Shah, Aihua Yuan, Sohail Khan, Mehwish K. Butt, Humaira Asghar. Bio-capped and green synthesis of ZnO/g-C₃N₄ nanocomposites and its improved antibiotic and photocatalytic activities: An exceptional approach towards environmental remediation[J]. 中国化学工程学报, 2023, 56(4): 215-224.
[9]	Dandan Ren, Shanshan Xiang, Yuwen Yan, Ruiying Kong, Xingchu Gong. Design and optimization of purification process of sinomenine hydrochloride[J]. 中国化学工程学报, 2023, 55(3): 63-72.
[10]	Zhengchi Yin, Xiaoke Wu, Yanwei Yang, Huayu Zhang, Wangtao Li, Ruimin Zhu, Qiancheng Zheng, Zhengbao Wang. Fabrication of ZIF-8 membranes on dual-layer ZnO-PES/PES organic hollow fibers by in-situ crystallization[J]. 中国化学工程学报, 2023, 55(3): 101-110.
[11]	Abid Ali, Bilal Ul Amin, Wenwu Yu, Taijiang Gui, Weiwei Cong, Kai Zhang, Zheming Tong, Jiankun Hu, Xiaoli Zhan, Qinghua Zhang. Eco-friendly biodegradable polyurethane based coating for antibacterial and antifouling performance[J]. 中国化学工程学报, 2023, 54(2): 80-88.
[12]	Jingjing Pan, Haoran Sun, Keyi Chen, Yuhao Zhang, Pengnian Shan, Weilong Shi, Feng Guo. Nanodiamonds decorated yolk-shell ZnFe₂O₄ sphere as magnetically separable and recyclable composite for boosting antibiotic degradation performance[J]. 中国化学工程学报, 2023, 54(2): 162-172.
[13]	Hongzhi Zhang, Huiyan Guo, Yang Liu, Chengxiang Shi, Lun Pan, Xiangwen Zhang, Ji-Jun Zou. Thixotropic composite hydrogels based on agarose and inorganic hybrid gellants[J]. 中国化学工程学报, 2023, 54(2): 240-247.
[14]	Meng Li, Jianliang Xu, Huixia Xiao, Xia Liu, Guangsuo Yu, Xueli Chen. Exploring influence of MgO/CaO on crystallization characteristics to understand fluidity of synthetic coal slags[J]. 中国化学工程学报, 2023, 53(1): 1-13.
[15]	Chao Zhang, Youzhi Liu, Weizhou Jiao, Hongyan Shen, Xigang Yuan, Shengkun Jia. An optimization method for enhancement of gas–liquid mass transfer in a bubble column reactor based on the entropy generation extremum principle[J]. 中国化学工程学报, 2023, 53(1): 83-88.