Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials

摘要/Abstract

摘要： The lanthanum aluminum mesoporous materials were synthesized using sodium dodecyl sulfate as a template agent by ultrasonic hydrothermal method.The resulting samples were characterized by low angle X-ray diffraction(XRD),N₂ adsorption-desorption studies,transmission electron microscopy(TEM)and surface morphology analysis(SEM),surface acid(NH₃-TPD),reducibility properties(TPR),X-ray energy dispersive spectrometer(EDS)and thermogravimetric analysis(TG/DTG).A l/La composite mesoporous material were synthesized with n(Al):n(La)=70:1.0,80℃ of reaction temperature,20 h of reaction time,12 h of crystallization time,650℃ of calcination temperature.The specific surface area of the sample is 273.90 m²·g^-1,with the average diameter 5.642 nm and pore volume 0.2354 cm³·g^-1.The samples have mesoporous structure and its particles are similar to a worm-shaped tubular structure.The influence of calcination temperature on the surface physical and chemical properties of Al/La composited mesoporous materials was examined,and the results showed that the acid strength was increased but the amount of acidic sites is decreased as the calcination temperature increased.It was found that the sample calcined at 650℃ had appropriate acid content,acid strength and better reducibility.

关键词: Al/La composite oxides, mesoporous material, synthesis, characterization

Abstract: The lanthanum aluminum mesoporous materials were synthesized using sodium dodecyl sulfate as a template agent by ultrasonic hydrothermal method.The resulting samples were characterized by low angle X-ray diffraction(XRD),N₂ adsorption-desorption studies,transmission electron microscopy(TEM)and surface morphology analysis(SEM),surface acid(NH₃-TPD),reducibility properties(TPR),X-ray energy dispersive spectrometer(EDS)and thermogravimetric analysis(TG/DTG).A l/La composite mesoporous material were synthesized with n(Al):n(La)=70:1.0,80℃ of reaction temperature,20 h of reaction time,12 h of crystallization time,650℃ of calcination temperature.The specific surface area of the sample is 273.90 m²·g^-1,with the average diameter 5.642 nm and pore volume 0.2354 cm³·g^-1.The samples have mesoporous structure and its particles are similar to a worm-shaped tubular structure.The influence of calcination temperature on the surface physical and chemical properties of Al/La composited mesoporous materials was examined,and the results showed that the acid strength was increased but the amount of acidic sites is decreased as the calcination temperature increased.It was found that the sample calcined at 650℃ had appropriate acid content,acid strength and better reducibility.

Key words: Al/La composite oxides, mesoporous material, synthesis, characterization

宋伟明, 左春玲, 邓启刚. Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials[J]. , 2011, 19(1): 70-75.

SONG Weiming, ZUO Chunling, DENG Qigang. Synthesis and Characterization of Worm-shaped Tubular Lanthanum Aluminum Composite Mesoporous Materials[J]. , 2011, 19(1): 70-75.

参考文献

1 Ribeiro, C.M., Conceicao, F.L., Lopes, J.M., “Comparative study of Al-MCM materials prepared at room temperature with different aluminium sources and by some hydrothermal methods”, Micropor. Mesopor. Mater., 92 (2), 270-285 (2006).
2 Chen, L., Liu, X.Q., “π-Complexation mesoporous adsorbents Cu-MCM-48 for ethylene-ethane separation”, Chin. J. Chem. Eng.,16 (4), 570-574 (2008).
3 Younghun, K., Pil, K., Changmook, K., Jongheop, Y., “Comparison of mesoporous aluminas synthesized using stearic acid and its salts”, Kor. J. Chem. Eng., 22 (2), 321-327 (2005).
4 Alieh, K., Hamid, R. A., Matin, P., “Production of syngas by CO₂ reforming on M_xLa_1-xNi_0.3Al_0.7O₃-d (M = Li, Na, K) Catalysts”, Ind. Eng. Chem. Res., 47 (16), 5892-5898 (2008).
5 Kenneth, A.B., Linjie, H., Josephine, M.H., “Controlled pore opening of Ni/Al₂O₃ using chemical vapor deposition in a fluidized bed reactor”, Ind. Eng. Chem. Res., 46 (2), 684-690 (2007).
6 Naik, B., Prasad, V.S., Ghosh, N.N., “Development of a simple aqueous solution based chemical method for synthesis of mesoporous γ-alumina powders with disordered pore structure”, J. Porous Mater., 17 (1), 115-121 (2010).
7 Wang, A.M., Zhou C., Wang, H., Shen, S.B., Xue, J.Y., Ouyang, P.K., “Covalent assembly of penicillin acylase in mesoporous silica based on macromolecular crowding theory”, Chin. J. Chem. Eng., 15 (6),788-790 (2007).
8 May, M., Navarrete, J., Asomoza, M., Gomez, R., “Tailored mesoporous alumina prepared from different aluminum alkoxide precursors”, J. Porous Mater., 14 (2), 159-164 (2007).
9 Suzuki, N., Yamauchi, Y., “One-step synthesis of hierarchical porous γ-alumina with high surface area”, J. Sol Gel Sci. Technol., 53 (2),428-433 (2010).
10 Zhang, Y., Liang, H., Zhao, C.Y., Liu, Y., “Macroporous alumina monoliths prepared by filling polymer foams with alumina hydrosols”, J. Mater. Sci., 44 (3), 931-938 (2009).
11 Pavese, M., Biamino, S., “Mesoporous alumina obtained by combustion synthesis without template”, J. Por. Mater., 16 (1), 59-64 (2009).
12 Kim, P., Joo, J.B., Kim, H., Kim, W., Kim, Y., Song, I.K., Yi, J., “Preparation of mesoporous Ni-alumina catalyst by one-step sol-gel method: Control of textural properties and catalytic application to the hydrodechlorination of o-dichlorobenzene”, Catal. Lett., 104 (1),3-8 (2005).
13 Niu, J.R., Liu, W., Dai, H.X., He, H., Zi, X.H., Li, P.H., “Preparation and characterization of highly active nanosized strontium-doped lanthanum cobaltate catalysts with high surface areas”, Chin. Sci. Bull., 51 (14), 1673-1681 (2006).
14 Jeon, J.K., Kim, C.,J., Park, Y.K., Ihm, S.K., “Catalytic properties of potassiumor lanthanum-promoted Co/γ-Al₂O₃ catalysts in carbon monoxide hydrogenation”, Kor. J. Chem. Eng., 21 (2), 365-369 (2004).
15 Dupeyrat, C.B., Ortega, F.M., Ganne, M., “Methane catalytic combustion on La-based perovskite type catalysts in high temperature isothermal conditions”, Appl. Catal. A, 206, 205-215 (2001).
16 Antoninho, V., Neftali, V.C., Luiz, F.D.P., “Synthesis of Ni nanoparticles in microporous and mesoporous Al and Mg oxides”, Micropor. Mesopor. Mater., 68 (1), 151-157 (2004).
17 Hussam, H., Ibrahim, P.K., Raphael, O.I., “Reforming of isooctane over Ni-Al₂O₃ catalysts for hydrogen production: Effects of catalyst preparation method and nickel loading”, Energy Fuels, 21 (2),570-580 (2007).
18 Zhang, Z.X., Bai, P., Xu, B.J., Yan, Z.F., “Synthesis of mesoporous alumina TUD-1 with high thermostability”, J. Por. Mater., 13,245-250 (2006).
19 Kim, Y., Lee, B., Jongheop, Y., “Effect of framework or textural nanoporosity on the bulk morphology of mesoporous aluminas”, Kor. J. Chem. Eng., 24 (4), 679-682 (2007).
20 Bhattacharyya, S., Gabashvili, A., Perkas, N., “Sonochemical insertion of silver nanoparticles into two-dimensional mesoporous alumina”, J. Phys. Chem. C., 111, 11161-11167 (2007).
21 Zhang, G., Li, L., Zhang, X., Yuan, F.L., Guang, H.Z., Fu, H.G., “The effect of La₂O₃ and gelatinization aid on the thermostability of active Al₂O₃ ”, J. Natural Sci. Heilongjiang University, 20 (2), 106-110 (2003). (in Chinese)
22 Yang, L.N., Joo, J.B., Kim, Y.J., Oh, S., Kim, N.D., Jongheop, Y., “Synthesis of superacidic mesoporous alumina and its application in the dehydration of glycerol”, Kor. J. Chem. Eng., 25 (5), 1014-1017 (2008).

[1]	Mingzhi Li, Zhikai Liu, Wang Yao, Chao Xu, Yangping Yu, Mei Yang, Guangwen Chen. Ultrasonic cavitation-enabled microfluidic approach toward the continuous synthesis of cesium lead halide perovskite nanocrystals[J]. 中国化学工程学报, 2023, 59(7): 32-41.
[2]	Haixiang Liu, Jun Zhang, Chunlei Dong, Gang Zhu, Guanben Du, Shuduan Deng. Synthesis, performance and structure characterization of glyoxal-monomethylolurea-melamine (G-MMU-M) co-condensed resin[J]. 中国化学工程学报, 2023, 59(7): 92-104.
[3]	Yi Wu, Pengfei Song, Ningyan Li, Yanan Jiang, Yuan Liu. Molybdenum tailored Co⁰/Co²⁺ active pairs on a perovskite-type oxide for direct ethanol synthesis from syngas[J]. 中国化学工程学报, 2023, 59(7): 279-289.
[4]	Kai Xue, Yanchun Xue, Jing Wang, Shuya Zhang, Xingmei Guo, Xiangjun Zheng, Fu Cao, Qinghong Kong, Junhao Zhang, Zhong Jin. KOH-assisted aqueous synthesis of ZIF-67 with high-yield and its derived cobalt selenide/carbon composites for high-performance Li-ion batteries[J]. 中国化学工程学报, 2023, 57(5): 214-223.
[5]	Shuang Qiu, Yonghou Xiao, Haoran Wu, Shengnan Lu, Qidong Zhao, Gaohong He. One-pot synthesis of bimetallic CeCu-SAPO-34 for high-efficiency selective catalytic reduction of nitrogen oxides with NH₃ at low temperature[J]. 中国化学工程学报, 2023, 56(4): 193-202.
[6]	Wufeng Wu, Xilu Hong, Jiang Fan, Yanying Wei, Haihui Wang. Research progress on the substrate for metal–organic framework (MOF) membrane growth for separation[J]. 中国化学工程学报, 2023, 56(4): 299-313.
[7]	Aiqin Gao, Xiang Luo, Huanghuang Chen, Aiqin Hou, Hongjuan Zhang, Kongliang Xie. Design of the reactive dyes containing large planar multi-conjugated systems and their application in non-aqueous dyeing[J]. 中国化学工程学报, 2023, 54(2): 264-271.
[8]	Tengjie Wang, Wenkai Li, Xuehui Ge, Ting Qiu, Xiaoda Wang. Kinetics measurement of ethylene-carbonate synthesis via a fast transesterification by microreactors[J]. 中国化学工程学报, 2023, 53(1): 243-250.
[9]	Xuan Gao, Zhihui Li, Dongsheng Zhang, Xinqiang Zhao, Yanji Wang. Synthesis and kinetics of 2,5-dicyanofuran in the presence of hydroxylamine ionic liquid salts[J]. 中国化学工程学报, 2023, 53(1): 310-316.
[10]	Xin Yong, Hong Chen, Huawang Zhao, Miao Wei, Yingnan Zhao, Yongdan Li. Insight into SO₂ poisoning and regeneration of one-pot synthesized Cu-SSZ-13 catalyst for selective reduction of NO_x by NH₃[J]. 中国化学工程学报, 2022, 46(6): 184-193.
[11]	N. M'hanni, T. Anik, R. Touir, M. Galai, M. Ebn Touhami, E.H. Rifi, Z. Asfari, S. Bakkali. Effect of additives on nickel-phosphorus deposition obtained by electroless plating: Characterization and corrosion resistance in 3%(mass) sodium chloride medium[J]. 中国化学工程学报, 2022, 44(4): 341-350.
[12]	Fangyou Yan, Wei Li, Jinli Zhang. Simultaneous synthesis of heat-integrated water networks by a nonlinear program: Considering the wastewater regeneration reuse[J]. 中国化学工程学报, 2022, 44(4): 402-411.
[13]	Yanliang Zhou, Qianjin Sai, Zhenni Tan, Congying Wang, Xiuyun Wang, Bingyu Lin, Jun Ni, Jianxin Lin, Lilong Jiang. Highly efficient subnanometer Ru-based catalyst for ammonia synthesis via an associative mechanism[J]. 中国化学工程学报, 2022, 43(3): 177-184.
[14]	Yichao Wu, Zhiwei Xie, Xiaofeng Gao, Xian Zhou, Yangzhi Xu, Shurui Fan, Siyu Yao, Xiaonian Li, Lili Lin. The highly selective catalytic hydrogenation of CO₂ to CO over transition metal nitrides[J]. 中国化学工程学报, 2022, 43(3): 248-254.
[15]	Baowen Wang, Zhongyuan Cai, Heyu Li, Yanchen Liang, Tao Jiang, Ning Ding, Haibo Zhao. Reaction characteristics investigation of CeO₂-enhanced CaSO₄ oxygen carrier with lignite[J]. 中国化学工程学报, 2022, 42(2): 319-328.