Zeolitic imidazolate framework-8 modified poly(vinylidene fluoride-co-hexafluoropropylene)/polyacrylonitrile composite separators for Li-ion batteries

doi:10.1016/j.cjche.2023.03.025

中国化学工程学报 ›› 2023, Vol. 62 ›› Issue (10): 291-296.DOI: 10.1016/j.cjche.2023.03.025

• Full Length Article • 上一篇下一篇

Zeolitic imidazolate framework-8 modified poly(vinylidene fluoride-co-hexafluoropropylene)/polyacrylonitrile composite separators for Li-ion batteries

Yanhuai Ding^1,2, Cong Zhang^1,2, Hao Zheng^1,2, Yi Han¹

1. Institute of Rheological Mechanics, Xiangtan University, Xiangtan 411105, China;
2. School of Mechanical Engineering and Mechanics, Xiangtan University, Hunan 411105, China

收稿日期:2022-09-22 修回日期:2023-03-18 出版日期:2023-10-28 发布日期:2023-12-23
通讯作者: Yanhuai Ding,E-mail:yhding@xtu.edu.cn;Yi Han,E-mail:1348390173@qq.com
基金资助:
This work was financially supported by National Natural Science Foundation of China (12002295), Key Scientific Research Project of Education Department of Hunan Province, Xiangtan City, China (22A0113) and Major Science and Technology Projects of Xiangtan Science and Technology Bureau (GX-ZD202210011).

Zeolitic imidazolate framework-8 modified poly(vinylidene fluoride-co-hexafluoropropylene)/polyacrylonitrile composite separators for Li-ion batteries

Yanhuai Ding^1,2, Cong Zhang^1,2, Hao Zheng^1,2, Yi Han¹

1. Institute of Rheological Mechanics, Xiangtan University, Xiangtan 411105, China;
2. School of Mechanical Engineering and Mechanics, Xiangtan University, Hunan 411105, China

Received:2022-09-22 Revised:2023-03-18 Online:2023-10-28 Published:2023-12-23
Contact: Yanhuai Ding,E-mail:yhding@xtu.edu.cn;Yi Han,E-mail:1348390173@qq.com
Supported by:
This work was financially supported by National Natural Science Foundation of China (12002295), Key Scientific Research Project of Education Department of Hunan Province, Xiangtan City, China (22A0113) and Major Science and Technology Projects of Xiangtan Science and Technology Bureau (GX-ZD202210011).

摘要/Abstract

摘要： As one of the most stable metal-organtic framework (MOF), zeolitic imidazolate framework-8 (ZIF-8) has been widely studied for applications in the field of energy storage, catalysis, and environment protection. In this paper, ZIF-8 was employed to enhance the electrochemical properties and thermal stability of the electrospun poly(vinylidene fluoride-co-hexafluoropropylene)/polyacrylonitrile (PVDF-HFP/PAN) composite separator. The results indicate that the test cells assembled with the composite separators show improved rate capability, high discharge capacity, and stable cycling performances. The addition of ZIF-8 can improve the affinity of PVDF-HFP/PAN toward liquid electrolytes, and further enhance the ionic conductivity of the composite separators. In addition, the thermal stability of the PVDF-HFP/PAN separator has been improved by ZIF-8 nanoparticles. This work can provide insight into the application of MOF materials in Li-ion batteries.

关键词: Nanotechnology, ZIF-8, PVDF-HFP/PAN, Composites, Electrolytes

Abstract: As one of the most stable metal-organtic framework (MOF), zeolitic imidazolate framework-8 (ZIF-8) has been widely studied for applications in the field of energy storage, catalysis, and environment protection. In this paper, ZIF-8 was employed to enhance the electrochemical properties and thermal stability of the electrospun poly(vinylidene fluoride-co-hexafluoropropylene)/polyacrylonitrile (PVDF-HFP/PAN) composite separator. The results indicate that the test cells assembled with the composite separators show improved rate capability, high discharge capacity, and stable cycling performances. The addition of ZIF-8 can improve the affinity of PVDF-HFP/PAN toward liquid electrolytes, and further enhance the ionic conductivity of the composite separators. In addition, the thermal stability of the PVDF-HFP/PAN separator has been improved by ZIF-8 nanoparticles. This work can provide insight into the application of MOF materials in Li-ion batteries.

Key words: Nanotechnology, ZIF-8, PVDF-HFP/PAN, Composites, Electrolytes

Yanhuai Ding, Cong Zhang, Hao Zheng, Yi Han. Zeolitic imidazolate framework-8 modified poly(vinylidene fluoride-co-hexafluoropropylene)/polyacrylonitrile composite separators for Li-ion batteries[J]. 中国化学工程学报, 2023, 62(10): 291-296.

参考文献

[1] Y.H. Jiang, Y.H. Ding, P. Zhang, F. Li, Z.M.Yang, Temperature-dependent on/off PVP@TiO² separator for safe Li-storage, J. Membr. Sci. 565 (2018) 33–41.
[2] X. Liu, K.D. Song, C. Lu, Y.T. Huang, X.L. Duan, S. Li, Y.H.Ding, Electrospun PU@GO separators for advanced lithium ion batteries, J. Membr. Sci. 555 (2018) 1–6.
[3] Y.H. Jiang, P. Zhang, H.B. Jin, X. Liu, Y.H.Ding, Flexible, nonflammable and Li-dendrite resistant Na²Ti³O⁷ nanobelt-based separators for advanced Li storage, J. Membr. Sci. 583 (2019) 190–199.
[4] Q. Tian, Q.H. Liu, K.D. Song, Y.F. Mei, W.Z. Lu, J.F. Peng, J. Zhou, Y.H. Ding, Fabrication of aligned PI/GO nanofibers for battery separators, Fibers Polym 22 (1) (2021) 30–35.
[5] K. Park, J.H. Cho, K. Shanmuganathan, J. Song, J. Peng, M. Gobet, S. Greenbaum, C.J. Ellison, J.B.Goodenough, New battery strategies with a polymer/Al₂O₃ separator, J. Power Sources 263 (2014) 52–58.
[6] T. Yvonne, C.Y. Zhang, C.H. Zhang, E. Omollo, S. Ncube, Properties of electrospun PVDF/PMMA/CA membrane as lithium based battery separator, Cellulose 21 (4) (2014) 2811–2818.
[7] T.H. Cho, T. Sakai, S. Tanase, K. Kimura, Y. Kondo, T. Tarao, M.Tanaka, Electrochemical performances of polyacrylonitrile nanofiber-based nonwoven separator for lithium-ion battery, Electrochem. Solid-State Lett. 10 (7) (2007) A159.
[8] Y.H. Ding, P. Zhang, Z.L. Long, Y. Jiang, F. Xu, W. Di, Preparation of PVdF-based electrospun membranes and their application as separators, Sci. Technol. Adv. Mater. 9 (1) (2008) 015005.
[9] K.D. Song, P. Zhang, Y.T. Huang, F. Xu, Y.H. Ding, Electrospun PU/PVP/GO separator for Li-ion batteries, Fibers Polym 20 (5) (2019) 961–965.
[10] Q.H. Liu, W.W. Jiang, W.Z. Lu, Y.F. Mei, F.K. He, M.H. Zhang, Y. Liu, Y.Q. Chen, J.F. Peng, Y.H. Ding, Anisotropic semi-aligned PAN@PVdF-HFP separator for Li-ion batteries, Nanotechnology 31 (43) (2020) 435701.
[11] Can, Liao, A flame-retardant, high ionic-conductivity and eco-friendly separator prepared by papermaking method for high-performance and superior safety lithium-ion batteries, Energy Storage Mater. 48 (2022) 123–132.
[12] A. Subramania, N.T.K. Sundaram, G.V.Kumar, Structural and electrochemical properties of micro-porous polymer blend electrolytes based on PVdF-co-HFP-PAN for Li-ion battery applications, J. Power Sources 153 (1) (2006) 177–182.
[13] W.W. Jiang, Y. Han, Y.H. Ding, Sepiolite and ZIF-67 co-modified PAN/PVdF-HFP nanofiber separators for advanced Li-ion batteries, Nanotechnology 33 (42) (2022) .
[14] D. Bansal, B. Meyer, M.Salomon, Gelled membranes for Li and Li-ion batteries prepared by electrospinning, J. Power Sources 178 (2) (2008) 848–851.
[15] S.T. Yang, W.H. Ma, A.L. Wang, J.F. Gu, Y.H. Yin, A core-shell structured polyacrylonitrile@poly(vinylidene fluoride-hexafluoro propylene) microfiber complex membrane as a separator by co-axial electrospinning, RSC Adv. 8 (41) (2018) 23390–23396.
[16] X.L. Leng, M.D. Yang, C.P. Li, W.U. Arifeen, T.J.Ko, High-performance separator for lithium-ion battery based on dual-hybridizing of materials and processes, Chem. Eng. J. 433 (2022) 133773.
[17] A.Â.L. Ahmad, U.R. Farooqui, N.A. Hamid, Porous (PVDF-HFP/PANI/GO) ternary hybrid polymer electrolyte membranes for lithium-ion batteries, RSC Adv. 8 (45) (2018) 25725–25733.
[18] X. Liang, L.L. Wang, Y. Wang, Y.C. Liu, Y. Sun, H.F. Xiang, Constructing multi-functional composite separator of PVDF-HFP/h-BN supported Co-CNF membrane for lithium-sulfur batteries, Sustainable Energy Fuels 6 (2) (2022) 440–448.
[19] M.L. Ding, R.W. Flaig, H.L. Jiang, O.M. Yaghi, Carbon capture and conversion using metal-organic frameworks and MOF-based materials, Chem. Soc. Rev. 48 (10) (2019) 2783–2828.
[20] N. Stock, S. Biswas, Synthesis of metal-organic frameworks (MOFs): Routes to various MOF topologies, morphologies, and composites, Chem. Rev. 112 (2) (2012) 933–969.
[21] X.W. Mu, X. Zhou, W. Wang, Y.L. Xiao, C. Liao, L.F. Han, Y.C. Kan, L.Song, Design of compressible flame retardant grafted porous organic polymer based separator with high fire safety and good electrochemical properties, Chem. Eng. J. 405 (2021) 126946.
[22] C. Li, L. Liu, J.L. Kang, Y. Xiao, Y.Q. Feng, F.F. Cao, H.Zhang, Pristine MOF and COF materials for advanced batteries, Energy Storage Mater. 31 (2020) 115–134.
[23] L.Y. Yang, J.H. Cao, W.H. Liang, Y.K. Wang, D.Y.Wu, Effects of the separator MOF-Al₂O₃ coating on battery rate performance and solid-electrolyte interphase formation, ACS Appl. Mater. Interfaces 14 (11) (2022) 13722–13732.
[24] Y.R. Lee, M.S. Jang, H.Y. Cho, H.J. Kwon, S. Kim, W.S.Ahn, ZIF-8: A comparison of synthesis methods, Chem. Eng. J. 271 (2015) 276–280.
[25] D. Fairen-Jimenez, S.A. Moggach, M.T. Wharmby, P.A. Wright, S. Parsons, T. Düren, Opening the gate: Framework flexibility in ZIF-8 explored by experiments and simulations, J. Am. Chem. Soc. 133 (23) (2011) 8900–8902.
[26] Can, Liao, Expandable nitrogen-doped carbon-based anodes fabricated from self-sacrificial metal-organic frameworks for ultralong-life lithium storage, Carbon 186 (2022) 46–54.
[27] G.S. Xu, J.F. Yao, K. Wang, L. He, P.A. Webley, C.S. Chen, H.T.Wang, Preparation of ZIF-8 membranes supported on ceramic hollow fibers from a concentrated synthesis gel, J. Membr. Sci. 385-386 (2011) 187–193.
[28] F. Cacho-Bailo, B. Seoane, C. Téllez, J.Coronas, ZIF-8 continuous membrane on porous polysulfone for hydrogen separation, J. Membr. Sci. 464 (2014) 119–126.
[29] Y.H. Ding, P.Zhang, Effect of Mg and Co co-doping on electrochemical properties of LiFePO⁴, Trans. Nonferrous Met. Soc. China 22 (2012) s153–s156.
[30] C.H. Deng, Y.H. Jiang, Z.Y. Fan, S.J. Zhao, D.H. Ouyang, J.J. Tan, P. Zhang, Y.H.Ding, Sepiolite-based separator for advanced Li-ion batteries, Appl. Surf. Sci. 484 (2019) 446–452.
[31] J. Yu, B.Q. Li, C.X. Zhao, J.N. Liu, Q. Zhang, Asymmetric air cathode design for enhanced interfacial electrocatalytic reactions in high-performance zinc-air batteries, Adv. Mater. 32 (12) (2020) e1908488.

Zeolitic imidazolate framework-8 modified poly(vinylidene fluoride-co-hexafluoropropylene)/polyacrylonitrile composite separators for Li-ion batteries

Zeolitic imidazolate framework-8 modified poly(vinylidene fluoride-co-hexafluoropropylene)/polyacrylonitrile composite separators for Li-ion batteries

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	Yinji Wan, Dekai Kong, Feng Xiong, Tianjie Qiu, Song Gao, Qiuning Zhang, Yefan Miao, Mulin Qin, Shengqiang Wu, Yonggang Wang, Ruiqin Zhong, Ruqiang Zou. Enhancing hydrophobicity via core–shell metal organic frameworks for high-humidity flue gas CO₂ capture[J]. 中国化学工程学报, 2023, 61(9): 82-89.
[2]	Reza Sacourbaravi, Zeinab Ansari-Asl, Esmaeil Darabpour. Magnetic polyacrylonitrile/ZIF-8/Fe₃O₄ nanocomposite bead as an efficient iodine adsorbent and antibacterial agent[J]. 中国化学工程学报, 2023, 61(9): 210-220.
[3]	Yingli Li, Zhishuncheng Li, Guangfei Qu, Rui Li, Shuaiyu Liang, Junhong Zhou, Wei Ji, Huiming Tang. Mechanism, behaviour and application of iron nitrate modified carbon nanotube composites for the adsorption of arsenic in aqueous solutions[J]. 中国化学工程学报, 2023, 60(8): 26-36.
[4]	Jiahao Lu, Zhimeng Wang, Qi Zhang, Cheng Sun, Yanyan Zhou, Sijia Wang, Xiangyun Qiu, Shoudong Xu, Rentian Chen, Tao Wei. The effects of amino groups and open metal sites of MOFs on polymer-based electrolytes for all-solid-state lithium metal batteries[J]. 中国化学工程学报, 2023, 60(8): 80-89.
[5]	Yafei Su, Xuke Zhang, Hui Li, Donglai Peng, Yatao Zhang. In-situ incorporation of halloysite nanotubes with 2D zeolitic imidazolate framework-L based membrane for dye/salt separation[J]. 中国化学工程学报, 2023, 58(6): 103-111.
[6]	Shanghong Ma, Haitao Zhang, Jianbo Qu, Xiuzhong Zhu, Qingfei Hu, Jianyong Wang, Peng Ye, Futao Sai, Shiwei Chen. Preparation of waterborne polyurethane/β-cyclodextrin composite nanosponge by ion condensation method and its application in removing of dyes from wastewater[J]. 中国化学工程学报, 2023, 58(6): 124-136.
[7]	Jianhui Zhou, Xin Lai, Jianfeng Hu, Haijie Qi, Shan Liu, Zhengguo Zhang. Design of a graphene oxide@melamine foam/polyaniline@erythritol composite phase change material for thermal energy storage[J]. 中国化学工程学报, 2023, 58(6): 282-290.
[8]	Chao Yang, Zhelin Su, Yeshuang Wang, Huiling Fan, Meisheng Liang, Zhaohui Chen. Insight into the effect of gel drying temperature on the structure and desulfurization performance of ZnO/SiO₂ adsorbents[J]. 中国化学工程学报, 2023, 56(4): 233-241.
[9]	Zhengchi Yin, Xiaoke Wu, Yanwei Yang, Huayu Zhang, Wangtao Li, Ruimin Zhu, Qiancheng Zheng, Zhengbao Wang. Fabrication of ZIF-8 membranes on dual-layer ZnO-PES/PES organic hollow fibers by in-situ crystallization[J]. 中国化学工程学报, 2023, 55(3): 101-110.
[10]	Qingyue Han, Suqing Wang, Wenhan Kong, Bing Ji, Haihui Wang. Composite polymer electrolyte reinforced by graphitic carbon nitride nanosheets for room-temperature all-solid-state lithium batteries[J]. 中国化学工程学报, 2023, 54(2): 257-263.
[11]	Jiacheng Chen, Jincheng Wang, Shuhong Li, Kailing Xiang, Shiqiang Song. Pyridine terminated polyurethane dendrimer/chlorinated butyl rubber nanocomposites with excellent mechanical and damping properties[J]. 中国化学工程学报, 2023, 53(1): 211-221.
[12]	Minjie Shi, Hangtian Zhu, Cheng Yang, Jing Xu, Chao Yan. Chemical reduction-induced fabrication of graphene hybrid fibers for energy-dense wire-shaped supercapacitors[J]. 中国化学工程学报, 2022, 47(7): 1-10.
[13]	Yingmeng Zhang, Luting Liu, Qingwei Deng, Wanlin Wu, Yongliang Li, Xiangzhong Ren, Peixin Zhang, Lingna Sun. Hybrid CuO-Co₃O₄ nanosphere/RGO sandwiched composites as anode materials for lithium-ion batteries[J]. 中国化学工程学报, 2022, 47(7): 185-192.
[14]	Jipeng Dong, Fei Wang, Guanghui Chen, Shougui Wang, Cailin Ji, Fei Gao. Fabrication of nickel oxide functionalized zeolite USY composite as a promising adsorbent for CO₂ capture[J]. 中国化学工程学报, 2022, 46(6): 207-213.
[15]	Iman Farirzadeh, Majid Riahi Samani, Davood Toghraie. Lead removal from aqueous medium using fruit peels and polyaniline composites in aqueous and non-aqueous solvents in the presence of polyethylene glycol[J]. 中国化学工程学报, 2022, 44(4): 253-259.