Crystallization of calcium silicate at elevated temperatures in highly alkaline system of Na2O-CaO-SiO2-H2O

doi:10.1016/j.cjche.2017.02.012

›› 2017, Vol. 25 ›› Issue (10): 1539-1544.DOI: 10.1016/j.cjche.2017.02.012

• Materials and Product Engineering • 上一篇下一篇

Crystallization of calcium silicate at elevated temperatures in highly alkaline system of Na₂O-CaO-SiO₂-H₂O

Ganyu Zhu¹, Huiquan Li^1,2, Shaopeng Li¹, Xinjuan Hou^1,2, Xingrui Wang¹

1 Key Laboratory of Green Process and Engineering, National Engineering Laboratory for Hydrometallurgical Cleaner Production Technology, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100190, China;
2 School of Chemistry and Chemical Engineering, University of Chinese Academy of Sciences, Beijing 100049, China

收稿日期:2016-10-27 修回日期:2017-02-14 出版日期:2017-10-28 发布日期:2017-03-21
通讯作者: Huiquan,E-mail address:hqli@ipe.ac.cn
基金资助:
Supported by the National Natural Science Foundation of China (51304184) and the Coal Based Key Scientific and Technological Project of Shanxi Province (MC2014-06).

Crystallization of calcium silicate at elevated temperatures in highly alkaline system of Na₂O-CaO-SiO₂-H₂O

Ganyu Zhu¹, Huiquan Li^1,2, Shaopeng Li¹, Xinjuan Hou^1,2, Xingrui Wang¹

1 Key Laboratory of Green Process and Engineering, National Engineering Laboratory for Hydrometallurgical Cleaner Production Technology, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100190, China;
2 School of Chemistry and Chemical Engineering, University of Chinese Academy of Sciences, Beijing 100049, China

Received:2016-10-27 Revised:2017-02-14 Online:2017-10-28 Published:2017-03-21
Supported by:
Supported by the National Natural Science Foundation of China (51304184) and the Coal Based Key Scientific and Technological Project of Shanxi Province (MC2014-06).

摘要/Abstract

摘要： In Na₂O-CaO-SiO₂-H₂O system, systematic investigations of phase and morphology of calcium silicate in hydrothermal conditions were concisely conducted for high-value utilization of silicon resource in high-alumina fly ash (HAFA). The results show that crystal composition and phase may be affected by relatively low concentration of NaOH, and sodium ions are rearranged into the structure to form NaCaHSiO₄ and Na₂Ca₃H₈Si₂O₁₂ with different C/S ratio at high concentration of NaOH. In addition, phases in wollastonite group possess the morphology of nanofiber. Formation of nanofiber is attributed to the difference of surface energies between axial and radial direction, and higher temperatures lead to easier growth along radial direction. The preparation of C-S-H with different phases and morphologies can guide for the application of silicate solution with high alkalinity with different purposes.

关键词: Crystallization, Hydrothermal, Calcium silicate, Nanofiber

Abstract: In Na₂O-CaO-SiO₂-H₂O system, systematic investigations of phase and morphology of calcium silicate in hydrothermal conditions were concisely conducted for high-value utilization of silicon resource in high-alumina fly ash (HAFA). The results show that crystal composition and phase may be affected by relatively low concentration of NaOH, and sodium ions are rearranged into the structure to form NaCaHSiO₄ and Na₂Ca₃H₈Si₂O₁₂ with different C/S ratio at high concentration of NaOH. In addition, phases in wollastonite group possess the morphology of nanofiber. Formation of nanofiber is attributed to the difference of surface energies between axial and radial direction, and higher temperatures lead to easier growth along radial direction. The preparation of C-S-H with different phases and morphologies can guide for the application of silicate solution with high alkalinity with different purposes.

Key words: Crystallization, Hydrothermal, Calcium silicate, Nanofiber

Ganyu Zhu, Huiquan Li, Shaopeng Li, Xinjuan Hou, Xingrui Wang. Crystallization of calcium silicate at elevated temperatures in highly alkaline system of Na₂O-CaO-SiO₂-H₂O[J]. , 2017, 25(10): 1539-1544.

参考文献

[1] S. Dai, L. Zhao, S. Peng, C.L. Chou, X. Wang, Y. Zhang, D. Li, Y. Sun, Abundances and distribution of minerals and elements in high-alumina coal fly ash from the Jungar Power Plant, Inner Mongolia, China, Int. J. Coal Geol. 81(2010) 320-332.
[2] J.M. Sun, P. Chen, Resourcing utilization of high alumina fly ash, Adv. Mater. Res. 652-654(2013) 2570-2575.
[3] H.Q. Li, J.B. Hui, C.Y. Wang, W.J. Bao, Z.H. Sun, Extraction of alumina from coal fly ash by mixed-alkaline hydrothermal method, Hydrometallurgy 147-148(2014) 183-187.
[4] G.H. Bai, T. Teng, A.G. Wang, J.G. Qin, P. Xu, P.C. Li, Alkali desilicated coal fly ash as substitute of bauxite in lime-soda sintering process for aluminum production, Trans. Nonferrous Met. Soc. 20(2010) 169-175.
[5] X.B. Xu, Y.B. Zhu, S. Zhang, Z.K. Liang, X.X. Chen, Y.B. Gong, Research on optimizing process of pre-desilication of high-aluminum fly ash, Light Met. 7(2013) 18-21.
[6] Z.H. Sun, W.J. Bao, H.Q. Li, J.B. Hui, C.Y. Wang, Q. Tang, Mineral phase change of highalumina fly ash during desilication and extraction of Al₂O₃ by alkali dissolution process, Chin. J. Process. Eng. 13(2013) 403-407.
[7] C. Feng, Y. Yao, Y. Li, X.M. Liu, H.H. Sun, Thermal activation on calcium silicate slag from high-alumina fly ash:A technical report, Clean Technol. Environ. Policy 16(2014) 667-672.
[8] J.J. Chen, J.J. Thomas, H.F.W. Taylor, H.M. Jennings, Solubility and structure of calcium silicate hydrates, Cem. Concr. Res. 34(2004) 1499-1519.
[9] D.R. Moorehead, E.R. Mccartney, Hydrothermal formation of calcium silicate hydrates, J. Am. Ceram. Soc. 48(1965) 565-569.
[10] S. Garrault-Gauffinet, A. Nonat, Experimental investigation of calcium silicate hydrate (C-S-H) nucleation, J. Cryst. Growth 200(1999) 565-574.
[11] N. Meller, C. Hall, J.S. Phipps, A new phase diagram for the CaO-Al₂O₃-SiO₂-H₂O hydro ceramic system at 200 degrees C, Mater. Res. Bull. 40(2005) 715-723.
[12] E.B. Nelson, G.L. Kalousek, Effect of Na₂O on calcium silicate hydrates at elevated temperature, Cem. Concr. Res. 7(1977) 687-694.
[13] Y.Z. Xi, L.S.D. Glasser, Hydrothermal study in the system Na₂O-CaO-SiO₂-H₂O at 300℃, Cem. Concr. Res. 14(1984) 741-748.
[14] K. Baltakys, R. Siauciunas, The influence of γ-Al₂O₃ and Na₂O on the formation of gyrolite in the stirring suspension, J. Mater. Sci. 41(2006) 4799-4805.
[15] E.A. Blakeman, J.A. Gard, C.G. Ramsay, H.F.W. Taylor, Studies on the system sodium oxide-calcium oxide-silica-water, J. Chem. Technol. Biotechnol. 24(1974) 239-245.
[16] W. Nocuń-Wczelik, Effect of Na and Al on the phase composition and morphology of autoclaved calcium silicate hydrates, Cem. Concr. Res. 29(1999) 1759-1767.
[17] I.G. Richardson, The calcium silicate hydrates, Cem. Concr. Res. 38(2008) 137-158.
[18] X.L. Hu, K. Yanagisawa, A. Onda, K. Kajiyoshi, Stability and phase relations of dicalcium silicate hydrates under hydrothermal conditions, J. Ceram. Soc. Jpn. 224(2006) 174-179.
[19] L. Black, K. Garbev, P. Stemmermann, K.R. Hallam, G.C. Allen, Characterisation of crystalline C-S-H phases by X-ray photoelectron spectroscopy, Cem. Concr. Res. 33(2003) 899-911.
[20] J.A. Gard, H.F.W. Taylor, The crystal structure of foshagite, Acta Crystallogr. 13(1960) 785-793.
[21] R.A. Rashid, R. Shamsudin, M.A.A. Habid, A. Jalar, In-vitro bioactivity of wollastonite materials derived from limestone and silica sand, Ceram. Int. 40(2014) 6847-6853.
[22] W. Li, Z.L. Jin, Z.H. Zhang, Application and synthesis of inorganic whisker materials, Prog. Chem. 15(2003) 264-274.
[23] M.Q. Li, Y.F. Chen, S.Q. Xia, J.H. Li, H.X. Liang, Microstructure and processing of ultralight calcium silicate insulation material, J. Chin. Ceram. Soc. 28(2000) 401-406.
[24] G.O. Assarsson, Hydrothermal reactions between calcium hydroxide and amorphous silica:The reactions between 180° and 220°, J. Phys. Chem. 61(1957) 473-479.
[25] S.Y. Hong, F.P. Glasser, Phase relations in the CaO-SiO₂-H₂O system to 200℃ at saturated steam pressure, Cem. Concr. Res. 34(2004) 1529-1534.
[26] F. Lu, B. Zhao, R. Li, W.D. Ruan, Crystal growth of barium nitrate on thiol-terminated self-assembled monolayers and a Raman spectroscopic investigation of the crystal facets, J. Cryst. Growth 426(2015) 33-37.
[27] R. Li, J.S. Gandhi, R. Pillai, R. Forrest, D. Starikov, A. Bensaoula, Epitaxial growth of (111)-oriented Zr_xTi_1-xN thin films on c-plane Al₂O₃ substrates, J. Cryst. Growth 404(2014) 1-8.
[28] H.F. Xu, P.R. Buseck, TEM investigation of the domain structure and superstructure in hillebrandite, Ca₂SiO₃(OH)₂, Am. Mineral. 81(1996) 1371-1374.

Crystallization of calcium silicate at elevated temperatures in highly alkaline system of Na₂O-CaO-SiO₂-H₂O

Crystallization of calcium silicate at elevated temperatures in highly alkaline system of Na₂O-CaO-SiO₂-H₂O

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	Xia Miao, Xiaofan Pang, Shiyu Li, Haoguang Wei, Jianhao Yin, Xiangming Kong. Mechanical strength and the degradation mechanism of metakaolin based geopolymer mixed with ordinary Portland cement and cured at high temperature and high relative humidity[J]. 中国化学工程学报, 2023, 60(8): 118-130.
[2]	Yingxi Gao, Jiayi Shi, Jie Wang, Fan Zhang, Shichao Tian, Zhiyong Zhou, Zhongqi Ren. Enrichment of nervonic acid in Acer truncatum Bunge oil by combination of two-stage molecular distillation, one-stage urea complexation and five-stage solvent crystallization[J]. 中国化学工程学报, 2023, 59(7): 61-71.
[3]	Guangyuan Chen, Tong Zhou, Meng Zhang, Zhongxiang Ding, Zhikun Zhou, Yuanhui Ji, Haiying Tang, Changsong Wang. Effects of heavy metal ions Cu²⁺/Pb²⁺/Zn²⁺ on kinetic rate constants of struvite crystallization[J]. 中国化学工程学报, 2023, 57(5): 10-16.
[4]	Pengbao Lian, Lizhen Chen, Dan He, Guangyuan Zhang, Zishuai Xu, Jianlong Wang. Crystallization thermodynamics of 2,4(5)-dinitroimidazole in binary solvents[J]. 中国化学工程学报, 2023, 57(5): 173-182.
[5]	Bingxiao Feng, Lining Hao, Chaoting Deng, Jiaqiang Wang, Hongbing Song, Meng Xiao, Tingting Huang, Quanhong Zhu, Hengjun Gai. A highly hydrothermal stable copper-based catalyst for catalytic wet air oxidation of m-cresol in coal chemical wastewater[J]. 中国化学工程学报, 2023, 57(5): 338-348.
[6]	Dandan Ren, Shanshan Xiang, Yuwen Yan, Ruiying Kong, Xingchu Gong. Design and optimization of purification process of sinomenine hydrochloride[J]. 中国化学工程学报, 2023, 55(3): 63-72.
[7]	Lianlian Zhao, Fufu Di, Xiaonan Wang, Sumbal Farid, Suzhen Ren. Constructing a hollow core-shell structure of RuO₂ wrapped by hierarchical porous carbon shell with Ru NPs loading for supercapacitor[J]. 中国化学工程学报, 2023, 55(3): 93-100.
[8]	Zhengchi Yin, Xiaoke Wu, Yanwei Yang, Huayu Zhang, Wangtao Li, Ruimin Zhu, Qiancheng Zheng, Zhengbao Wang. Fabrication of ZIF-8 membranes on dual-layer ZnO-PES/PES organic hollow fibers by in-situ crystallization[J]. 中国化学工程学报, 2023, 55(3): 101-110.
[9]	Meng Li, Jianliang Xu, Huixia Xiao, Xia Liu, Guangsuo Yu, Xueli Chen. Exploring influence of MgO/CaO on crystallization characteristics to understand fluidity of synthetic coal slags[J]. 中国化学工程学报, 2023, 53(1): 1-13.
[10]	Zhiwei Du, Jinxue Cheng, Qinglin Huang, Mingxing Chen, Changfa Xiao. Electrospinning organic solvent resistant preoxidized poly(acrylonitrile) nanofiber membrane and its properties[J]. 中国化学工程学报, 2023, 53(1): 289-299.
[11]	Pengbao Lian, Lizhen Chen, Daozhen Huang, Jianxin Xu, Zishuai Xu, Cai Cao, Jiaxiang Zhao, Jianlong Wang. Crystallization thermodynamics of 2,4(5)-dinitroimidazole in eleven pure solvents[J]. 中国化学工程学报, 2022, 48(8): 236-243.
[12]	Zhibin Ma, Xueli Zhang, Guangjun Lu, Yanxia Guo, Huiping Song, Fangqin Cheng. Hydrothermal synthesis of zeolitic material from circulating fluidized bed combustion fly ash for the highly efficient removal of lead from aqueous solution[J]. 中国化学工程学报, 2022, 47(7): 193-205.
[13]	Huawang Zhao, Xiaomin Wu, Zhiwei Huang, Ziyi Chen, Guohua Jing. A comparative study of the thermal and hydrothermal aging effect on Cu-SSZ-13 for the selective catalytic reduction of NO_x with NH₃[J]. 中国化学工程学报, 2022, 45(5): 68-77.
[14]	Yuanjie Li, Qiuxiang Yin, Meijing Zhang, Ying Bao, Baohong Hou, Jingkang Wang, Jiting Huang, Ling Zhou. Characterization and structure analysis of the heterosolvate of erythromycin thiocyanate[J]. 中国化学工程学报, 2022, 44(4): 268-274.
[15]	Zeng Wei Heng, Woon Chan Chong, Yean Ling Pang, Lan Ching Sim, Chai Hoon Koo. Photocatalytic degradation of organic pollutants using green oil palm frond-derived carbon quantum dots/titanium dioxide as multifunctional photocatalysts under visible light radiation[J]. 中国化学工程学报, 2022, 51(11): 21-34.